Effect of Crystallographic Texture on Magnetic Characteristics of Cobalt Nanowires

Cobalt nanowires with controlled diameters have been synthesized using electrochemical deposition in etched ion-track polycarbonate membranes. Structural characterization of these nanowires with diameter 70, 90, 120 nm and length 30 mu m was performed by scanning electron microscopy, high-resolution transmission electron microscopy, and X-ray diffraction techniques. The as-prepared wires show uniform diameter along the whole length and X-ray diffraction analysis reveals that [002] texture of these wires become more pronounced as diameter is reduced. Magnetic characterization of the nanowires shows a clear difference of squareness and coercivity between parallel and perpendicular orientations of the wires with respect to the applied field direction. In case of parallel applied field, the coercivity has been found to be decreasing with increasing diameter of the wires while in perpendicular case; the coercivity observes lower values for larger diameter. The results are explained by taking into account the magnetocrystalline and shape anisotropies with respect to the applied field and domain transformation mechanism when single domain limit is surpassed.

Microcalorimetric and IR spectroscopic studies of CO adsorption on molybdenum nitride catalysts

The adsorption of CO on both nitrided and reduced passivated Mo(2)N catalysts in either alumina supported or unsupported forms was studied by adsorption microcalorimetry and infrared (IR) spectroscopy. The CO is adsorbed on nitrided Mo(2)N catalysts on three different surface sites: 4-fold vacancies, Mo(delta+) ( 0 < delta < 2) and N sites, with differential heats of CO adsorption decreasing in the same order. The presence of the alumina-support affects the energetic distribution of the adsorption sites on the nitrided Mo(2)N, i.e. weakens the CO adsorption strength on the different sites and changes the fraction of sites adsorbing CO in a specific form, revealing that the alumina supported Mo(2)N phase shows lower electron density than pure Mo(2)N. On reduced passivated Mo(2)N catalysts the CO was found to adsorb mainly on Mo(4+) sites, although some slightly different surface Mo(delta+) d (0 < delta < 2) sites are also detected. The nature, density and distribution of surface sites of reduced passivated Mo(2)N/gAl(2)O(3) were similar to those on reduced MoO(3)/gamma-Al(2)O(3).

Promoting effects in hydrogenation and hydrodesulfurization reactions on the zirconia and titania supported catalysts

Tetralin hydrogenation (HYD) and thiophene hydrodesulfurization (HDS) were studied for the supported MoS2 and WS2 sulfides, either non-promoted or promoted with Co and Ni. The supports used were ZrO2, alumina-stabilized TiO2 and pure alumina. Preparation of catalysts included presulfidation of non-promoted system with subsequent addition of promoter and resulfidation. It has been found that the nature of promoter plays determining role for the catalytic performance. The most active in both HYD and HDS reactions are Ni-promoted Mo and W catalysts, supported on ZrO2. (C) 2003 Published by Elsevier B.V.

Microstructure and NO2 sensing properties of Fe2O3 thin films

W-doped Fe2O3 films have been fabricated on polycrystalline alumina substrates by the RF magnetron sputtering method, and effects of annealing temperature on the NO2 sensing properties have been examined. The crystal structure of the obtained film changed from Fe3O4 to α-Fe2O3 after annealing at temperatures of 500 to 500°C in air. An increase in the annealing temperature increased the particle size, resulting in a decrease in the NO2-gas sensitivity. These results suggest that the NO2 sensitivity of W-doped Fe2O3 film depends on the particle size.

Selective, peroxidase substrate based "signal-on" colorimetric assay for the detection of chromium (VI)

Due to the potentially adverse effects of the chromium (VI) on the human health and also on the environment, the quantitative determination of Cr(VI) is of particular interest. This work herein reports a facile, selective and rapid colorimetric determination of Cr(VI) based on the peroxidase substrate-2,2'-azino-bis(3-ethylbenzo-thiazoline-6-sulfonic acid) diammonium salt (ABTS) as the color developing agent. ABTS, which was usually acted as peroxidase substrate for the enzyme linked immunosorbent assay, is used here for the first time to fabricate the "signal-on" colorimetric Assay for Cr(VI).

Bluish-white emission from radical carbonyl impurities in amorphous Al2O3 prepared via the Pechini-type sol-gel process

Many efforts have been devoted to exploring novel luminescent materials that do not contain expensive or toxic elements, or do not need mercury vapor plasma as the excitation source. In this paper, amorphous Al2O3 powder samples were prepared via the Pechini-type sol-gel process. The resulting samples were characterized by X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, field emission scanning electron microscopy (FESEM), photoluminescence (PL) excitation and emission spectra, kinetic decay, and electron paramagnetic resonance (EPR).

Failure of the plasma-sprayed coating of lanthanum hexaluminate

Lanthanum magnesium hexaluminate (LaMgAl11O19, LMA) is an attractive material for thermal barrier coatings (TBCs), and the failure of its coating was studied in this work by thermal cycling, X-ray diffraction, dilatometric measurement and thermal gravimetric-differential thermal analysis. The dilatometric measurement indicates that even though the bulk material of LMA has a higher sintering-resistance than the typical TBC material, i.e. yttria-stabilized zirconia (YSZ), the plasma sprayed coating of LMA has two serious contractions due to the re-crystallization of LMA and phase transitions of alumina.

