Heat capacity enhancement and thermodynamic properties of nanostructured amorphous SiO2

The heat capacity of nanostructured amorphous SiO2 (na-SiO2) has been measured by adiabatic calorimetric method over the temperature range 9-354 K. TG and differential scanning calorimeter (DSC) were also employed to determine the thermal stability. Glass transition temperature (T-g) for the two same grain sizes with different specific surface of naSiO(2) samples and one coarse-grained amorphous SiO2 (ca-SiO2) sample were determined to be 1377, 1397 and 1320 K, respectively. The low temperature experimental results show that there are significant heat capacity (C-P) enhancements among na-SiO2 samples and ca-SiO2. Entropy, enthalpy, Gibbs free energy and Debye temperature (theta (D)) were obtained based on the low temperature heat capacity measurement of na-SiO2. The Cp enhancements of na-SiO2 were discussed in terms of configurational and vibrational entropy. (C) 2001 Elsevier Science B.V. All rights reserved.

Enhancement of molar heat capacity of nanostructured Al2O3

The nanosized alumina prepared by the hydrolysis method with an average particle size of 20 nm was characterized by X-ray diffraction. The heat capacity measurements of the prepared sample were carried out using an adiabatic calorimeter in the temperature range from 78 to 370 K. Enhancement of heat capacity was observed in the nanostructured materials as the heat capacity data were compared with those of the corresponding coarse-grained materials. The enhanced heat capacity was discussed on the basis of experiments. Differential scanning calorimetry and thermogravimetry were used to determine the thermal stability of the nanostructured alumina.

Low temperature specific heat and thermal stability of Fe-B ultrafine amorphous alloy particles

Fe-B ultrafine amorphous alloy particles (UFAAP) were prepared by chemical reduction of Fe3+ with NaBHO4 and confirmed to be ultrafine amorphous particles by transmission electron microscopy and X-ray diffraction. The specific heat of the sample was measured by a high precision adiabatic calorimeter, and a differential scanning calorimeter was used for thermal stability analysis. A topological structure of Fe-B atoms is proposed to explain two crystallization peaks and a melting peak observed at T=600, 868 and 1645 K, respectively.

Calorimetric study of Wood alloy

The heat capacities of Wood alloy have been measured with an automatic adiabatic calorimeter over the temperature range of 80 similar to 360 K. The thermodynamic data of solid-liquid phase transition have been obtained from the heat capacity measurements. The melting temperature, enthalpy and entropy of fusion of the substance are 345.662 K, 18.47 J.g(-1) and 0.05343 J.g(-1).K-1, respectively. The necessary thermal data are provided for the low temperature thermodynamic study of the alloy.

Heat capacity and thermochemical study of trifluoroacetamide (C2H2F3NO)

The low-temperature heat capacities of trifluoroacetamide were precisely determined with a small sample precision automated adiabatic calorimeter over the temperature range from 78 to 404 K. A solid-to-solid phase transition, a fusion and a phase transition from a liquid crystalline phase to fully liquid phase have been observed at the temperatures of 336.911+/-0.102, 347.622+/-0.094 and 388.896+/-0.160 K, respectively. The molar enthalpies of these phase transitions as well as the chemical purity of the substance were determined to be 5.576+/-0.004, 11.496+/-0.007, 1.340+/-0.005 kJ mol(-1) and 99.30 mol%, respectively, on the basis of the heat capacity measurements. The molar entropies of the three phase transitions were calculated to be 16.550+/-0.012, 33.071+/-0.029 and 3.447+/-0.027 J mol(-1) K-1, respectively. Further researches of the thermochemical properties for this compound have been carried out by means of TG and DSC techniques. (C) 2000 Elsevier Science B.V. All rights reserved.

Heat capacities of Al62.5Cu25Fe12.5 quasicrystals and B2 related crystals

The heat capacities of two Al62.5Cu25Fe12.5 samples containing icosahedral quasicrystals and B2 related crystals respectively were measured with a high-precision automatic adiabatic calorimeter over the temperature range of 75-385 K. The heat capacities of both samples increase with temperature. At the low temperature range, the heat capacity of the quasicrystalline sample is higher than that of the B2 approximate. However, the heat capacity of the B2 sample becomes higher above 254.987 K. (C) 1999 Elsevier Science B.V. All rights reserved.

