Preparation and characterization of metal-chitosan nanocomposites

Various metal-chitosan nanocomposites were synthesized, including silver (Ag), gold (Au), platinum (Pt), and palladium (Pd) in aqueous solutions. Metal nanoparticles were formed by reduction of corresponding metal salts with NaBH4 in the presence of chitosan. And chitosan molecules adsorbing onto the surface of as-prepared metal nanoparticles formed the corresponding metal-chitosan nanocomposites. Transmission electron microscopy (TEM) images and UV-vis spectra of the nanocomposites revealed the presence of metal nanoparticles. Comparison of all the resulting particles size, it shows that silver nanoparticles are much larger than others (Au, Pt and Pd). In addition, the difference in particles size leads to develop different morphologies in the films cast from prepared metal-chitosan nanocomposites. Polarized optical microscopy (POM) images show a batonet-like structure for Ag-chitosan nanocomposites film, while for the films cast from other metal (Au, Pt, and Pd)-chitosan nanocomposites, some branched-like structures with a few differences among them were observed under POM observation.

Preparation and characterization of ultrathin multilayer films based on polyoxometalate Mo8V2O28 center dot 7H(2)O

The ultrathin multilayer films of sphere-shaped polyoxomolybdate Mo8V2O28.7H(2)O (abbreviated to Mo8V2) and poly(allylamine hydrochloride) (DAH) have been prepared by the layer-by-layer (LbL) self-assembly method. The (Mo8V2/DAH)(m) multilayer films have been characterized by X-ray photoelectron spectra (XPS) and atomic force microscopy (AFM). The electrochemistry behavior of the film at room temperature was investigated.

Preparation and properties of microporous membrane from poly(vinylidene fluoride-co-tetrafluoroethylene) (F2.4) for membrane distillation

Flat-sheet microporous membranes from F2.4 for membrane distillation (MD) were prepared by phase inversion process. Dimethylacetamide (DMAC) and LiClO(4)(.)3H(2)O/trimethyl phosphate (TMP) were, respectively, used as solvent and pore-forming additives. The effects of casting solution composition, exposure time prior to coagulation and temperature of precipitation bath on F2.4 membrane structure were investigated. The morphology of resultant porous membrane was observed by scanning electron microcopy. Some natures of F2.4 porous membrane after drying in air, such as mechanical properties and hydrophobicity, were exhibited and compared with poly(vinylidene fluoride) (PVDF) membrane prepared by the same ways. Stress-at-break and strength stress of F2.4 microporous membrane are higher than that of PVDF membrane, and elongation percentage of F2.4 membrane at break is about eight-fold as great as that of PVDF membrane. Contact angle of F2.4 microporous membrane to water (86.6 +/- 0.51degrees) was also larger than that of PVDF mernbrane (80.0 +/- 0.78degrees). MD experiment was carried out using a direct contact membrane distillation (DCMD) configuration as final test to permeate performance of resultant microporous membrane.

One-step preparation and characterization of PDDA-protected gold nanoparticles

Poly(diallyl dimethylammonium) chloride (PDDA), an ordinary and watersoluble, cationic polyelectrolyte, was investigated for its ability to generate and stabilize gold colloids from a chloroauric acid precursor. In this reaction, PDDA acted as both reducing and stabilizing agents for gold nanoparticles (AuNPs). More importantly, PDDA is a quaternary ammonium polyelectrolyte, which shows that the scope of the reducing and stabilizing agents for metal nanoparticles can be extended from the amine-containing molecules to quaternary ammonium polyelectrolytes or salts. UV-vis spectroscopy, transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS) and Fourier transform infrared (FTIR) were used to characterize the synthetic AuNPs. The PDDA-protected AuNPs obtained are very stable and have relative narrow size distribution.

Preparation and properties of sulfonated poly(ether ether ketone)s (SPEEK)/polypyrrole composite membranes for direct methanol fuel cells

Polypyrrole (Ppy) was successfully introduced into methyl substituted sulfonated poly(ether ether ketone) (SPEEK) membranes by polymerization in SPEEK solutions to improve their methanol resistance. Uniform polypyrrole (Ppy) distributed composite membranes were formed by this method by the interaction between SPEEK and Ppy. The properties of the composite membranes were characterized in detail. The composite membranes show very good proton conductive capability (25 degrees C: 0.05-0.06s cm(-1)) and good methanol resistance (25 degrees C: 5.3 x 10(-7) 1.1 x 10(-6) cm(2) s(-1)). The methanol diffusion coefficients of composite membranes are much lower than that of pure SPEEK membranes (1.5 x 10(-6) cm(2) s(-1)). The composite membranes show very good potential usage in direct methanol fuel cells (DMFCs).

