2-[2-(Phenylsulfonyl)ethyl]isoindoline-1,3-dione

In the title compound, C16H13NO4S, the phthalimide ring system makes a dihedral angle of 56.7 (1)degrees with the phenyl ring.

Preparation of polymer/silica nanoscale hybrids through sol-gel method involving emulsion polymers. II. Poly(ethyl acrylate)/SiO2

Poly(ethyl acrylate) (PEA)/SiO2 hybrids with different compositions were prepared under different casting temperatures and pH values. Their morphology as investigated by transmission electron microscopy (TEM) shows that samples with different compositions have different morphologies. When the SiO2 content is lower, PEA is the continuous phase and SiO2 is the dispersed phase. At higher SiO2 content, the change in phase morphology takes place, nd PEA gradually dispersing in the form of latex particles in SiO2 matrix. Change in phase morphology depends mainly on the time the sol-gel transition occurs. At suitable casting temperature and pH value, PEA/SiO2 in 95/5 and 50/50 hybrids with even dispersion was obtained.

Mechanisms of sodium and potassium ions transfer facilitated by dibenzo-15-crown-5 across the water /1,2-dichloroethane interface using micropipettes

The transfer of sodium and potassium ions facilitated by dibenzo-15-crown-5 (DB15C5) has been studied at the micro-water/1,2-dichloroethane (water/DCE) interface supported at the tip of a micropipette. Cyclic volt-ammetric measurements were performed in two limiting conditions: the bulk concentration of Na+ or K+ in the aqueous phase is much higher than that of DB15C5 in the organic phase (DB15C5 diffusion controlled process) and the reverse condition (metal ion diffusion controlled process). The mechanisms of the facilitated Na+ transfer by DB15C5 are both transfer by interfacial complexation (TIC) with 1 : 1 stoichiometry under these two conditions, and the corresponding association constants were determined at log beta(1) = 8.97 +/- 0.05 or log beta(1) = 8.63 +/- 0.03. However, the transfers of K+ facilitated by DB15C5 show different behavior. In the former case it is a TIC process and its stoichiometry is 1 : 2, whereas in the latter case two peaks during the forward scan were observed, the first of which was confirmed as the formation of K (DB15C5)(2) at the interface by a TIC mechanism, while the second one may be another TIC process with 1 : 1 stoichiometry in the more positive potential. The relevant association constants calculated for the complexed ion, K+(DB15C5)(2), in the organic phase in two cases, logbeta(2), are 13.64 +/- 0.03 and 11.34 +/- 0.24, respectively.

Study of facilitated potassium ion transfer across a water vertical bar 1,2-dichloroethane interface using different phase volume ratio systems

A study of potassium ion transfer across a water \ 1,2-dichloroethane (W \ DCE) interface facilitated by dibenzo-18-crown-6 (DB18C6) with various phase volume ratio systems is presented. The key point was that a droplet of aqueous solution containing a redox couple, Fe(CN)(6)(3-)/Fe(CN)(6)(4-), with equal molar ratio, was first attached to a platinum electrode surface, and the resulting droplet electrode was then immersed into the organic solution containing a hydrophobic electrolyte to construct a platinum electrode/aqueous phase/organic phase system. The interfacial potential of the W \ DCE within the series could be externally controlled because the specific compositions in the aqueous droplet make the Pt electrode function like a reference electrode as long as the concentration ratio of Fe(CN)(6)(3-)/Fe(CN)(6)(4-) remains constant. In this way, a conventional three-electrode potentiostat can be used to study the ion transfer process at a liquid \ liquid (L \ L) interface facilitated by an ionophore with variable phase volume ratio (r = V-o/V-w). The effect of r on ion transfer and facilitated ion transfer was studied in detail experimentally. We also demonstrated that as low as 5 x 10(-8) M DB18C6 could be determined using this method due to the effect of the high phase volume ratio.

Preparation and characterization of poly(ethyl acrylate)/bentonite nanocomposites by in situ emulsion polymerization

Transparent poly(ethyl acrylate) (PEA)/bentonite nanocomposites containing intercalated-exfoliated combinatory structures of clay were synthesized by in situ emulsion polymerizations in aqueous dispersions containing bentonite. The samples for characterization were prepared through direct-forming films of the resulting emulsions without coagulation and separation. An examination with X-ray diffraction and transmission electron microscopy showed that intercalated and exfoliated structures of clay coexisted in the PEA/bentonite nanocomposites. The measurements of mechanical properties showed that PEA properties were greatly improved, with the tensile strength and modulus increasing from 0.65 and 0.24 to 11.16 and 88.41 MPa, respectively. Dynamic mechanical analysis revealed a very marked improvement of the storage modulus above the glass-transition temperature. In addition, because of the uniform dispersion of silicate layers in the PEA matrix, the barrier properties of the materials were dramatically improved. The permeability coefficient of water vapor decreased from 30.8 x 10(-6) to 8.3 x 10(-6) g cm/cm(2)s cmHg. (C) 2002 Wiley Periodicals, Inc.

