Polymerizing 1,3-butadiene into syndiotactic 1,2-polybutadiene with art iron(III) catalyst system has been investigated. Activity of the catalyst was affected by the type of cocatalyst alkylaluminum and the phosphorus compound as an electron donor, molar ratio of catalyst components, and their aging sequence and aging time of the catalyst. The microstructure and configuration of the polymer was decided by the catalyst components, the higher [Al]/[Fe] molar ratio tending to yield syndiotactic 1,2-polybutadiene, while the higher [P]/[Fe] molar ratio favors the formation of amorphous 1,2-polybutadiene.

Synthesis and characterization of maleated poly(3-hydroxybutyrate)

Graft copolymerization of maleic anhydride (MA) onto poly(3-hydroxybutyrate) (PHB) was carried out by use of benzoyl peroxide as initiator. The effects of various polymerization conditions on graft degree were investigated, including solvents, monomer and initiator concentrations, reaction temperature, and time. The monomer and initiator concentrations played an important role in graft copolymerization, and graft degree could be controlled in the range from 0.2 to 0.85% by changing the reaction conditions. The crystallization behavior and the thermal stability of PHB and maleated PHB were studied by DSC, WAXD, optical microscopy, and TGA. The results showed that, after grafting MA, the crystallization behavior of PHB was obviously changed. The cold crystallization temperature from the glass state increased, the crystallization temperature from the melted state decreased, and the growth rate of spherulite decreased. With the increase in graft degree, the banding texture of spherulites became more distinct and orderly. Moreover, the thermal stability of maleated PHB was obviously improved, compared with that of pure PHB.

Ethylene polymerization by self-immobilized neutral nickel catalysts bearing allyl groups

[Ni(Ph)(PPh3)(N,O)] complexes containing phenyliminophenolato ligands (N,O) (1: N,O = A; 2: N,O = B; 3: N,O = Q 4: N,O = D; 5: N,O = E) have been synthesized and characterized. The molecular structure of 4 was determined by single-crystal X-ray analysis. Complexes 2-5 bearing allyl groups have been investigated as self-immobilized catalysts for ethylene polymerization without the use of co-catalysts. The high ethylene polymerization activities of ca. 10(5) g.PE mol(-1) Ni.h(-1) and high molecular weight (M-w approximate to 10(5)) of polyethylene could be accomplished by changing the ligand structures and reaction conditions. The self-immobilization of catalysts brings about a dramatic increase in the catalytic activities of ethylene polymerization.

Syntheses of biphenyl polyimides via nickel-catalyzed coupling polymerization of bis(chlorophthalimide)s

A facile method for the synthesis of biphenyl polyimides, which involves the nickel-catalyzed coupling of aromatic dichlorides containing imide structure in the presence of zinc and triphenylphosphine, has been developed. The polymerizations proceeded smoothly under mild conditions and produced biphenyl polyimides with inherent viscosities of 0.13-0.98 dL/g. The polymerizations of bis(4-chlorophthalimide)s with bulky side substituents gave high molecular weight polymers. Low molecular weight polymers from bis(4-chlorophthalimide)s containing rigid diamine moieties and bis(3-chlorophthalimide)s were obtained because of the formations of polymer precipitate and cyclic oligoimides, respectively. The effects of various factors, such as amount of catalyst, solvent volume, ligand, reaction temperature, and time, on the polymerization were studied. The random copolymerization of two bis(chlorophthalimide)s in varying proportions produced medium molecular weight material. The TgS of prepared polyimides were observed at 245-311 degreesC, and the thermogravimetry of polymers showed 10% weight loss in nitrogen at 470-530 degreesC.

Reverse atom transfer radical polymerization of (-)-menthyl methacrylate

The reverse atom transfer radical polymerization(RATRP) of (-)-menthyl methacrylate ((-)-MnMA) with AIBN(AIBN/CuCl2/bipyridine(bipy) or (-)sparteine((-)Sp) =1/2/4) initiating system in THF has been studied. The dependence of the specific rotation on molecular weight was investigated.