Preparation and simulation of an additional catalyst layer for direct methanol fuel cell

An additional anode catalyst layer with PtRu/C was hot pressed between two Nafion (R) 112 membranes and a conventional direct methanol fuel cell (DMFC) cathode/membrane/anode assembly with the above membranes as separator was fabricated. The additional catalyst layer formed an assistant cell with the cathode to prevent methanol crossover. A simple one-dimensional mathematical model was presented to describe the performance of this new type of membrane electrode assembly system. As seen from both experimental result and model analysis, the additional catalyst layer can not only effectively prevent the methanol crossover, but also generate electrical power with the crossover methanol. The percentage of output power of the assistant cell to the total power analyzed by the model is about 40% under usual condition, which is much higher than that from experimental result, indicating the potential of the development in the DMFC designing. It was also discovered that the electrical power generated from the assistant cell with crossover methanol could take higher percentage in total electrical power when the main DMFC current density became lower.

Preparation and characterization of a novel solid solution of aluminum in tungsten carbide by mechanically activated high-temperature reaction

In this work, a novel substitutional solid solution (W0.8Al0.2)C was synthesized by mechanically activated high-temperature reaction. X-ray diffraction was used for phase identification during the whole reaction process. Environment scanning electronic microscopy-field emission gun and energy dispersive x-ray were used to investigate the microstructure and the quantitative material composition of the specimen. (W(0.8)A(10.2))C was found to crystallize in the WC-type, and the cell parameters were a = 2.907(1) angstrom and c = 2.837(1) angstrom. The hardness of (W0.8Al0.2)C was tested to be 19.3 +/- 1 GPa, and the density was 13.19 +/- 0.05 g cm(-3).

Preparation and properties of ternary polyimide/SiO2/polydiphenyisiloxane composite films

A series of novel ternary polyimide/SiO2/polydiphenylsiloxane (PI/SiO2/PDPhS) composite films were prepared through co-hydrolysis and condensation between tetramethoxysilane, diphenyldimethoxysilane (DDS) and aminopropyltriethoxysilane-terminated polyamic acid, using an in situ sol-gel method. The composite films exhibited good optical transparency up to 30 wt% of total content of DDS and SiO2. SEM analysis showed that the PDPhS and SiO2 were well dispersed in the PI matrix without macroscopic separation of the composite films. TGA analysis indicated that the introduction of SiO2 could improve the thermal stability of the composite films. Dynamic mechanical thermal analysis showed that the composite films with low DDS content (5 wt%) had a higher glass transition temperature (T-g) than pure PI matrix. When the content of DDS was above 10 wt%, the T-g of the composite decreased slightly due to the plasticizing effect of flexible PDPhS linkages on the rigid PI chains. The composite films with high SiO2 content exhibited higher values of storage modulus. Tensile measurements also showed that the modulus and tensile strength of the composite films increased with increasing SiO2 content, and the composite films still retained a high elongation at break due the introduction of DDS.

Preparation and characterization of post-derivatives from functional polystyrene (ATRP) with p-nitroaniline-azomethine phenol and their thermal and optical study

The functional polystyrene, (Cl-PS)(2)-CHCOOCH2CH2OH ( designated as XPSt and coded P2) was prepared by ATRP at 130(0)C using CuCl and bipyridine as catalysts, 2,2-dichloro acetate-ethylene glycol (DCAG) as multifunctional initiator and THF as solvent. 4-Nitoroaniline azomethine-4' phenol (P1) as chromophores were covalently linked to the functional end groups of the polymer by using simple displacement reaction. The functional polystyrenes, namely XPSt (P2) and (PS)(2)-CHCOOCH2CH2OH, designated as X-PSt and coded P3 and their post-derivatives, namely, DXPSt (P4) and DX-PSt (P5) respectively were characterized by IR, NMR and UV spectroscopies, gel permeation chromatography (GPC) and thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC), polarising optical microscopy (POM) and XRD studies. DSC showed that incorporation of chromophores in the side chains of polymers towards the polystyrene moiety increases the rigidity of the polymer and subsequently, its glass transition temperature; however the incorporation of side chain towards the alcoholic functional group decreases the glass transition temperature. The post derivatives do not play any significant role to increase the thermal stability ( TGA).

