Flexural fatigue behavior of injection-molded composites based on poly(phenylene ether ketone)

Flexural fatigue tests were conducted on injection-molded short fiber composites, carbon fiber/poly(phenylene ether ketone) (PEK-C) and glass fiber/PEK-C (with addition of polyphenylene sulfide for improving adhesion between matrix and fibers), using four-point bending at stress ratio of 0.1. The fatigue behavior of these materials was presented. By comparing the S-N curves and analyzing the fracture surfaces of the two materials, the similarity and difference of the failure mechanisms in the two materials were discussed. It is shown that the flexural fatigue failure of the studied materials is governed by their respective tensile properties. The matrix yielding is main failure mechanism at high stress, while at lower stress the fatigue properties appear fiber and interface dominated. (C) 1997 John Wiley & Sons, Inc.

Liquid crystalline polymer as a processing agent in blends of poly(ether-ketone)/LCP70

Blends of a liquid crystalline thermotropic copolyester (LCP70) and an amorphous phenolphthalein based poly(ether-ketone)(PEK-C) with two viscosities were prepared by melt blending. The blends' morphology, rheological and mechanical properties were investigated by DSC, SEM, mechanical and rheological tests. It was observed that the optimum composition of the PEK-C/LCP70 blend was 10 wt% LCP for both mechanical and rheological properties. When the LCP content was less than 10%, the LCP phase existed as finely dispersed fibrous domains with a diameter of about 1 mu m in the matrix, and both tensile and flexural properties were improved. In contrast, when the LCP content reached 20% or more, the LCP domains coalesced to ellipsoidal particles with a diameter of about 5 mu m, and the mechanical properties decreased as a result. It is demonstrated that pure PEK-C with a high viscosity which was difficult to process by melt extrusion, could be extruded conveniently when 10% LCP70 was incorporated. It is emphasized that LCP not only can be used as a reinforcing phase but also an effective processing agent for engineering thermoplastics, especially for those with high viscosity and narrow processing window. (C) 1997 Elsevier Science Ltd.

Residual properties of an injection-molded poly(phenylene ether ketone) carbon composite during flexural fatigue

The present work investigates the effects of cyclic fatigue loading on the residual properties of an injection-molded composite, carbon-fiber-reinforced poly(phenylene ether ketone) (CF/PEK-C), and damage development in this material under fatigue lending. Test specimens, which had been conditioned to various preselected fatigue damage stages, were measured for their residual properties. The results indicated that cyclic fatigue loading alters the constitutive behavior of the injection-molded composite, especially in the non-linear portion of the stress/strain curve. The residual strength decreases with increase in the number of fatigue cycles as a consequence of the accumulation of fatigue damage, which is dominated by the growth of microcracks. While the residual modulus increases slightly with cyclic fatigue loading, this is probably due to the oriented hardening resulting from creep deformation which is induced during cyclic loading. (C) 1997 Elsevier Science Limited.

Reinforced effect of wollastonite on phenolphthalein poly(ether ketone)

The mechanical properties of wollastonite-filled phenolphthalein poly(ether ketone) (PEK-C) composites have been studied at room temperature and 200 degrees C. The dispersion of wollastonite particles in PEK-C matrix were investigated by means of scanning electron microscope. The modulus and strength of the composites increased with filler content. The reinforced effect of wollastonite on PEK-C is more marked at elevated temperature. The glass transition temperature of the composites is higher than that of PEK-C and is independent of filler content. The restriction effect of tiller particles on the molecular mobility of the polymer matrix should be attributed to the reinforcement. (C) 1997 John Wiley & Sons, Inc.

Isolation, spectra, structure, and ring-opening polymerization of strained macrocyclic aryl(ether ketone) dimer

Macrocyclic arylene ether ketone dimer was isolated from a mixture of cyclic oligomers obtained by the nucleophilic substitution reaction of bisphenol A and 4,4'-difluorobenzophenone and easily polymerized to high molecular weight linear poly(ether ketone). The cyclic compound was characterized by FTIR, H-1- and C-13-NMR, and single-crystal x-ray diffraction. Analysis of the spectral and crystal structure reveals extreme distortions of he phenyl rings attached to the isopropylidene center and of the turning points of the molecular polygons. The release of the ring strain on ring-opening combined with entropical difference between the linear polymer chain and the more rigid macrocycle at temperatures of polymerization may be the proposed motivating factors in the polymerization of this precursor to high molecular weight poly(ether ketone). (C) 1997 John Wiley & Sons, Inc.