Thermal-shock resistance of LnMgAl(11)O(19) (Ln = La, Nd, Sm, Gd) with magnetoplumbite structure

Lanthanide hexaaluminates including LaMgAl11O19, NdMgAl11O19, SmMgAl11O19 and GdMgAl11O19 were synthesized via Sol-Gel method. Due to the anisotropic crystal growth, these oxides crystallize in the form of platelets and the platelet thickness increases with the decrease of rare-earth ionic radius. It was observed that the thermal-shock resistances of LaMgAl11O19, NdMgAl11O19 and SmMgAl11O19 oxides were superior to 8YSZ as proved by water quenching tests. In addition, the thinner the platelet. the more interstices are retained in the sintered specimen, and the better thermal-shock resistance the oxide has. Based on SEM images, it can be seen that the SmMgAl11O19 sample exhibits a mixture of the intergranular and transgranular fracture after thermal cycling failure.

Hot-corrosion behaviors of overlay-clad yttria-stabilized zirconia coatings in contact with vanadate-sulfate salts

A dense clad overlay with chemical inertness was achieved on top of the plasma-sprayed YSZ thermal barrier coatings by laser in order to protect them from hot-corrosion attack. The Al2O3-clad YSZ coating exhibited good hot-corrosion behavior in contact with salt mixture of vanadium pentoxide (V2O5) and sodium sulfate (Na2SO4) for a longtime of 100 h at 1173 K. The LaPO4-clad YSZ coating showed corrosion resistance inferior to the Al2O3-clad one. Yttria was leached from YSZ by reaction between Y2O3 and V2O5, which caused progressive destabilization transformation of YSZ from tetragonal (t) to monoclinic (m) phase. The chemical inertness of the clad layers and the restrained infiltration of the molten corrosive salts by the dense clad layers were primary contributions to improvement of the hot-corrosion resistances.

Orientation of Syndiotactic Polystyrene Crystallized in Cylindrical Nanopores

Syndiotactic polystyrene (sPS) nanorods with different diameters have been prepared by using anodic aluminum oxide templates, and the orientation of the sPS crystals in the nanorods has been investigated by FT-IR spectroscopy. It is found that the c axis of the beta' crystals preferentially oriented perpendicular to the axis of the nanorod, and the degree of orientation is lower as the diameter of the nanorod decreases. This unexpected result is attributed to nuclei formed at the surface of the nanopores and their subsequent growth, in addition to the preferential growth compatible with the pore direction by the nuclei formed in the bulk film and in the nanorods.

Crystallization and orientation of syndiotactic polystyrene in nanorods

Syndiotactic polystyrene (sPS) nanorods of 200 and 80 nm diameters were prepared by infiltrating porous anodic alumina oxide templates with polymer melt, and the crystallinity and orientation of various forms of sPS crystals in the nanorods were studied by FTIR spectroscopy and electron diffraction. For sPS crystallized from amorphous state at lower temperatures, a-form crystals were found in the nanorods with random orientation and the same degree of crystallinity as that in the bulk. However, for sPS crystallized from molten state at 260 degrees C, while no preferred orientation was found for the chains in the melt, the beta-crystals formed in the nanorods oriented preferentially with the c-axis aligning perpendicular to the axial direction of the nanorod, and the degree of crystallinity was significantly lower than that in the bulk. The crystallinity decrease was more profound for nanorods of smaller diameter. These results were also supported by electron diffraction data and can be attributed to competition between nucleation and crystal growth in the nanotemplates.

Ceramic materials for thermal barrier coatings

This paper summarizes the basic properties of ceramic materials for thermal barrier coatings. Ceramics, in contrast to metals, are often more resistant to oxidation, corrosion and wear, as well as being better thermal insulators. Except yttria stabilized zirconia, other materials such as lanthanum zirconate and rare earth oxides are also promising materials for thermal barrier coatings.

Synthesis and photoluminescence of the Y2O3 : Eu3+ phosphor nanowires in AAO template

The monodisperse array and nanowires Of Y2O3:Eu3+ phosphor were synthesized using anodic aluminum oxide (AAO) template by sol-gel method. Scanning electron microscope (SEM) images indicated that Y2O3:Eu3+ nanowires are parallelly arranged, all of which are in uniform diameter of about 50 nm. The high-magnification SEM image showed that each nanowire is composed of a lot of agglutinating particles. The patterns of selected-area electron diffraction confirmed that Y2O3:EU3+ nanowires mainly consist of polycrystalline materials. Excitation and emission spectra Of Y2O3:E U3+/AAO composite films were measured. The characteristic red emission peak of EU3+ ion attributed to D-5(0)-->F-7(2) transition in Y2O3:EU3+/AAO nanowires broadened its halfwidth.

微孔-介孔复合SiO2-Al2O3分子筛的水热合成研究

中国科学院山西煤炭化学研究所