Characterization and thermodynamic study of ultra-fine particle of Ni-B amorphous alloy

Ultra-fine particle of Ni-B amorphous alloy was prepared by chemical reduction of Ni2+ with NaBH4 and characterized with TEM and XRD. The heat capacity and thermal stability were measured with a high-precision automatic adiabatic calorimeter and DTA. The upper limit of applied temperature of the substance was found to be 684 K for use as catalyst. (C) 1999 Elsevier Science B.V. All rights reserved.

Low-temperature heat capacity and phase transition of n-hexatriacontane

The heat capacities of crystalline and liquid n-hexatriacontane were measured with an automatic adiabatic calorimeter over the temperature range of 80-370 K. Two solid-to-solid phase transitions at the temperatures of 345.397 and 346.836 K, and a fusion at the temperature of 348.959 K have been observed. The enthalpies and entropies of these phase transitions as well as the chemical purity of the substance were determined on the basis of the heat capacity measurements. Thermal decomposition temperatures of the compound were measured by thermogravimetric analysis. (C) 1999 Elsevier Science B.V. All rights reserved.

Heat capacity and thermodynamic properties of N-(2-cyanoethyl) aniline (C9H10N2)

The low temperature heat capacities of N-(2-cyanoethyl)aniline were measured with an automated adiabatic calorimeter over the temperature range from 83 to 353 K. The temperature corresponding to the maximum value of the apparent heat capacity in the fusion interval, molar enthalpy and entropy of fusion of this compound were determined to be 323.33 +/- 0.13 K, 19.4 +/- 0.1 kJ mol(-1) and 60.1 +/- 0.1 J K-1 mol(-1), respectively. Using the fractional melting technique, the purity of the sample was determined to be 99.0 mol% and the melting temperature for the tested sample and the absolutely pure compound were determined to be 323.50 and 323.99 K, respectively. A solid-to-solid phase transition occurred at 310.63 +/- 0.15 K. The molar enthalpy and molar entropy of the transition were determined to be 980 +/- 5 J mol(-1) and 3.16 +/- 0.02 J K-1 mol(-1), respectively. The thermodynamic functions of the compound [H-T - H-298.15] and [S-T - S-298.(15)] were calculated based on the heat capacity measurements in the temperature range of 83-353 K with an interval of 5 K. (c) 2004 Elsevier B.V. All rights reserved.

Low temperature heat capacity of (S)-ibuprofen

Molar heat capacities of ( S)-ibuprofen were precisely measured with a small sample precision automated adiabatic calorimeter over the temperature range from 80 to 370 K. Experimental heat capacities were fitted into a polynomial equation of heat capacities ( C-p,C- m) with reduced temperature ( X), [ X = f(T)]. The polynomial equations for ( S)-ibuprofen were C-p,C- m(s) = - 39.483 X-4 - 66. 649 X-3 + 95. 196 X-2 + 210. 84 X + 172. 98 in solid state and C-p,C- m(L) = 7. 191X(3) + 4. 2774 X-2 + 56. 365 X + 498. 5 in liquid state. The thermodynamic functions relative to the reference temperature of 298. 15 K, H-T - H-298.15 and S-T - S-298.15, were derived for the( S)-ibuprofen. A fusion transition at T-m = (324. 15 +/- 0. 02) K was found from the C-p - T curve. The molar enthalpy and entropy of the fusion transition were determined to be (18. 05 +/- 0. 31) kJ.mol(-1) and (55. 71 +/- 0. 95) J.mol(-1).K-1, respectively. The purity of the ( S)-ibuprofen was determined to be 99. 44% on the basis of the heat capacity measurement. Finally, the heat capacities of ( S)-ibuprofen and racemic ibuprofen were compared.

