Studies on the alkylation of isobutane with butene over WO3/ZrO2 strong solid acid (I) - Effect of preparation, load of WO3 and calcination temperature

A series of WO3/ZrO2 strong solid acid prepared under different conditions were studied. Their crystal structures, surface properties and acidities were determined by means of XRD, DTA-TG, H-2- TPR, Laser Raman and acidity measurements. The results revealed that ZrO2 in WO3/ZrO2 existed mainly in tetragonal phase, the addition of WO3 plays an important role to stabilize tetragonal phase of ZrO2 and thus the catalyst had a considerable surface area. WO3 in WO3/ZrO2 was dispersed and crystalized in WO3 crystalite on ZrO2 surface and partly reacted with ZrO2 to form the bond of Zr-O-W, which acts as the strong solid acid site. The catalytic properties of WO3/ZrO2 strong solid acid for alkylation of iso-butane with butene under the different conditions were investigated. They had a better reaction performance than other strong solid acids, a parallel relationship could be drawn between the catalytic activity and the amount of acid sites as well as the acidic strength of the catalysts.

WO_3/ZrO_2固体强酸催化剂上异丁烷/丁烯的烷基化反应Ⅱ.过渡金属的助催化作用

制备了一系列用过渡金属M (M =Pt,Co ,Ni,Mn ,Fe,Cu)活化的WO3 /ZrO2 固体强酸催化剂 ,用XRD ,DTA TG ,H2 TPR ,NH3 TPD等测定了其晶型结构、表面状态和酸量 .结果表明 ,各样品中的ZrO2 主要以T晶相存在 ,但T晶相ZrO2 所占的比例因过渡金属不同而异 ,比表面积比WO3 /ZrO2 稍有下降 ;金属Pt的引入使呈单层分散的WO3 的表面状态发生了改变 .研究了异丁烷 /丁烯烷基化反应 ,其反应活性与酸量的测定结果有对应关系 ;与WO3 /ZrO2 相比 ,M WO3 /ZrO2 上的丁烯转化率均稍有下降 ,但具有更高的i C08选择性 .从反应机理分析了添加过渡金属无显著效果的原因.

WO_3/ZrO_2固体强酸催化剂上异丁烷-丁烯烷基化反应的研究Ⅲ.超细ZrO_2载体对催化剂性能的影响

制备了以超细 Zr O2 为载体的 WO3/ Zr O2 、 SO42 - / Zr O2 、 Mo O3/ Zr O2 固体强酸催化剂 ,并用 XRD、 DTA-TG、 H2 - TPR、 NH3- TPD等方法表征了其晶型结构、表面状态和酸性 .结果表明 ,超细 Zr O2 及其催化剂均主要以 T-晶相存在 ,与通常以 Zr(OH) 4为载体制备的同类催化剂相比 ,Zr O2 中的 T-晶相所占比例虽有所下降 ,但具有更大的比表面积、酸强度和对金属氧化物的负载能力 ,且酸强度随焙烧温度升高而增强 ,表明其表面状态亦有较大变化 .研究了以超细 Zr O2 为载体的固体强酸催化剂上 ,异丁烷 -丁烯的烷基化反应 ,与通常以 Zr(OH) 4为载体制得的催化剂相比 ,其具有更好的烯烃转化率 ,在烷基化产物中 ,C5 ～ C7裂解产物较多 ,使 C80的选择性有所下降

WO_3/ZrO_2固体强酸催化剂上异丁烷-丁烯烷基化反应研究(Ⅰ)──钨负载量和焙烧温度的影响

制备了系列 WO3/ Zr O2 固体强酸催化剂 ,用 XRD,DTA-TG,H2 -TPR,Raman光谱和酸性测定等方法测定其晶型结构、表面状态和酸性 .结果表明 ,WO3/ Zr O2 中的 Zr O2 基本以 T晶相存在 ,WO3对稳定 T晶相有重要作用 ,样品具有较大的表面积 .分散于 Zr O2 表面上的 WO3主要以单层分散和析出的 WO3晶粒形式存在 ,部分可能与 Zr O2 作用形成 Zr— O—W键并起强酸作用 .研究了各种实验条件下的异丁烷 -丁烯烷基化反应 .与其它固体酸相比 ,具有较高的起始活性和 i-C08选择性 ,且与酸强度和酸量有较好的对应关系

