Morphology control and luminescence properties of YAG : Eu phosphors prepared by spray pyrolysis

Starting from nitrate aqueous solutions with citric acid and polyethylene glycol (PEG) as additives, Y3Al5O12:Eu (YAG:Eu) phosphors were prepared by a two-step spray pyrolysis (SP) method. The obtained YAG:Eu phosphor particles have spherical shape, submicron size and smooth surface. The effects of process conditions of the spray pyrolysis on the crystallinity, morphology and luminescence properties of phosphor particles were investigated. The emission intensity of the phosphors increased with increasing of sintering temperature and solution concentration due to the increase of the crystallinity and particles size, respectively. Adequate amount of PEG was necessary for obtaining spherical particles, and the optimum emission intensity could be obtained when the concentration of PEG was 0.10 g/ml in the precursor solution. Compared with the YAG:Eu phosphor prepared by citrate-gel (CG) method with non-spherical morphology, spherical YAG:Eu phosphor particles showed a higher emission intensity.

Synthesis and properties of cerium oxide nanometer powders by pyrolysis of amorphous citrate

CeO2 nanometer powders of different sizes were prepared at low temperature by pyrolysis of amorphous citrate. XRD patterns show that CeO2 is cubic in structure, space group O-h(5)-F-M3M. TEM indicates that the prepared CeO2 is spherical in shape, and the particle size distribution is in narrow range. It was found that calcination temperature is a more important factor affecting the crystallite size of CeO2 than calcining time, the smaller the particle, the bigger the crystal lattice distortion, the worse the crystal growth. Solubility test of CeO2 in nitric acid reveals that the surface activity of CeO2 decreases with the increasing particle sizes. IR spectra analysis shows that the absorption of Ce-O bond is shifted to higher energy with the decrease of CeO2 particle sizes.

Effect of irradiation on pyrolysis of polypropylene in the presence of zeolites

For recycling of waste polymers, the degradation behavior of PP was studied with a combination of radiolysis and thermolysis methods. The results revealed that thermal degradation temperature of PP was significantly reduced when PP was irradiated in the presence of a zeolite. The irradiation-induced temperature reduction depended on the zeolite structure and composition, as well as on the morphology of the mixture. Identification of pyrolysis products indicated that, in the absence of zeolite, irradiation resulted only in a change of the product distribution but no formation of new compounds. In the presence of zeolite, however, a series of oxidized products were formed. In addition, the pyrolysis could be performed at a much lower temperature. (C) 1996 Elsevier Science Limited

Effects of zeolites on the pyrolysis of polypropylene

With the intention of understanding chemical recycling of waste polymers, various kinds of zeolites were used as catalysts in the pyrolysis of polypropylene (PP). The effects of zeolites on the degradation temperature and pyrolyzed products of PP were studied. It was found that the degradation temperature of PP strongly depended on the type of zeolite used and the amount added. One type of HY zeolite (320HOA) was shown to be a very effective catalyst. Pyrolysis products, which were identified by using a coupled gas-chromatograph-mass-spectrometer, were also affected by the addition of zeolites. Some zeolites did not change the structure of the products but narrowed the product distribution to a smaller molecule region, while the HY zeolite led to hydrocarbons concentrated at those containing 4-9 carbons. Furthermore, some new compounds with cyclic structures were found in the presence of the HY zeolite. (C) 1996 Elsevier Science Limited

THERMAL-DECOMPOSITION PROCESSES OF SOME ELECTRICALLY CONDUCTING POLYMERS INVESTIGATED BY DIRECT PYROLYSIS MASS-SPECTROMETRY

Thermal decomposition processes of poly(thio-1,4-phenylene) (PPS), polythiophene (PT) and polyaniline (PAn) were investigated by direct pyrolysis EI or CI mass spectrometry (DPMS). They can provide up to heptemer pyrolynates and give some structure properties. The results indicate that the thermal degradation all undergoes in radical decomposition, PPS pyrolyzes into linear and cyclic oligmers, but PT and PAn pyrolyze only into linear oligmers.

Thermal decomposition processes of polyaniline and poly-o-toluidine investigated by direct pyrolysis mass spectrometry

The thermal decomposition of polyaniline(PAn) and poly-o-toluidine(POT) was studied by means of direct pyrolysis mass spectrometry(DM) and MS/MS, The results showed that both benzene-diamine and quinone-diimine units were produced, and the intensities of fragments corresponding to quinone-diimine units increased as the oxidation degrees increased, The mechanism of thermal decomposition of PAn and POT was given for the first time.

Analysis of ingredient and heating value of municipal solid waste

Great differences between municipal solid wastes(MSW)produced at different places and different times in terms of such parameters as physical ingredient and heating value lead to difficulty in effective handling of MSW. In this paper, ingredient, heating value and their temporal varying trends of typical MSW in Beijing were continuously measured and analyzed. With consideration of the process in pyrolysis and incineration, correlation between physical ingredients and heating values was induced, favorable for evaluation of heating value needed in handling of MSW from simple analysis of physical ingredients of it.