Study on polymer micelles of hydrophobically modified ethyl hydroxyethyl cellulose using single-molecule force spectroscopy

Individual hydrophobically modified ethyl hydroxyethyl cellulose (HM-EHEC) molecules under different conditions were elongated using a new atomic force microscope (AFM) based technique-single-molecule force spectroscopy (SMFS). The critical concentration of HM-EHEC for micelle-like clusters at a solid/liquid interface was around 0.8 wt %, which is lower than that in solution. The different mechanical properties of HM-EHEC below and above the critical concentration were displayed on force-extension curves. Through a comparison with unmodified hydroxyethyl cellulose, substituent-induced effects on nanomechanical features of HM-EHEC were investigated. Because of hydrophobic interactions and cooperative binding with the polymer, surfactants such as sodium dodecyl sulfate (SDS) dramatically influence the elastic properties of HM-EHEC below the critical concentration, and further addition of SDS reduces the interactions between the hydrophobic groups and the surfactant.

A new kind of potassium sensor based on capacitance measurement of mimic membrane

A novel type of potassium sensor based on the capacitance change of valinomycin-incorporated bilayer supported on a gold electrode has been developed and characterized. The lipid membrane was Formed by painted method and monitored simultaneously by capacitance variation. The capacitance of the electrode-supported membrane was found to be modulated by different concentrations of K+. Investigating the capacitance change allows a simple and specific technique for the measurement of potassium ion in solution. Especially, the homemade capacitance meter is, to our knowledge, used to monitor the bilayer membrane formation and detect K+ for the first time. It has been proved that this capacitance measurement is a very useful technique because it is simple and sensitive compared to the other methods.

Crystal structure of mixed sodium-potassium paradodecatungstate 6-hydrate

The crystal structure of K7Na3[H2W12O42]3 . 6H(2)O was determined by X-ray crystallography,and refined to R=0.0864 based on 7024 observed reflections (I>2 sigma(I)). The crystallographic parameters are a=11.755(2), b=13.0493(3), c=16.289(3) Angstrom; alpha=77.13(3)degrees, beta=82.92(3)degrees, gamma=89.65(3)degrees, triclinic, space group, P (1) over bar, V=2416.7(8) Angstrom(3), Z=2, M-r=3330.98, D-cal=4.578Mg/m(3), F(000)=2904; mu (MoK alpha)=29.170mm(-1), T=293K. Two independent polyanions are centered respectively at 1,1,1/2 and 1/2, 1/2, 0, approximately perpendicular to each other with dihedral angle between the equatorial planes of the molecules at 96 degrees. K+ and Na+ respectively occupy the clefts of the two discrete polyanions.

Mechanism-transformation synthesis and characterization of poly(styrene-b-2-ethyl-2-oxazoline) diblock copolymer

By mechanism-transformation (anionic --> cationic) poly(styrene-6-2-ethyl-2-oxazoline) diblock copolymer, PS-b-PEOx, was synthesized in two steps. The first step is the polymerization of styrene block capped with ethylene oxide and its tosylation; the second step is the cationic ring-opening polymerization of 2-ethyl-2-oxazoline. The products were thoroughly characterized by various methods, such as H-1-NMR, IR, DMA, TEM and SAXS. The results show that the copolymer obtained possesses high molecular weight and narrow molecular weight distribution.

Effect and mechanism in compatibilization of poly(styrene-b-2-ethyl-2-oxazoline) diblock copolymer in poly(2,6-dimethyl-1,4-phenylene oxide) poly(ethylene-ran-acrylic acid) blends

The compatibilization effect of poly(styrene-b-2-ethyl-2-oxazoline) diblock copolymer, P(S-b-EOx), on immiscible blends of poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) and poly(ethylene-co-acrylic acid) (EAA) is examined in terms of phase structure and thermal, rheological and mechanical properties, and its compatibilizing mechanism is investigated by Fourier-transform infrared spectroscopy. The block copolymer, synthesized by a mechanism transformation copolymerization, is used in solution blending of PPO/EAA. Scanning electron micrographs show that the blends exhibit a more regular and finer dispersion on addition of a small amount of P(S-b-EOx). Thermal analysis indicates that the grass transition of PPO and the lower endothermic peal; of EAA components become closer on adding P(S-b-EOx), and the added diblock copolymer is mainly located at the interface between the PPO and EAA phases. The interfacial tension estimated by theological measurement is significantly reduced on addition of a small amount of P(S-b-EOx). The tensile strength and elongation at break increase with the addition of the diblock copolymer for PPO-rich blends, whereas the tensile strength increases but the elongation at break decreases for EAA-rich blends. This effect is interpreted in terms of interfacial activity and the reinforcing effect of the diblock copolymer, and it is concluded that the diblock copolymer plays a role as an effective compatibilizer for PPO/EAA blends. The specific interaction between EAA and polar parts of P(S-b-EOx) is mainly hydrogen bonding. (C) 1998 Elsevier Science Ltd. All rights reserved.