异丁烷-丁烯烷基化反应催化剂的研究Ⅳ.Zr(SO_4)_2和Zr(SO_4)_2/Al_2O_3(SiO_2)

制备了一系列不同焙烧温度的 Zr(SO4) 2 及 Zr(SO4) 2 负载量不同的 Zr(SO4) 2 / Al2 O3(Si O2 )固体强酸催化剂 ,用 XRD、IR、BET、TG- DTA、NH3- TPD、Hamm ett指示剂等方法研究了该催化体系的晶型、结构、比表面、酸量及酸强度随负载量和焙烧温度的变化规律 .将 Zr(SO4) 2 负载在 Al2 O3和 Si O2 两种载体上呈现不同的特性 .在 Al2 O3上明显地延缓了 Zr(SO4) 2 的分解和 Zr O2的晶相转变 .并且使酸量和酸强度有所提高 .研究了异丁烷 -丁烯烷基化反应 ,结果表明 ,对 973和 10 2 3K焙烧的 Zr(SO4) 2 样品 ,活性最好 ,而对 Zr(SO4) 2 / Al2 O3,负载量在 m(Zr(SO4) 2 ) /m(Al2 O3) =0 .5 / 1.0左右时活性最好 .各种样品均具有较高的 C08选择性.

Preparation of stable mesoporous silica FSM-16 from water glass in the presence of cetylpyridium bromide

The synthesis and characterization of the mesoporous materials FSM-16 (folded sheets mesoporous materials) with highly ordered structure in open-vessel by using cetylpyridium bromide (CPBr) and the single-layered polysilica Kanemite as new template and silicon source, respectively, has been investigated systematically. The hexagonal arrangements of uniformly size pores were characterized by FTIR. XRD. nitrogen adsorption. TG-DTA. SEM and TEM. Especially, the porous products with higher surface areas show remarkable thermal stability up to 1000 C. The potential application as carrier of catalysts or host-guest materials is anticipated. (C) 2001 Elsevier Science B.V. All rights reserved.

用3种方法合成Y_3Al_5O_(12)∶RE~(3+)(RE=Eu,Dy)发光粉的对比研究

以金属硝酸盐为反应原料 ,分别采用柠檬酸 凝胶法、共沉淀法和固相法制备了YAG和YAG∶RE3+ (RE =Eu ,Dy) (1% ,摩尔分数 )发光粉 ,并通过XRD ,TG DTA和发光光谱对样品进行了表征。柠檬酸 凝胶法、共沉淀法和固相法制备的YAG和YAG∶Eu的晶相形成温度分别是 80 0和 90 0℃。Eu3+ 在非晶态和晶态YAG中其激发和发射光谱有明显差异 ,在一定温度范围内 ,发光强度随烧结温度的升高而增强。由于碳杂质的存在 ,90 0和 10 0 0℃下柠檬酸 凝胶法制备样品的发射强度较其他两种方法低。

Preparation and spectra study of TiO2 gel doped with fluorescein

TiO2 gel doped with fluorescein was prepared by a sol-gel method, and the fluorescence of fluorescein and its effect on formation of the: gel were investigated with absorption, fluorescence, IR spectroscopies and TG-DTA analysis. The results indicated that FL incorporated into TiO2 gel had exhibited big changes compared to that in ethanol solution both in the absorption and the emission spectra, and the formation of TiO2 gel was influenced greatly by FL.

Synthesis, crystal structure and properties of H-8[P4W14O58Na4 (H2O)(20)] center dot 16H(2)O

A novel heteropoly tungstophosphates, H-8[P4W14O58Na4(H2O)(20)] . 16H(2)O, was synthesized by hydrothermal method and characterized by elemental analysis, IR spectrum and single-crystal X-ray structure analysis. The thermal stability of the compound was investigated by using TG-DTA. The crystal is triclinic system with space group P (1) over bar, a = 1. 137 9(2) nm, b=1. 363 2(3) nm, c=1. 627 1(3) nm; alpha=78. 20(3)degrees, beta=71, 20(3)degrees, gamma= 71. 62(3)degrees; V = 2. 252 5(8) nm(3), Z=1, M-r= 4 374. 38, D-c = 3. 225 mg/cm(3), mu = 18. 007 mm(-1), F(000)=1 972, R=0. 074 2, R-w=0. 200 4. The result of structure analysis shows that the anion of the compound consists of two PW7O29Na2(H2O)(10) subunits and two linked phosphorous atoms. A kind of microporous with size of 0. 661 4 nm X 0. 318 9 nm was formed in the crystal structure.

