Lanthanum zirconate nanofibers with high sintering-resistance

The PVP/lanthanum nitrate/zirconium oxychloride (PVP-precursor) nanofiber was prepared by electrospinning technique. Lanthanum zirconate (La2Zr2O7, LZ) in the nanofiber is formed after calcination at 800 degrees C and the nanofiber with pyrochlore structure and a diameter of 100-500 nm can be obtained by calcination of the above precursor fiber at 1000 degrees C for 12 h. The surface of the fiber is rough but the continuous microstructure is still maintained after calcination. LZ fibers stack randomly, resulting in a structure with a low contact area between the fibers. This special structure makes the fiber to have a high resistance to sintering at elevated temperatures. The BET (Brunauer-Emmett-Teller) specific surface areas of the LZ fiber and powder calcined at different temperatures are shown in this paper, and the fiber was characterized by TG-DTA (thermal gravimetry-differential thermal analysis), XRD (X-ray diffraction), N-2 absorption-desorption porosimetry and SEM (scanning electron microscopy).

Sol-gel synthesis and photoluminescent properties of LaPO4 : A (A = Eu3+, Ce3+, Tb3+) nanocrystalline thin films

Rare-earth ion (Eu3+, Tb3+, Ce3+)- doped LaPO4 nanocrystalline thin films and their patterning were fabricated by a Pechini sol-gel process combined with soft lithography on silicon and silica glass substrates. X-Ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric and differential thermal analysis (TG-DTA), atomic force microscopy (AFM), scanning electron microcopy (SEM), optical microscopy, absorption and photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting films. The results of XRD indicate that the films begin to crystallize at 700 degreesC and the crystallinity increases with increasing annealing temperature. The morphology of the thin film depends on the annealing temperature and the number of coating layers. The 1000 degreesC annealed single layer film is transparent to the naked eye, uniform and crack-free with a thickness of about 200 nm and an average grain size of 100 nm. Patterned thin films with different strip widths ( 5 - 50 mm) were obtained by micromolding in capillaries ( soft lithography). The doped rare earth ions show their characteristic emission in the nanocrystalline LaPO4 films, i.e., Eu3+ D-5(0)-F-7(J) (J = 1, 2, 3, 4), Tb3+ D-5(3,4) - F-7(J) ( J = 6, 5, 4, 3, 2) and Ce3+ 5d-4f transition emissions, respectively. Both the lifetimes and the PL intensities of Eu3+ and Tb3+ increase with increasing annealing temperature, and the optimum concentrations for them were determined to be 5 mol% and 16 mol% of La3+ in LaPO4 thin films, respectively. An energy transfer phenomenon from Ce3+ to Tb3+ has been observed in LaPO4 nanocrystalline thin films, and the energy transfer efficiency depends on the doping concentration of Tb3+ if the concentration of Ce3+ is fixed.

Patterning and luminescent properties of nanocrystallineY(2)O(3): Eu3+ phosphor films by sol-gel soft lithography

Nanocrystalline Y2O3:Eu3+ phosphor films and their patterning were fabricated by a Pechini sol-gel process combined with a soft lithography. X-ray diffraction (XRD), thermogravimetric and differential thermal analysis (TG-DTA), atomic force microscopy (AFM), optical microscopy, UV/vis transmission and photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting films. The results of XRD indicated that the films began to crystallize at 500 degreesC and the crystallinity increased with the elevation of annealing temperatures. Uniform and crack free non-patterned phosphor films were obtained, which mainly consisted of grains with an average size of 70 nm. Using micro-molding in capillaries technique, we obtained homogeneous and defects-free patterned gel and crystalline phosphor films with different stripe widths (5, 10, 20 and 50 mum). Significant shrinkage (50%) was observed in the patterned films during the heat treatment process. The doped Eu3+ showed its characteristic emission in crystalline Y2O3 phosphor films due to an efficient energy transfer from Y2O3 host to them. Both the lifetimes and PL intensity of the Eu3+ increased with increasing the annealing temperature from 500 to 900 degreesC, and the optimum concentrations for Eu3+ were determined to be 5 mol%.

