Upgrading of liquid fuel from the vacuum pyrolysis of biomass over the Mo-Ni/gamma-Al2O3 catalysts

High amounts of acid compounds in bio-oil not only lead to the deleterious properties such as corrosiveness and high acidity, but also set up many obstacles to its wide applications. By hydrotreating the bio-oil under mild conditions, some carboxylic acid compounds could be converted to alcohols which would esterify with the unconverted acids in the bio-oil to produce esters. The properties of the bio-oil could be improved by this method. In the paper, the raw bio-oil was produced by vacuum pyrolysis of pine sawdust. The optimal production conditions were investigated. A series of nickel-based catalysts were prepared. Their catalytic activities were evaluated by upgrading of model compound (glacial acetic acid). Results showed that the reduced Mo-10Ni/gamma-Al2O3 catalyst had the highest activity with the acetic acid conversion of 33.2%. Upgrading of the raw bio-oil was investigated over reduced Mo-10Ni/gamma-Al2O3 catalyst. After the upgrading process, the pH value of the bio-oil increased from 2.16 to 2.84. The water content increased from 46.2 wt.% to 58.99 wt.%. The H element content in the bio-oil increased from 6.61 wt.% to 6.93 wt.%. The dynamic viscosity decreased a little. The results of GC-MS spectrometry analysis showed that the ester compounds in the upgraded bio-oil increased by 3 times. it is possible to improve the properties of bio-oil by hydrotreating and esterifying carboxyl group compounds in the bio-oil.

Partial oxidation reforming of biomass fuel gas over nickel-based monolithic catalyst with naphthalene as model compound

With naphthalene as biomass tar model compound, partial oxidation reforming (with addition of O-2) and dry reforming of biomass fuel gas were investigated over nickel-based monoliths at the same conditions. The results showed that both processes had excellent performance in upgrading biomass raw fuel gas. Above 99% of naphthalene was converted into synthesis gases (H-2+CO). About 2.8 wt% of coke deposition was detected on the catalyst surface for dry reforming process at 750 degrees C during 108 h lifetime test. However, no Coke deposition was detected for partial oxidation reforming process, which indicated that addition of O-2 can effectively prohibit the coke formation. O-2 Can also increase the CH4 conversion and H-2/CO ratio of the producer gas. The average conversion of CH4 in dry and partial oxidation reforming process was 92% and 95%, respectively. The average H-2/CO ratio increased from 0.95 to 1.1 with the addition of O-2, which was suitable to be used as synthesis gas for dimethyl ether (DME) synthesis.