以水滑石为前体的Mg-Al-M复合氧化物对催化消除NOx的活性

通过H2-TPR，XRD，TG-DTA及比表面积测定等对ＭｇＡｌ水滑石化合物进行了表征，研究了焙烧温度对水滑石物理性质的影响．在此基础上，研究了ＭｇＡｌ水滑石中加入过渡金属（Ｍ）离子后对ＮＯ＋ＣＯ反应的催化活性．结果发现，含有Ｃｕ离子的样品对ＮＯ＋ＣＯ反应有较高的催化活性，并与ＣｏＡｌＭ的催化性能进行了比较

H_8[P_4W_(14)O_(58)Na_4(H_2O)_(20)]·16H_2O的合成、晶体结构与性质

用水热法合成了 H8[P4 W14 O58Na4 (H2 O) 2 0 ]· 16 H2 O,通过 X射线单晶衍射、元素分析和IR进行了结构表征 ,用 TG- DTA研究了热稳定性 .晶体属三斜晶系 ,P1空间群 ,a=1.1379(2 )nm,b=1.36 32 (3) nm,c=1.6 2 71(3) nm;α=78.2 0 (3)°,β=71.2 0 (3)°,γ=71.6 2 (3)°;V=2 .2 52 5(8) nm3 ,Z=1,Mr=4 374 .38,Dc=3.2 2 5mg/ cm3 ,μ=18.0 0 7mm-1,F(0 0 0 ) =1972 ,R=0 .0 74 2 ,Rw=0 .2 0 0 4 .标题化合物的阴离子是由两个 PW7O2 9Na2 (H2 O) 10 亚单元通过与两个磷原子上键合的氧连接而成 ,分子内形成了一个 0 .6 6 14nm× 0 .3189nm的微孔.

La_(0.2)Ca_(0.8)MnO_3催化剂活性相的结构和形成机理

利用TG，DTA，XRD和XPS方法研究了La0.2Ca0.8MnO3催化剂的结构和形成机理．样品用La，Ca，Mn混合硝酸盐制备．随着焙烧温度的升高发生了一系列的固相反应，发现氨氧化催化剂催化活性与生成的CaMnO3含量成正比．在900℃制备的含有CaMnO3，La0.575Ca0.425MNO3，Mn2O3和La2O3的混合物是氨氧化最佳催化剂，活性相是CaMnO3，并具有大量的氧空穴.

α-B-Keggin型杂多化合物K_5H[Co_4(VW_9O_(33))_2]·5H_2O的合成和结构

合成了新化合物K_5H[Co_4(VW_9O_(33))·5H_2O,并运用IR,UV-ViS,DTA和单晶X射线衍射对其结构进行了表征.测定结果证实标题化合物具有α-B-Keggin型结构,两个(VW_9O_(33)~(7-)结构单元由四个Co(Ⅱ)O_6 八面体连接.杂多化合物属单斜晶系P2_(1/n),a=1.2307(3)nm,b=2.1250(4)nm,c=1.5817(3)nm,β=91.86(3)°,V=4.1343(14)nm~3,R=0.0895,R_w=0.2180.

Synthesis and thermo-decomposition mechanism of rare earth complexes with phenylacetic acid

Rare earth complexes with phenylacetic acid (LnL(3) . nH(2)O, Ln is Ce, Nd, Pr, Ho, Er, Yb and Y, L is phenylacetate, n = 1-2) were prepared and characterized by elemental analysis, IR spectroscopy, chemical analysis, and X-ray crystal structure. The mechanism of thermal decomposition of the complexes was studied by means of TG-DTG, DTA and DSC. The activation energy and enthalpy change for the dehydration and melting processes were determined.

Studies on preparation, characterization of cobalt(II) phenanthroline and 8-hydroxyquinoline complexes/Y zeolite, and catalytic hydroxylation of phenol

Cobalt(II) phenanthroline and 8-hydroxyquinoline complexes/Y zeolite, denoted as CoPhen/Y and CoOx/Y respectively, were prepared, The formation of the metal complexes mentioned above within the cages of Y zeolite and their crystal structures were determined by elementary analyses, TG-DTA, diffuse reflectance UV-Vis, SEM, BET and XRD methods. The influence of experimental parameters upon phenol conversion and product selectivities was investigated as well.