The multiple melting behaviour of immiscible poly(ether ether ketone) poly(ether diphenyl ether ketone) blend

Poly(ether ether ketone)/poly(ether diphenyl ether ketone) blend containing 30 wt% PEDEK was used to investigate the melting behaviour of immiscible PEEK/PEDEK blends. The results measured from differential scanning calorimetry (d.s.c.) and wide-angle X-ray diffraction (WAXD) showed that immiscible PEEK/PEDEK blends isothermally crystallized at a temperature between Tg and Tm-2 (PEEK's normal melting point) from the glassy state also exhibited the multi-melting behaviour like poly(aryl ether ketones) homopolymers. In addition, the low-temperature melting peak was independent of composition of poly(aryl ether ketones) blends and only associated with the thermal history. (C) 1997 Elsevier Science Ltd.

The synthesis and thermotropic liquid crystalline behavior of the novel poly(aryl ether ketone)s containing chloro-side group

The novel poly(aryl ether ketone)s containing chloro-side group were synthesized by nucleophilic substitution reactions of 4,4'-biphenol and chlorohydroquinone with either 4,4'-difluorobenzophenone(BP/CH/DF) or 1,4-bis(p-fluorobenzoyl)benzene (BP/CH/BF) and their thermotropic liquid crystalline properties were characterized by a variety of experimental techniques. The thermotropic liquid crystalline behavior was observed in the copolymers containing 50 and 70% biphenol. Melting transition (Tm) and isotropization transition (Ti) both appeared in the DSC thermograms. A banded texture was formed after shearing the sample in the liquid crystalline state. The novel poly(aryl ether ketone)s had relatively higher glass transition temperature (Tg) in the range of 168 similar to 200 degrees C and lower melting temperature (Tm) in the range of 290 similar to 340 degrees C. The thermal stability (Td) was in the range of 430 similar to 490 degrees C.

Crystallization behavior of a novel poly(aryl ether ketone): PEDEKmK

Isothermal melt and cold crystallization kinetics of PEDEKmK linked by meta-phenyl and biphenyl were investigated by differential scanning calorimetry in two temperature regions. Avrami analysis is used to describe the primary stages of the melt and cold crystallization, with exponent n = 2 and n = 4, respectively. The activation energies are -118 kJ/mol and 510 kJ/mol for crystallization from the melt and the glassy states, respectively. The equilibrium melting point T-m(0) is estimated to be 309 degrees C by using the Hoffman-Weeks approach, which compares favorably with determination from the Thomson-Gibbs method. The lateral and end surface free energies derived from the Lauritzen-Hoffman spherulitic growth rate equation are sigma = 8.45 erg/cm(2) and sigma(e) = 45.17 erg/cm(2), respectively. The work of chain folding q is determined as 3.06 kcal/mol. These observed crystallization characteristics of PEDEKmK are compared with those of the other members of poly(aryl ether ketone) family. (C) 1997 John Wiley & Sons, Inc.

Novel poly(aryl ether ketone)s containing various pendant groups .2. Gas-transport properties

The gas transport of hydrogen, oxygen, nitrogen, carbon dioxide, and methane gases in a series of poly(aryl ether ketone)s was examined. These polymer membranes have a wide range of permeability coefficients and permselectivity coefficients, showing excellent gas-transport properties. The enhanced interchain interaction in the polymers due to intermolecular hydrogen bonds and ionic bonds results in a considerable increase in permselectivity but a decrease in permeability. On the contrary, the polymers with bulky arkyl substituents show significantly increased permeability. The causes of this trend are interpreted in terms of the free volume, interchain distance, and glass transition temperature together with the respective contribution of gas solubility and diffusivity to the overall permeability. Of interest is the observation that the ionomer IMPEK-K+, which simultaneously contains bulky isopropyl substituents and pendant carboxylate groups, exhibits over twice higher CO2 permeability and 15% higher CO2/CH4 permselectivity than those of bisphenol-A p'olysulfone (PSF). The possibility of using the new synthesized poly(aryl ether ketone)s in gas separation membrane application is also discussed. (C) 1997 John Wiley & Sons, Inc.