溶胶-凝胶法合成Sr_2CeO_4及其发光性能的研究

采用Pechini溶胶 凝胶法合成了Sr2 CeO4 粉末。利用X射线衍射 (XRD)、扫描电镜 (SEM)、热重及差热分析 (TG DTA)以及发光光谱等测试手段对Sr2 CeO4 的结晶过程、发光性质进行了研究。XRD结果表明,用Pe chini溶胶 凝胶法合成的样品800℃时已开始结晶,900℃时可得到三斜晶系的Sr2 CeO4 多晶粉末。扫描电镜照片可以看出颗粒大小不均匀,粒径约为1～5μm。发光光谱测试表明Sr2 CeO4 粉末的激发光谱是一个宽带双峰结构,分别位于310nm和340nm。这个宽带属于Ce4 + 的电荷迁移带。用340nm激发样品,其发射光谱也是一个宽带,最大峰位于475nm ,这个峰属于Ce4 + 的f→t1g跃迁。用310nm激发得到的发射光谱与用340nm激发得到的发射光谱相同。

Synthesis of new solid solutions on neodymium-stabilized La2Mo2O9

A new ionic conductor La2-xNdxMo2O9 (x=0.0-2.0) has been synthesized by wet-chemistry method. The precursors and the resultant oxide powders were characterized by DTA/TG, DSC, XRD and XPS techniques. Effect of substituting Nd for La reveals that the phase transition which occurs in La2Mo2O9 around 565degreesC disappears when x>0.2. And the maximum amount of Nd stabilized the high temperature phase of beta-La2Mo2O9 from cubic to tetragonal is about x=1.6. The measurements of impedance spectroscopy indicate that the ionic conductivity becomes considerably higher in comparison to that of La2Mo2O9.

Citrate-gel synthesis and luminescent properties of ZnGa2O4 doped with Mn2+ and EU3+

By using inorganic salts as raw materials and citric acid as complexing agent, spinel oxide ZnGa2O4 and Mn2+, Eu3+-doped ZnGa2O4 phosphor powders were prepared by a citrate-gel process. X-ray diffraction (XRD), TG-DTA, FT-IR. and luminescence excitation and emission spectra were used to characterize the resulting products. The results of XRD reveal that the powders begin to crystallize at 500 degreesC and pure ZnGa2O4 phase is obtained at 700 degreesC, which agrees well with the results of TG-DTA and FT-IR. In the crystalline ZnGa2O4, the Eu shows its characteristic red (615 nm, D-5(0)-F-7(2)) emission with a quenching concentration of 5 mol% (of Ga3+), and the Mn shows green emission (505 nm, T, A,) with a quenching concentration of 0.1 mol% (of Zn2+). The luminescence mechanism of ZnGa2O4:Mn2+/Eu3+ is presented.

Preparation of Y3Al5O12 : Eu phosphors by citric-gel method and their luminescent properties

By using metal nitrates as starting materials and citric acid as complexing agent, Y3Al5O12 (YAG) and Y3Al5O12:Eu (1 mol%) (YAG:Eu) powder phosphors were prepared by a citrate-gel method. The formation process of YAG and YAG:Eu were investigated by means of XRD, TG-DTA and FT-IR spectra. The purified crystalline phases of YAG and YAG:Eu were obtained at 800 degreesC. The crystalline YAG:Eu phosphors showed an orange-red emission with D-5(0)-F-7(1) (591 nm) as the most prominent group, whose intensity was dependent on the pH value of the starting solution, citric acid content and firing temperature. It has been found that the suitable pH and citric acid/metal ratio are 3 and 2 for obtaining the highest emission intensity, respectively. The emission intensity increases steadily with increasing the annealing temperature from 800 to 1200 degreesC, and nearly remains constant after 1200 degreesC. Furthermore, great differences were observed for the lifetimes and the charge transfer band of Eu3+ in crystalline and amorphous states of YAG.