Sodium sulfonate-functionalized poly(ether ether ketone)s

A new monomer, sodium 5,5'-carbonylbis(2-fluorobenzenesulfonate) (1), was synthesized by sulfonation of 4,4'-difluorobenzophenone (2) with fuming sulfuric acid. Poly(ether ether ketone)s containing sodium sulfonate groups were synthesized directly via aromatic nucleophilic substitution from the sodium sulfonate-functionalized monomer 1 and Bisphenol A (3) in the presence of potassium carbonate in dimethyl sulfoxide. The polycondensation proceeds without any side reactions. The differential scanning calorimetry measurement indicated that the polymers are amorphous and the glass transition temperatures increase with the content of sodium sulfonate groups in the polymer chain. The degree of substitution with sodium sulfonate groups has strong influence on their thermal stability and solubility.

Synthesis and characterization of diblock copolymer of butadiene and 2-ethyl-2-oxazoline

By mechanism-transformation (anionic --> cationic) polymerization, diblock copolymer of butadiene and 2-ethyl-2-oxazoline (PBd-b-PEOx) was synthesized in two steps. The first step is the polymerization of butadiene block capped with ethylene oxide and its tosylation; the second step is the cationic ring-opening polymerization of 2-ethyl-2-oxazoline. The products were characterized by various methods, such as IR, (HNMR)-H-1, DMA, TEM and SAXS. The results show that the obtained copolymers possess high molecular weight and narrow molecular weighs distribution, and that the content of 1,4-structure was controllable.

Photoluminescence study of Langmuir-Blodgett films of blend poly 3-(2-(5-chlorobenzotriazole)ethyl) thiophene

The multilayer Langmuir-Blodgett (LB) films of pr,ly 3-(2-(5-chlorobenzotriazole)ethyl) thiophene (PCBET) blended with amphibious arachidic acid (AA) were prepared and characterized. The photoluminescence intensity of the blend film was enhanced as the AA increased by a certain amount. The PCBET excimers were not formed in the blend LB films.

The miscibility of homopolymer random copolymer blends .1. Poly(styrene-co-acrylonitrile) poly(ethyl methacrylate) and poly(styrene-co-acrylonitrile) poly(methyl methacrylate) blends

The miscibility of blends of poly(styrene-co-acrylonitrile) (SAN) with poly(methyl methacrylate) (PMMA) or poly(ethyl methacrylate) (PEMA) has been investigated by means of NMR and DSC techniques. It is found that there are intermolecular interactions between the phenyl groups in SAN and carbonyl groups in PMMA or PEMA, and the strength of this intermolecular interaction strongly depends on the properties of ester side groups in PEMA or PMMA, composition of the blends and a certain composition of the copolymer. It is this specific interaction instead of the intramolecular repulsion force within the copolymer that plays a key role for the miscibility of SAN/PMMA and SAN/PEMA blends.

IN-SITU SCANNING-TUNNELING-MICROSCOPY IMAGE OF A HIGHLY ORIENTED PYROLYTIC-GRAPHITE ELECTRODE MODIFIED WITH POTASSIUM BIS(11-MOLYBDOSILICATO) DYSPROSATE(III) IN SODIUM-SULFATE SOLUTION

The variation in molecule adsorption mode on pretreated highly oriented pyrolytic graphite electrodes, modified with the title complex K10H3[Dy(SiMo11O39)(2)] by cyclic voltammetry in the title complex solution, was observed in situ by electrochemical scanning tunnelling microscopy (ECSTM) with molecular resolution in sodium sulphate solution. According to the ECSTM images and the known molecular structure we conclude that the adsorption mode of the title complex modified electrode changed during potential cycling from ''vertical'' to ''inclined'' and then ''horizontal'' or ''flat'' mode, i.e. the title complex adsorbed on the surface of electrode by one ligand of the complex at first, then began to incline and was finally adsorbed by two ligands of the complex. This result indicates that the adsorption mode on the modified electrode surface changed during potential cycling in the sulphate solution and a much more stable molecular layer was formed. The change in adlattice of adsorbates on the modified electrode surface from hexagonal to rectangular was also observed by ECSTM. A plausible model was given to explain this process.