Synthesis and properties of novel organosoluble polyimides derived from 1,4-bis[4-(3,4-dicarboxylphenoxy)]triptycene dianhydride and various aromatic diamines

A novel triptycene-based dianhydride, 1,4-bis[4-(3,4-dicarboxylphenoxy)]triptycene dianhydride, was prepared from 4-nitro-N-methylphthalimide and potassium phenolate of 1,4-dihydroxytriptycene (1). The aromatic nucleophilic substitution reaction between 4-nitro-N-methylphthalimide and I afforded triptycene-based bis(N-methylphthalimide) (2), which hydrolyzed and subsequently dehydrated to give the corresponding dianhydride (3). A series of new polyimides containing triptycene moieties were prepared from the dianhydride monomer (3) and various diamines in in-cresol via conventional one-step polycondensation method. Most of the resulting polyimides were soluble in common organic solvents, such as chloroform, THF, DMAc and DMSO. The polyimides exhibited excellent thermal and thermo-oxidative stabilities with the onset decomposition temperature and 10% weight loss temperature ranging from 448 to 486 degrees C and 526 to 565 degrees C in nitrogen atmosphere, respectively. The glass transition temperatures of the polyimides were in the range of 221-296 degrees C. The polyimide films were found to be transparent, flexible, and tough. The films had tensile strengths, elongations at break, and tensile moduli in the ranges 95-118 MPa, 5.3-16.2%, and 1.03-1.38 GPa, respectively. Wide-angle X-ray diffraction measurements revealed that these polyimides were amorphous.

Shear-enhanced crystallization of a thermoplastic polyimide derived from 3,3 ',4,4 '-oxydiphthalic dianhydride and 4,4 '-oxydianiline

The aim of this work is to investigate the effect of consecutive shear on the crystallization of an amorphous aromatic polyimide (PI) derived from 3,3',4,4'oxydiphthalic dianhydride (3,3',4,4'-ODPA) and 4,4-oxydianiline (ODA). At 260 degrees C, the increase of shear rate or shear time leads to the increase of crystallinity. Indeed, increasing shear rate can also accelerate the crystallization behavior. Moreover, it was found that a new melting peak appeared at higher temperature for long time or high rate sheared sample. The enhancement of crystallization behavior appears directly linked to the increase of crystal thickness. Particularly, the effect of shear temperature was investigated, and the results revealed that the crystallization of the PI was more sensitive to shear at 260 degrees C, which was 10 degrees above the glass transition temperature (250 degrees C) of the PI. Possible mechanism was proposed to illustrate the effect of consecutive shear on the crystallization of the PI polymer.