Hydrothermal stability and catalytic activity of aluminum-containing mesoporous ethane-silicas

Aluminum was incorporated into the mesoporous framework of ethane-silica by one-pot condensation of Al(OiPr)(3) with 1,2-bis(trimethoxysilyl)ethane using octadecyltrimethylammonium chloride as surfactant. Powder X-ray diffraction patterns, nitrogen sorption analysis, and TEM results reveal the formation of an ordered mesoporous material with uniform porosity. Al-27 MAS NMR confirms the incorporation of aluminum in the framework. The synthesized materials exhibit extremely high hydrothermal stability in boiling water (no obvious change of mesostructure and textural properties was observed even after refluxing in water for 100 h), which could be mainly contributed to the ethane-bridged mesoporous framework. The aluminum-containing mesoporous ethane-silicas are efficient catalysts for the alkylation of 2,4-di-tert-butylphenol by cinnamyl alcohol to yield a flavan.

Synthesis and spectroscopic study of mesoporous aluminum methylphosphonate foam templated by dibutyl methylphosphonate

New types of templates and novel interactive mechanisms between template and framework are very important for creating porous materials. In this work, by using neutral dibutyl methylphosphonate as a template, an inorganic-organic hybrid mesoporous material, aluminum methylphosphonate, was prepared. The as-synthesized material was studied by P-31 magnetic angle spinning nuclear magnetic resonance (MAS NMR), Al-27 MAS NMR, C-13 CP/MAS, FT-IR spectroscopy, thermogravimetry (TG), differential thermal analysis (DTA), and transmission electron microscopy. After thermal treatment at 673 K and 10 mmHg for 2 h, hybrid mesoporous foam was obtained. The transformation process was investigated by FT-IR. TG-DTA results indicate that the methyl group bonded to the framework keeps intact up to 792 K under air and 823 K under nitrogen. The characterization results from nitrogen gas adsorption-desorption measurements show that the BET surface area and the Barrett-Joyner-Halenda desorption cumulative pore volume of the foam are 90 m(2) g(-1) and 0.32 cm(3) g(-1) respectively. (C) 2003 Elsevier Inc. All rights reserved.

Structure of an unexpected trimer from the reaction of ageratochromene II with aluminum chloride

A new trimer from the reaction of ageratochromene [1] (6,7-dimethoxy-2,2-dimethyl-1-benzopyran) with anhydrous aluminum chloride was shown to be 3,4-dihydro-6,7-dimethoxy-2,2-dimethyl-3-(6',7'-dimethoxy-2',2'-di-methyl-2H-1-benzopyran-4'-yl)-4-(3" 4"-dihydro-6", 7"-dimethoxy-2",2"-dimethyl-2H-1-benzopyran-3"-yl)-2H-1-benzopyran. Its structure was confirmed by NMR (H-1, C-13, DEPT-135. COSY, HMBC, HSQC, TOCSY and NOESY), IR, mass spectra and elemental analysis. Copyright (C) 2002 John Wiley Sons, Ltd.

Cesium hydroxide doped tris-(8-hydroxyquinoline) aluminum as an effective electron injection layer in inverted bottom-emission organic light emitting diodes

We demonstrate highly efficient inverted bottom-emission organic light-emitting diodes (IBOLEDs) by using cesium hydroxide (CsOH) doped tris-(8-hydroxyquinoline) aluminum (Alq(3)) as the electron injection layer on indium tin oxide cathode, which could significantly enhance the electron injection, resulting in a large increase in luminance and efficiency. The maximum luminance, current efficiency, and power efficiency reach 21 000 cd/cm(2), 6.5 cd/A, and 3.5 lm/W, respectively, which are 40%-50% higher in efficiency than that of IBOLEDs with cesium carbonate (Cs2CO3) doped Alq(3) as the electron injection layer, where the efficiencies are only 4.5 cd/A and 2.2 lm/W.

Origin of negative differential resistance and memory characteristics in organic devices based on tris(8-hydroxyquinoline) aluminum

Negative differential resistance (NDR) and memory phenomenon have been realized in current-voltage (I-V) characteristics of indium tin oxide/tris(8-hydroxyquinoline) aluminum/aluminum devices. The I-V curves have been divided into three operational regions that are associated with different working regimes of the devices: (i) bistable region, (ii) NDR region, and (iii) monotonic region. The bistable region disappeared after a couple of voltage sweeps from zero to a positive voltage. The bistable nature can be reinstated by applying a suitable negative voltage.