Preparation and characterization of nanocrystalline CeO2 by precipitation method

CeO2 nanocrystalline particulates with different sizes were prepared by precipitation method using ethanol as dispersive and protective reagent. XRD spectra show that the synthesized CeO2 has cubic crystalline structure of space group O-H(5)-F-M3M, when calcination temperature is in the range of 250 similar to 800 degreesC. TEM images reveal that CeO2 particles are spherical in shape. The average size of the particles increases with the increase of calcination temperature. Thermogravimetric analysis indicates that the weight loss of precursor mainly depends on the calcination temperature, and little depends on the calcination time. Measurements of CeO2 relative density show that the relative density of CeO2 nanocrystalline powders increases with increasing CeO2 particle size.

Preparation and characterization of luminescent cubic MCM-48 impregnated with an Eu3+ beta-diketonate complex

We report on the preparation of luminescent silica mesoporous molecular sieves (MCM-48) activated by the europium complex Eu(DBM)(3) . 2H(2)O (where DBM = dibenzoylmethane), using a simple wet impregnation method. Different concentrations of Eu(DBM)(3) . 2H(2)O were introduced into the MCM-48 cubic structure, and the resulting samples were washed with ethanol for different times. UV-Vis absorption measurements and thermogravimetric analysis were used to estimate the amount of Eu complex that has been incorporated within the pores of the MCM-48 host. The various samples were characterized by X-ray powder diffraction (XRD), infrared spectroscopy, diffuse reflectance (DR) and fluorescence measurements. The results reveal that Eu complexes have been successfully introduced into the pores of MCM-48 without disrupting the structure. All the impregnated MCM-48 materials show the typical red luminescence of Eu3+ when excited with a UV lamp. Shifts of the absorption maxima were observed in the DR and fluorescence excitation spectra and will be discussed in relation with guest-host interactions between the organic complex and the silica matrix. The decay profiles of the europium luminescence in the different samples were also measured and discussed.

Preparation and characterization of a layered transparent luminescent thin film of silica-CTAB-Tb(acac)(3) composite with mesostructure

A layered luminescent mesostructured thin film of silica-CTAB-Tb(acac)(3) composite has been synthesized by a dip-coating process through an in situ sol-gel method. The terbium (Tb3+) ion and beta-diketone organic ligand acetylacetone (acac) were introduced into the precursor solution, respectively. The as-synthesized composite film was transparent, colorless and possessed a layered structure. After the composite film was dried at 50 degreesC for a few minutes Tb(acac)(3) complex was synthesized in the mesostructured thin film, which can be indicated by the luminescence of the composite film under the UV lamp. The properties of the samples were characterized by XRD, absorption, Fourier transform infrared spectroscopy, and luminescent spectra.

Preparation and properties of polyethylene/montmorillonite nanocomposites by in situ polymerization

Polyethylene (PE)/montmorillonite (MMT) nanocomposites were prepared by in situ coordination polymerization using a MMT/MgCl2/TiCl4 catalyst activated by AI(Et),. The catalyst was prepared by first diffusing MgCl2 into the swollen MMT layers, followed by loading TiCl4 on the inner/outer layer surfaces of MMT where MgCl2 was already deposited. The intercalation of MMT layers by MgCl2 and TiCl, was demonstrated by the enlarged interlayer spacing determined by WAXD. The nanoscale dispersion of MMT layers in the polyethylene matrix was characterized by WAXD and TEM. As a consequence, the crystallinity of the nanocomposite decreased sharply, whereas the tensile strength was significantly improved compared to that of virgin polyethylene of comparable molecular weight. The confinement of the nanodispersed MMT layers to molecular chain and the strong interaction between the nanoscale MMT layers and the resin matrix were thought to account for the decrease of crystallinity and the remarkable enhancement of strength.