Polymerization of acrylonitrile with (diisopropylamido) bis (indenyl) lanthanides

The polymerization of acrylonitrile was studied using ( diisopropylamido) his ( indenyl) lanthanides, Ind(2)LnN(i-Pr)(2)(Ln = Y, Yb) as a single-component catalyst. The effects of the amount of catalyst, monomer concentration and polymerization temperature on catalytic activity and molecular weight of polyacrylonitrile (PAN) were studied. The results show that the catalytic activity is raised obviously with rising polymerization temperature. The monomer conversion reaches 64% under polymerization temperature, monomer concentration and catalyst concentration are 50 degreesC, 5.1 mol . L (-1) and 0. 3 % (molar ratio) sequentially. The conversion and molecular weight of the polymer increase appreciably with adding additive, PhONa. When the molar ratio of PhONa to the catalyst is three I the conversion and the molecular weight is 76% and 1.32 x 10(4), respectively. The initiation mechanism for the polymerization of acrylonitrile was proposed.

The nature of the interaction between polyaniline and 2,5-dimercapto-1,3,4-thiadiazole in electrochemical redox processes

The interaction between polyaniline (PAn) and 2,5-dimercapto-1,3,4-thiadiazole (DMcT) was investigated by means of cyclic voltammetry and UV-visible spectroscopy. The results show that the polymerization-depolymerization reaction of DMcT or its dilithium salt Li(2)DMcT is a kinetically quasi-reversible process. PAn exhibits very weak electrochemical activity in neutral propylene carbonate. After doping with protonic acid, such as hydrochloric acid or maleic acid etc., however, it shows an extensively enhanced electroactivity. For the complex system, PAn-DMcT or PAn-Li(2)DMcT, polyaniline has no catalytic activity for the electrochemical polymerization-depolymerization reaction of DMcT or DMcT(2-). Instead, the enhancement of the electrochemical redox activity of PAn-DMcT system compared with that of PAn, DMcT, Li(2)DMcT, and PAn-Li(2)DMcT comes from the protonic doping of PAn by DMcT.

Preparation and characterization of poly(ethyl acrylate)/bentonite nanocomposites by in situ emulsion polymerization

Transparent poly(ethyl acrylate) (PEA)/bentonite nanocomposites containing intercalated-exfoliated combinatory structures of clay were synthesized by in situ emulsion polymerizations in aqueous dispersions containing bentonite. The samples for characterization were prepared through direct-forming films of the resulting emulsions without coagulation and separation. An examination with X-ray diffraction and transmission electron microscopy showed that intercalated and exfoliated structures of clay coexisted in the PEA/bentonite nanocomposites. The measurements of mechanical properties showed that PEA properties were greatly improved, with the tensile strength and modulus increasing from 0.65 and 0.24 to 11.16 and 88.41 MPa, respectively. Dynamic mechanical analysis revealed a very marked improvement of the storage modulus above the glass-transition temperature. In addition, because of the uniform dispersion of silicate layers in the PEA matrix, the barrier properties of the materials were dramatically improved. The permeability coefficient of water vapor decreased from 30.8 x 10(-6) to 8.3 x 10(-6) g cm/cm(2)s cmHg. (C) 2002 Wiley Periodicals, Inc.

Asymmetric polymerization of menthyl methacrylate by anionic catalysts

In this paper, (-)menthyl methacrylate((-)MnMA) was polymerized at -78degreesC in toluene with three types of anionic catalysts, which were complexes of fluorenyllithium with (-)sparteine -((-)-Sp), (S, S)-(+)-2, 3-dimethoxy-1, 4-bis(dimethylamino)butane((+)DDB) and N,N,N,N'-tetramethylethylenediamine(TMEDA), and the chiral optical property of the obtained polymer was studied. The circular dichroism (CD) spectrum of the polymer showed negative Cotton effect.

Silane bridged polymerized metallocene catalyst for ethylene polymerization

The polymerized metallocene catalyst 4 was prepared by the co-polymerization of ansa-zirconocene complex [CH3Si(2)]ZrCl2 (3) containing vinyl substituted silane bridge with styrene in the presence of radical initiator. Catalyst 4 was found to display high ethylene polymerization activity of 2.28 x 10(6) g PE/(mol . h) with a viscosity average molecular weight (M-eta) value of 61.6 x 10(3) using methylalumoxane (MAO) as a co-catalyst. The ethylene polymerization has been investigated under different conditions.

