Characterization of porous silicon nitride/silicon oxynitride composite ceramics produced by sol infiltration

Porous silicon nitride/silicon oxynitride composite ceramics were fabricated by silica sol infiltration of aqueous gelcasting prefabricated Si3N4 green compact. Silica was introduced by infiltration to increase the green density of specimens, so suitable properties with low shrinkage of ceramics were achieved during sintering at low temperature. Si2N2O was formed through reaction between Si3N4 and silica sol at a temperature above 1550 degrees C. Si3N4/Si2N2O composite ceramics with a low linear shrinkage of 1.3-5.7%, a superior strength of 95-180 MPa and a moderate dielectric constant of 4.0-5.0 (at 21-39 GHz) were obtained by varying infiltration cycle and sintering temperature. (C) 2010 Published by Elsevier B.V.

Methanol synthesis from CO2 using a silicone rubber/ceramic composite membrane reactor

A one-dimensional isothermal pseudo-homogeneous parallel flow model was developed for the methanol synthesis from CO2 in a silicone rubber/ceramic composite membrane reactor. The fourth-order Runge-Kutta method was adopted to simulate the process behaviors in the membrane reactor. How those parameters affect the reaction behaviors in the membrane reactor, such as Damkohler number Da, pressure ratio p(r), reaction temperature T, membrane separation factor alpha, membrane permeation parameter phi , as well as the non-uniform parameter of membrane permeation L-1, were discussed in detail. Parts of the theoretical results were tested and verified; the experimental results showed that the conversion of the main reaction in the membrane reactor increased by 22% against traditional fixed bed reactor, and the optimal non-uniform parameter of membrane permeation rate, L-1.opt ,does exist. (C) 2003 Elsevier B.V All rights reserved.

Polymeric fullerene oxide films produced by decomposition of hexanitro[60]fullerene

A new poly(fullerene oxide) thin film material has been fabricated by thermal activation and electron bombardment on hexanitro[60]fullerene (HNF) film deposited on a An substrate, all under vacuum conditions. The reaction products in the polymerization process are analyzed by XPS, UPS, IR, TGA-MS and LDI-MS techniques. It is found that the main effect of thermal and radiation treatments is to induce cleavage of -NO bonds from HNF molecules resulted in the release of nitric oxide gas and the formation of fullerene-bound oxyradicals, C-60-C-6. Spectroscopic evidence strongly suggests that rearrangement of fullerenic nitro moieties into nitrito groups is involved in the HNF decomposition process prior to the generation of reactive oxyradical intermediates. Consequently, the intermolecular coupling reaction of these oxyradicals leads to carbon polymer networks containing oxygen-bridged fullerenes. The thermally generated polymeric thin film is stable up to 900 K. Electron bombardment is also effective in both the decomposition of -NO2 groups and the removal of -OH groups present in HNF films. UV irradiation at 365 nm alone is shown to be not as efficient for the polymer formation. (C) 2003 Elsevier Ltd. All rights reserved.