Sol-gel-derived BPO4/Ba2+ as a new efficient and environmentally-friendly bluish-white luminescent material

In this paper, BPO4 and Ba2+-doped BPO4 powder samples were prepared by the sol-gel process using glycerol and poly(ethylene glycol) as additives. The structure and optical properties of the resulting samples were characterized by X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, field emission scanning electron microscopy (FESEM), diffuse reflection spectra, photoluminescence (PL) excitation and emission spectra, quantum yield, kinetic decay, and electron paramagnetic resonance (EPR), respectively. It was found that the undoped BPO4 showed a weak purple blue emission (409 nm, lifetime 6.4 ns) due to the carbon impurities involved in the host lattice. Doping Ba2+ into BPO4 resulted in oxygen-related defects as additional emission centers which enhanced the emission intensity greatly (> 10x) and shifted the emission to a longer-wavelength region (lambda(max) = 434 nm; chromaticity coordinates: x = 0.174, y = 0. 187) with a bluish-white color. The highest emission intensity was obtained ;when doping 6 mol % Ba2+ in BPO4, which has a quantum yield as high as 31%. The luminescent mechanisms of BPO4 and Ba2+-doped BPO4 were discussed in detail according to the existing models for silica-based materials.

耐甲醇氧还原复合催化剂四苯基铁卟啉-铂的研究

用平衡吸附法制备了炭载四苯基铁卟啉 铂 (FeTPP Pt/C)复合催化剂 ,比较了经不同温度热处理的FeTPP Pt/C和Pt/C对O2 还原的催化活性和耐甲醇能力。结果表明 ,热处理可改善Pt/C催化剂的耐甲醇能力 ;热处理的FeTPP Pt/C复合催化剂具有较高的氧还原催化活性和良好的耐甲醇能力 ,并且 70 0℃处理的FeTPP Pt/C对O2 还原的催化活性最高。

Synthesis, structure and ionic conductivity of La2/3-xLi3xMoO4

A series of compounds, La2/3 - xLi3xMoO4, were first prepared. Their structures are tetragonal scheelites with the cationic defects. The cell parameters a, c and values of c/a decrease with the increasing of the substitution amount (3x) of lithium ion. Cationic vacancies are getting more as Li+ concentration is lower. The diffusion of lithium ion is predominant. The concentration of charge carriers increases with increasing the substitution amount (3x) of lithium ion, meanwhile, the concentration of cationic vacancies decreases. The conductivity approaches the best when the substitution amount (3x) of lithium ion is about 0.3. The conductivity of La0.567Li0.3MoO4 is 6.5 x 10(-6) S . cm(-1) at room temperature.

Synthesis and characterization of sandwiched heteropolycompound

New complex K5O4Na4H5 [Sn-3(PW9O34)(2)]. 16N(2)O was prepared and its structure was determined by elemental analysis, IR, P-31, W-183 NMR, polarography, XPS and X-ray crystallography. The anion has A-alpha-Keggin structure. The new complex crystallize is the monoclinic, P2(1)/n with a = 1.3625 (3) nm, b = 2.3625 (5) nm, c = 2.9306 (6) nm, alpha = 90 degrees, beta = 99.67 (3)degrees, gamma = 90 degrees, V = 9.299 nm(3), Z = 4.

夹心杂多化合物的合成及晶体结构

PW_9O_(34)~(9-)(简写PW_9)阴离子可以与Sn~(4+)反应生成[Sn_3~Ⅳ(PW_9O_(34))_2]~(6-)杂多化合物.标题化合物经元素分析、红外、极借、~(31)P和~(183)W核磁共振谱、X射线光电子能谱及X射线单晶测定了结构.K_5O_4Na_4H_5[Sn_3(PW_9O_(34))_2]·16H_2O的单晶是单斜晶系,空间群P2_1/n,晶胞参数a=1.3625(3)nm,b=2.3625(5)nm,c=2.9306(6)nm,α=90°,β= 99.67(3)°,γ=90°,V=9.299nm~3,Z=4.它是一种三个Sn~(4+)在两个PW_9单元间的夹心结构.

Electrochemistry of heteropolyanions in coulombically linked self-assembled monolayers

A composite film containing heteropolyanion was fabricated on gold by attaching the Keggin-type heteropolyanion, PMo12O403- on a 4-aminothiophenol SAM via Au-S bonding. Reflection FTIR, cyclic voltammetry and XPS were used for the characterization of the composite film. Reflection FTIR studies indicate that there is some Coulombic interaction between PMo12O403- and the surface amino group in the composite film, which greatly improves the film stability and prevents effectively the destructive intermolecular aggregation. The composite him shows three reversible redox couples within the pH range pH less than or equal to 7.0, attributed to three two-electron and two-proton electrochemical reduction-oxidation processes of PMo12O403-. Compared with PMo12O403- in the solution, the PMo12O403- of the composite film electrode can exist in a larger pH range, and shows smaller peak-to-peak separation, and more reversible reaction kinetics. Moreover, the composite him obtained shows a good catalytic activity for the reduction of BrO3-. (C) 1998 Elsevier Science S.A. All rights reserved.