Measurements of the heat capacity of an azeotropic mixture of water and n-butanol from 78 to 320 K

Molar heat capacities of n-butanol and the azeotropic mixture in the binary system [water (x=0.716) plus n-butanol (x=0.284)] were measured with an adiabatic calorimeter in a temperature range from 78 to 320 K. The functions of the heat capacity with respect to thermodynamic temperature were established for the azeotropic mixture. A glass transition was observed at (111.9 +/- 1.1) K. The phase transitions took place at (179.26 +/- 0.77) and (269.69 +/- 0.14) K corresponding to the solid-liquid phase transitions of. n-butanol and water, respectively. The phase-transition enthalpy and entropy of water were calculated. A thermodynamic function of excess molar heat capacity with respect to temperature was established, which took account of physical mixing, destructions of self-association and cross-association for n-butanol and water, respectively. The thermodynamic functions and the excess thermodynamic ones of the binary systems relative to 298.15 K were derived based on the relationships of the thermodynamic functions and the function of the measured heat capacity and the calculated excess heat capacity with respect to temperature.

Heat capacity and thermodynamic properties of myclobutanil

The low-temperature heat capacities of myclobutanil (C15H17CIN4) were precisely measured with an automated adiabatic calorimeter over the temperature range from 78 to 368 K. The sample was observed to melt at (348.800 +/- 0.06) K. The molar enthalpy and entropy of the melting as well as the chemical purity of the substance were determined to be Delta(fus)H(m) = (30931 +/- 11) J.mol(-1), Delta(fus)S(m) = (88.47 +/- 0.02) J.mol(-1).K-1 and 99.41%, respectively. Further research of the melting process for this compound was carried out by means of DSC technique. The result was in agreement with that obtained from the measurements of heat capacities.

Heat capacity and enthalpy of fusion of fenoxycarb

Fenoxycarb was synthesized and its heat capacities were precisely measured with an automated adiabatic calorimeter over the temperature range from 79 to 360 K. The sample was observed to melt at (326.31 +/- 0.14) K. The molar enthalpy and entropy of fusion as well as the chemical purity of the compound were determined to be (26.98 +/- 0.04) kJ-mol(-1), (82.69 +/- 0.09) J-K-1-mol(-1) and 99.53% +/- 0.01%, respectively. The thermodynamic functions relative to the reference temperature (298.15 K) were calculated based on the heat capacity measurements in the temperature range between 80 and 360 K. The extrapolated melting temperature for the absolutely pure compound obtained from fractional melting experiments was (326.62 +/- 0.06) K. Further research on the melting process of this compound was carried out by means of differential scanning calorimetry technique. The result was in agreement with that obtained from the measurements of heat capacities.

Thermodynamic properties of ethanol and gasoline blended fuel

The heat capacities (C-p) of five types of gasohol (50 wt % ethanol and 50 wt % unleaded gasoline 93(#) (E50), 60 wt % ethanol and 40 wt % unleaded gasoline 93(#) (E60), 70 wt % ethanol and 30 wt % unleaded gasoline 93(#) (E70), 80 wt % ethanol and 20 wt % unleaded gasoline 93(#) (E80), and 90 wt % ethanol and 10 wt % unleaded gasoline 93(#) (E90), where the "93" denotes the octane number) were measured by adiabatic calorimetry in the temperature range of 78-320 K. A glass transition was observed at 95.61, 96.14, 96.56, 96.84, and 97.08 K for samples from the E50, E60, E70, E80, and E90 systems, respectively. A liquid-solid phase transition and a solid-liquid phase transition were observed in the respective temperature ranges of 118-153 and 155-163 K for E50, 117-150 and 151-164 K for E60, 115-154 and 154-166 K for E70, 113-152 and 152-167 K for E80, and 112-151 and 1581-167 K for E90. The polynomial equations of Cp and the excess heat capacities (C-p(E)), with respect to the thermodynamic temperature, were established through least-squares fitting. Based on the thermodynamic relationship and the equations obtained, the thermodynamic functions and the excess thermodynamic functions of the five gasohol samples were derived.