Fabrication, patterning, and optical properties of nanocrystalline YVO4 : A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films via sol-gel soft lithography

Nanocrystalline YVO4:A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films and their patterning were fabricated by a Pechini sol-gel process combined with soft lithography. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric and differential thermal analysis (TG-DTA), atomic force microscopy (AFM) and optical microscopy, UV/vis transmission and absorption spectra, photoluminescence (PL) spectra, and lifetimes were used to characterize the resulting films. The results of XRD indicated that the films began to crystallize at 400 degreesC and the crystallinity increased with the increase of annealing temperatures. Transparent nonpatterned phosphor films were uniform and crack-free, which mainly consisted of grains with an average size of 90 nm. Patterned gel and crystalline phosphor film bands with different widths (5-60 mum) were obtained. Significant shrinkage and a few defects were observed in the patterned films during the heat treatment process. The doped rare earth ions (A) showed their characteristic emission in crystalline YVO4 phosphor films because of an efficient energy transfer from vanadate groups to them. The Sm3+ and Er3+ ions also showed upconversion luminescence in a YVO4 film host. Both the lifetimes and PL intensity of the rare earth ions increased with increasing annealing temperature from 400 to 800 degreesC, and the optimum concentration for Eu3+ was determined to be 7 mol % and those for Dy3+, Sm3-, and Er3+ were 2 Mol % of Y3- in YVO4 films, respectively.

An organic-inorganic vanadium oxide with one-dimensional ladder-type structure: hydrothermal synthesis, structure and characterization of [V4O10(o-phen)(2)]

A novel organic-inorganic hybrid vanadium oxide [V4O10(o-phen)(2)], involving all vanadium atoms present in +5 oxidation, has been hydrothermally synthesized and characterized by elemental analysis, IR, UV-vis, ESR, XPS spectra and TG-DTA thermal analysis. The single-crystal X-ray diffraction shows that the red-brown crystal is formed in the triclinic system, space group P (1) over bar, a = 9.782(2), b = 6.5124(14), c = 19.765(4) Angstrom, alpha = 89.94(2)degrees, beta = 100.66(2)degrees, gamma = 89.86(2)degrees. The title compound exhibits an infinite one-dimensional ladder-type tetravanadate skeleton with organonitrogen donors of o-phenanthroline ligands coordinated directly to the vanadium oxide framework.

Sol-gel deposition and luminescent properties of oxyapatite Ca-2(Y,Gd)(8)(SiO4)(6)O-2 phosphor films doped with rare earth and lead ions

Rare-earth and lead ions (Eu3+, Tb3+, Dy3+, Pb2+) doped Ca2Y8 (SiO4)(6)O-2 and Ca2Gd8(SiO4)(6)O-2 thin films have been dip- coated on silicon and quartz glass substrates through the sol- gel route. X- Ray diffraction (XRD), TG- DTA, scanning electron microscopy (SEM), atomic force microscopy (AFM), FT- IR and luminescence excitation and emission spectra as well as luminescence decays were used to characterize the resulting films. The results of XRD reveal that these films remain amorphous below 700 degreesC, begin to crystallize at 800 degreesC and crystallize completely around 1000 degreesC with an oxyapatite structure. The grain structure of the film can be seen clearly from SEM and AFM micrographs, where particles with various shapes and average size of 250 nm can be resolved. Eu3+ and Tb3+ show their characteristic red (D-5(0)-F-7(2)) and green (D-5(4) - F-7(5)) emission in the films with a quenching concentration of 10 and 6 mol% (of Y3+), respectively. The lifetime and emission intensity of Eu3+ increase with the temperature treatment from 700 to 1100 degreesC, while those of Tb3+ show a maximum at 800 degreesC. Energy transfer phenomena have been observed by activating the oxyapatite film host- lattice Ca2Gd8(SiO4)(6)O-2 with Tb3+ (Dy3+). In addition, Pb2+ can sensitize the Gd3+ sublattice in Ca2Gd8(SiO4)(6)O-2.

