Polyaniline for corrosion prevention of mild steel coupled with copper

Polyaniline emeraldine base/epoxy resin (EB/ER) coating was investigated for corrosion protection of mild steel coupled with copper in 3.5% NaCl solution. EB/ER coating with 5-10 wt% EB had long-term corrosion resistance on both uncoupled steel and copper due to the passivation effect of EB on the metal surfaces. During the 150 immersion days, the impedance at 0.1 Hz for the coating increased in the first 1-40 days and subsequently remained constant above 10(9) Omega cm(2), whereas that for pure ER coating fell below 10(6) Omega cm(2) after only 30 or 40 days. Immersion tests on coated steel-copper galvanic couple showed that EB/ER coating offered 100 times more protection than ER coating against steel dissolution and coating delamination on copper, which was mainly attributed to the passive metal oxide films formed by EB blocking both the anodic and cathodic reactions. Salt spray tests showed that 100 mu m EB/ER coating protected steel-copper couple for at least 2000 h.

Mechanism and life study on polyaniline anti-corrosion coating

Solvent free polyaniline emeraldine base(EB) corrosion protection coating was prepared, employing aliphatic polyamine as solvent of EB as well as hardener of epoxy resin. This coating passed 2000h of salt fog test when the EB loading was about 1 wt%. The interaction between EB and iron indicated that EB acted as a "quasi-catalyst" to cause the formation of densed iron oxide film in the interface.

Polyaniline as marine antifouling and corrosion-prevention agent

Conductive polyaniline was found to have special marine antifouling property. The coating from conducting polyaniline and epoxy resin(or polyurethane) can last 6-9 months in Southern China sea, i.e., less than 10% of the coating surface was fouled during this period. The conducting polyaniline has special synergetic antifouling effect on other antifouling agents like cuprous oxide or 4, 4'-dichlorodiphenyltrichloroethane. The conductivity of the polyaniline was found to be extremely important for its antifouling effect. Moreover, employing aliphatic polyamine as solvent of emeraldine base and curing agent of epoxy resin, a new technique to process corrosion prevention coating containing emeraldine base was developed, therefrom the emeraldine base and epoxy resin was in molecular level blending. This technique was solvent free and extremely effective, i.e., only 1wt% of emeraldine base in the coating can have good corrosion prevention property.

INHIBITION OF CORROSION BY HEXADECYL TRIMETHYL AMMONIUM BROMIDE LANGMUIR-BLODGETT MONOLAYERS ON CARBON-STEEL

Langmuir-Blodgett (LB) monolayers of hexadecyl trimethyl ammonium bromide (HTAB) were deposited onto a carbon steel surface to investigate the inhibition of corrosion by measurement of the polarization resistance and cyclic voltammetry. The corrosion proc

XPS STUDY OF CORROSION BEHAVIOUR OF TITANIUM IN H2C2O4 SOLUTION

The corrosion behaviour of titanium substance and the XPS characterization of Ti surface in the H2C2O4 solution have been first studied by X-ray photoelectron spectroscopy, The experimental results show that there am mile Ti-2 and Ti2+ on sample surface in 10% H2C2O4 solution for two boars corrosion at 80 degrees C, but if corrosion is extended to 4 hones, the surface composition is mainly TiO2 with a small amount of Ti2+. This result corresponds to the structure of TiH1.642 composion in sample surface found by XRD analysis. Since bath TiO2 and the surface coating RuO2 are of Gald-Redstone structure, therefore electrode materials of Ti-Ru are stable in chemical industry.