甲烷氧化偶联含锂多元复合氧化物催化剂的失活机理

对甲烷氧化偶联反应活性较高的多元复合氧化物催化剂（Ｌｉ－Ｔｉ－Ｌａ．Ｌｉ－Ｍｎ－Ｌａ，Ｌｉ－Ｎｉ－Ｌａ）的稳定性和失活机理进行了初步探讨，利用ＸＲＤ，ＩＲ，ＸＰＳ和Ｏ２－ＴＰＤ等方法对催化剂进行了表征．结果表明，催化剂在高温及反应气氛的作用下，由于表面锂的流失，使体相晶格中的锂向表面扩散，导致含锂活性相结构的分解（或部分分解），从而减少了体相及表相氧空位和活性氧种的数量，降低了晶格氧的活动性，致使催化剂活性降低.

THE SYNTHESIS AND CRYSTAL-STRUCTURE OF [LA(OH2)(5)(PHEN)(2)]CL-3-CENTER-DOT-4H(2)O-CENTER-DOT-PHEN

[La(OH2)(5)(phen)(2)]Cl-3 4H(2)O.phen is centric, Pnna, with a = 19.946(7), b = 16.458(5), c = 12.207(4)Angstrom and D-calc = 1.57 g cm(-3) for Z = 4. The La(III) ion resides on a crystallographic twofold axis and is coordinated to four nitrogen atoms (fr

STRUCTURE OF [LA(NO3)(3)(OH2)(2)(OHME)(BIPY)].15-CROWN-5

[La(NO3)(3)(OH2)(2)(OHMe)(bipy).15-crown-5 is monoclinic, P2(1)/n, with a = 11.239(6), b = 19.302(7), c = 14.458(8) Angstrom, beta = 92.47(5)degrees, and D-calc = 1.63 g cm(-3) for Z = 4. In the complex, two nitrogen atoms (from bipy) and nine oxygen atom

水溶性聚合物和两亲聚合物19．磺化液体聚丁二烯──种新型液膜用表面活性剂

一种新的聚工二烯型表面活性剂ＬＹＦ经液体聚了二烯磺化方法制备而得，并应用于液膜分离研究之中。发现无论内水相是酸性还是碱性，由该表面活性剂制得的Ｗ／Ｏ型乳状液在稳定性、溶胀率和破乳诸方面均具有令人满意的综合性能。为深入了解液膜的稳定性，我们测定了处于两种水相间的双分子膜的强度。发现由ＬＹＦ所形成的双分子膜具有最大的膜强值，优于聚异丁烯型的表面活性剂ＥＣＡ４３６０和ＥＭ３０１．

X-射线荧光分析中薄膜试样的面积和厚度对分析结果的影响

本文就薄膜法制样、用X-射线荧光谱法分析稀土样品时,试样面积和厚度对分析结果产生的影响作了定量研究,提出的有关分析条件和参数用于实际样品分析中,获得了满意的分析结果。

掺W对Bi系中高Tc超导相的影响

自Maeda发现高Tc超导体BiSrCaCuO以来,引起了人们广泛兴趣;由于它有较高的超导转变温度(Tc>100K),无剧毒、价廉和自高温冷却到室温无结构相变等特点,Bi系是一很有实用前景的高Tc超导体;已经确定Bi系中含有三个超导相(2201,2212,2223相),但是迄今要制得较纯的2223高Tc相还有一定困难,无疑这对它的基础研究和实用开发都受到了限制,因此制备更纯的Bi系2223相具有重要的意义。

PREPARATION AND MOLECULAR-STRUCTURE OF METHYLBIS(TERT-BUTYLCYCLOPENTADIENYL)NEODYMIUM AND METHYLBIS(TERT-BUTYLCYCLOPENTADIENYL)GADOLINIUM

Bis(t-butylcyclopentadienyl)lanthanide chloride (Ln = Nd or Gd) reacts with one equivalent of methyllithium in ether/tetrahydrofuran to give the complex [(C5H4tBu)2LnCH3]2 (Ln = Nd or Gd). The structure of [(C5H4tBu)2NdCH3]2 has been determined by X-ray analysis. The crystals are monoclinic of space group Cm with a = 9.538(2), b = 23.298(4), c = 9.505(3) angstrom, beta = 119.53(2)-degrees, V = 1828.0(7) angstrom 3, D(calc.) = 1.458 g/cm3 and Z = 2 for the dimer. The two (C5H4tBu)2Nd units in the dimer are connected by asymmetrical methyl bridges with independent Nd-C bond lengths of 2.70(2) and 2.53(2) angstrom and Nd-C-Nd angles of 94.7(9) and 87.3(6)-degrees.

杂多化合物催化性能的研究——在相转移条件下由十二钨磷杂多酸钠催化的H_2O_2分解反应动力学和机理

在相转移条件下研究了由Na_2HPW_(12)O_(40)(简写为PW_(12))催化的H_2O_2分解反应动力学。相转移催化剂氯代十六烷基吡啶与H_2O_2作用生成的含活性氧的中间化合物,在CHCl_3中溶解度很大但不稳定,可分解放出氧气。在此基础上,深入分析了两相反应的特点,提出了反应机理,首次推导出其反应动力学方程,并验证了与实验结果的一致性。

乙丙共聚物及其共混物晶型探讨

用广角X-射线衍射(WAXD)和偏光显微镜(PLM)方法,研究了具有乙丙长序列乙丙共聚物及其共混物,发现通过熔融慢冷结晶样品,C_3含量在30mol％以上,衍射角2θ=20°处出现了属于γ-PP晶型的(140),(130)晶面衍射。含有乙丙长序列链结构的乙丙共聚物及共混物属(α+γ)混晶结构;含乙丙长序列的EPR以γ-相为主,嵌段物和共混物则以α-PP为主,形成γ-PP结构的必要条件是含有乙丙长序列链结构样品熔融慢冷结晶。