柠檬酸-凝胶法合成ZnGa_2O_4∶Mn~(2+)/Eu~(3+)及其发光性能的研究

采用柠檬酸 凝胶法合成了纯的ZnGa2 O4粉末以及ZnGa2 O4∶Mn2 + /Eu3 + 粉末 ,利用X射线衍射(XRD)、热重及差热分析 (TG DTA)、发光光谱等测试手段对ZnGa2 O4和ZnGa2 O4∶Mn2 + /Eu3 + 的结晶过程、发光性质进行了研究。XRD结果表明 ,柠檬酸 凝胶法合成的样品在 5 0 0℃时已开始结晶 ,在 70 0℃时可得到纯相的ZnGa2 O4多晶粉末 ,这比传统固相法的烧结温度低 5 0 0℃。发光光谱测试表明ZnGa2 O4∶Mn2 + 在4 5 0nm和 5 0 6nm处出现两个发射带 ,前者属于ZnGa2 O4基质的发射 ,后者属于Mn2 + 的4T1→6A1的跃迁发射。ZnGa2 O4∶Eu3 + 则呈现Eu3 + 的特征红光发射 ,最强峰位于 6 13nm ,属于Eu3 + 的5D0 →7F2 超灵敏跃迁。通过光谱分析进一步证实了ZnGa2 O4∶Mn2 + /Eu3 + 的发光机理是基质敏化 ,吸收能量并向激活离子传递能量

溶胶-凝胶法制备纳米Pb(Zr_(0.52)Ti_(0.48))O_3

以醋酸铅 ,硝酸氧锆 ,钛酸四丁酯为原料用溶胶 -凝胶法制备了纳米 Pb( Zr0 .52 Ti0 .48) O3 ( PZT)。结果表明 ,随溶剂中乙二醇单甲醚与水的比例的增大 ,PZT粉体的晶化温度增高 ,晶粒的粒径尺寸也增大 ,当V( C3 H8O2 ) / V( H2 O) =4 .4 7时 ,不仅凝胶完成时间短 ,且可得到粒度分布集中、晶化温度低的 PZT粉体。用原子力显微镜测定 PZT的粒径为 6 0～ 70 nm,用 TG-DTA分析确定在 4 43℃即可发生晶化反应 ,在 5 0 0℃下结晶完善。通过对不同温度下热处理的粉体的红外光谱和 X射线衍射的分析 ,对溶胶 -凝胶法制备 PZT粉体形成钙钛矿结构的过程进行了研究。

Characterization of Y2O3 : Eu coated with polystyrene

The core-shell Y2O3:Eu3+/polystyrene particles was prepared by surface modification with citric acid and emulsion polymerization method of styrene. The DTA curve of coated particles exhibits a small and wide exothermic peak of organic compound around 387 degreesC. The carbonyl stretching vibration band was shifted to low wavenumber in FTIR spectrum and the binding energy of Y3d5/2 was shifted to high-energy band in XPS spectrum. The results of FTIR and XPS show that citric acid was coupled to the particles surface. The hydrophilic surface became amphiphilic by modification of citric acid. So styrene could adsorb on particles surface to form emulsion structure which inorganic core was inside. EDS spectra show that Y2O3:Eu3+ particles were coated uniformly with polystyrene.

A new preparation of zinc sulfide nanoparticles by solid-state method at low temperature

A novel solid-state method of the preparation of zinc sulfide nanoparticles is reported. By solid-state reaction of zinc acetate and thioacetamide at low temperature, zinc sulfide nanoparticles of different sizes were prepared. The temperature of preparation varied from room temperature to 300 degrees C. The particles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), differential thermal analysis (DTA), and photoluminescence spectrum. X-ray diffraction patterns revealed that the particles exhibited pure zinc-blende crystal structure and that particle size increased with increasing temperature. The TEM micrograph showed that the mean particle size was about 40 nm for the sample heated at 100 degrees C. A blue shift was observed in the photoluminescence emission spectrum. A possible mechanism of the reaction corresponding to our observation is proposed, (C) 2000 Elsevier Science Ltd. All rights reserved.

Synthesis, characterization, stability and relaxation behaviours of rare earth heteropolymetalates

Two rare earth heteropolymetalates K9GdW10O36 and K-11[Gd(PW11O39)(2)] have been synthesized and characterized by IR and elemental analysis. Their stability has been studied by TG - DTA. The TG - DTA analysis show that both complexes are of good thermal stability. Their relaxivity in D2O is 6.89 and 5.27 mmol(-1).s(-1) respectively. Interaction with BSA has also been investigated. The results indicate that the two rare earth heteropolymetalate may be potential contrast agent for MRI.