The kinetics of the thermal decomposition of poly(3-hydroxybutyrate) and maleated poly(3-hydroxybutyrate)

The thermal decomposition mechanism of maleated poly(3-hydroxybutyrate) (PHB) was investigated by FTIR and H-1 NMR. The results of experiments showed that the random chain scission of maleated PHB obeyed the six-membered ring ester decomposition process. The thermal decomposition behavior of PHB and maleated PHB with different graft degree were studied by thermogravimetry (TGA) using various heating-up rates. The thermal stability of maleated PHB was evidently better than that of PHB. With increase in graft degree, the thermal decomposition temperature of maleated PHB gradually increased and then declined. Activation energy E. as a kinetic parameter of thermal decomposition was estimated by the Flynn-Wall-Ozawa and Kissinger methods, respectively. It could be seen that approximately equal values of activation energy were obtained by both methods.

Polymerized unsymmetrical iron post-metallocene catalyst for ethylene polymerization

The unsymmetrical allyl containing post-metallocene complex [ArN = C( Me)] [(ArN)-N-' = C(Me)]C5H3NFeCl2 [Ar = 2,6(i- Pr)(2)C6H3, Ar' = 4-allyl-2,6-(i-Pr)(2)C6H3] (3) has been prepared and characterized. Complex (3) can be co-polymerized with styrene in the presence of radical initiator to produce polymerized post-metallocene catalyst which exhibits high activity for ethylene polymerization (2.5 x 10(6) g PE/mol Fe.h).

Synthesis, structure and ring-opening polymerization of phenolphthalein macrocyclic polyarylates

Phenolphthalein based polyarylate macrocyclic oligomers were selectively synthesized by an interfacial polycondensation reaction of o-phthaloyl dichloride with phenolphthalein. The high selectivity benefits from the role of phenolphthalein as a color indicator, an efficient phase transfer catalyst, acid a preferred conformation of the starting materials as indicated by analyzing a single-crystal X-ray structure of an analogous macrocycle. The melt ROP of phenolphthalein polyarylate cyclic dimer was studied using nucleophilic initiators, The molecular weight of the resulting polymers builds up very rapidly at the very early stage of polymerization but decreases with time. During the ROP of cyclic dimer, analogous macrocycles with higher degree of polymerization (n greater than or equal to 3) and linear oligomers were produced by backbiting reaction especially at later stage of polymerization. Conversion of cyclic dimer is very fast at the earlier stage of polymerization and then increases slowly with time as analyzed by gel permeation chromatography. However, the total amount of cyclic oligomers in the ROP system increases with time at the later stage of polymerization because of the formation of larger macrocycles. The resulting polymers are amorphous. Glass transition temperatures (T(g)s) of these polymers are influenced by the polymerization time, type of initiator, and initiator concentration.

Poly(3-dodecylthiophenes) polymerized with different amounts of catalyst

The effect of the amount of the catalyst FeCl3, used during the direct oxidation polymerization, on the structure and properties of the obtained poly(3-dodecylthiophene) (P3DDT) was investigated in this paper. Such measurements as gel permeation chromatography (GPC), nuclear magnetic resonance (NMR) spectroscopy, thermal analysis, X-ray diffraction, infrared spectroscopy (FTIR) and ultraviolet-visible (W-vis) spectroscopy were applied. It is found that a suitable addition of FeCl3 can contribute to generate a P3DDT with greater percentage of head-to-tail head-to-tail (HT-HT) linkages, which are generally favored. The reduction of the other linkage defects helps to lengthen conjugation length, thus leading to more orderly chain packing. (C) 2000 Elsevier Science S.A. All rights reserved.

Study on a novel polyimide precursor prepared by a modified polymerization of monomeric reactants (MPMR) procedure

A novel polyimide precursor based on the dimethyl ester of 3,3',4,4'-biphenyltetracarboxylic acid, 4,4'-methylene dianiline and the monomethyl ester of 5-norbornene-2,3-dicarboxylic acid (BPDE/MDA/NE) was prepared by a modified polymerization of monomeric reactants (PMR) approach (MPMR). The composition of the precursor was quantitatively characterized by means of FTIR, HPLC and GC. The fractions of imide, amic ester and amic acid units in the precursor, typically prepared by refluxing in 1,4-dioxane for 2 h, were 33.7, 30.8 and 1.1 mol-%, respectively. The portion of free MDA was 3.34 wt.-% as determined by HPLC.