The crystal structure and drawing-induced polymorphism in poly(aryl ether ketone)s .2. Poly(ether ether ketone ketone), PEEKK

The crystal structure, morphology and polymorphism induced by uniaxial drawing of poly(ether ether ketone ketone) [PEEKK] have been studied by transmission electron microscopy (TEM), electron diffraction (ED) and wide angle X-ray diffraction (WAXD). On the basis of WAXD and ED patterns,the crystal structure of unoriented PEEKK is determined to have two-chain orthorhombic packing with unit cell parameters of a 0.772 nm, b = 0.600 nm, c = 1.004 nm (form I), A stress-induced crystal modification (form II) is identified and found to possess a two-chain orthorhombic lattice with unit cell dimensions of a = 0.461 nm, b = 1.074 nm, c = 1.080 nm. The 7.5% increase in c-axis dimension for form II is attributed to an overextended chain conformation, arising from extensional deformation during uniaxial drawing and fixed ''in-situ'' through strain-induced crystallization. The average ether-ketone bridge bond angles in form II crystal are determined to be 148.9 degrees by using standard bond lengths. The crystal morphology of PEEKK bears a great similarity to that of PEEK. The crystals grow in the form of spherulites and have the b-axis of unit cell radial. The effects of draw rate on strain-induced crystallization and induction of form II structure are also discussed.

Nonisothermal melt and cold crystallization kinetics of poly(aryl ether ether ketone ketone)

Analysis of the nonisothermal melt and cold crystallization kinetics of poly(aryl ether ether ketone ketone) (PEEKK) was performed by using differential scanning calorimetry (DSC). The Avrami equation modified by Jeziorny could describe only the primary stage of nonisothermal crystallization of PEEKK. And, the Ozawa analysis, when applied to this polymer system, failed to describe its nonisothermal crystallization behavior. A new and convenient approach for the nonisothermal crystallization was proposed by combining the Avrami equation with the Ozawa equation. By evaluating the kinetic parameters in this approach, the crystallization behavior of PEEKK was analyzed. According to the Kissinger method, the activation energies were determined to be 189 and 328 kJ/mol for nonisothermal melt and cold crystallization, respectively.

Crystallization process and morphology structure of poly(aryl ether ether ketone ketone) containing meta-phenyl links

The crystallization process and morphology of poly(aryl ether ether ketone ketone) containing meta-phenyl links (PEEKmK) have been investigated by transmission electron microscopy and electron diffraction. The results indicate that the thin films of PEEKmK isothermally crystallized from both the glassy state and the melt at the temperature range of 180 similar to 250 degrees C consist of two kinds of morphological forms, i. e. large (order of mu m), flat-on single crystals and narrow, lath-like, edge-on lamellae, The latter consists of the spherulites. Meanwhile, the growing process of the two kinds of morphological forms has been discussed.

The crystal structure and drawing induced polymorphism in poly(aryl ether ketone)s .3. Crystallization during hot-drawing of poly(ether ether ketone ketone)

The evolution of crystallinity and polymorphism during hot-drawing of amorphous poly(ether ether ketone ketone) (PEEKK) as a function of strain rate, draw ratio, and temperature was investigated. In modification I, the competition of chain extension and molecular alignment is responsible for the strain rate and temperature dependence. Modification II crystallization is basically controlled by chain extension during stretching. The former can be transformed into the latter via relaxation during stretching or annealing at elevated temperature.

The double-melting behavior of poly(ether diphenyl ether ketone)

Poly(ether diphenyl ether ketone) (PEDEK) synthesized by the nucleophilic route has the following chemical structure: [GRAPHICS] At some given temperatures for a given time isothermally crystallized PEDEK sample exhibits two endothermic peaks which are similar to PEEK and PEEKK The melting behavior of PEDEK crystallized from the glassy state is investigated through differential scanning calorimeter (DSC). We consider that the high-melting peak is related to the perfect crystals and the low-melting peak is associated with a few imperfect crystals. (C) 1997 John Wiley & Sons, Inc.

Crystal structure and crystallinity of poly(aryl ether biphenyl ether ketone ketone)

The crystal structure of poly(aryl ether biphenyl ether ketone ketone) (PEDEKK) was determined to comprise a two-chain orthorhombic unit cell with dimensions a 0.778 nm, b = 0.606 nm and c = 2.375 nm by using wide-angle X-ray diffraction (WAXD). According to the orthorhombic system, the 12 reflections of this polymer were indexed. The crystallite size increases with increasing the crystallization temperature. The results of the degree of crystallinity (W-c,W-x) calculated from WAXD were compatible with those from density (W-c,W-d) and calorimetry (W-c,W-h) measurements.