Electrochemical and thermodynamic investigation of diniconazole and triadimefon as corrosion inhibitors for copper in synthetic seawater

This paper presents the investigation of diniconzole and triadimefon as chemical corrosion inhibitors for freshly polished copper in synthetic seawater (3.5% NaCl solution). Determination of weight loss, polarization curves, electrochemical impedance spectroscopy (EIS), and SEM, were performed to analyze the inhibiting performance of these compounds. Polarization curves show that they act as mixed-type inhibitors. EIS indicates that an adsorption film of the inhibitors is formed on copper surface. The highest values of inhibition efficiency are respectively, 99.2% and 97.3% at 100 mg/L concentration. Thermodynamic calculation suggests that chemisorptions between the compounds and copper are accordance with Langmuir adsorption isotherm. (C) 2010 Elsevier Ltd. All rights reserved.

Corrosion fatigue of welded joints of steel for marine platform

Experiments on the corrosion fatigue behaviour of welded joints of the steel for marine platform in air and seawater, and of the joints in seawater with cathodic protection, yielded data for linear regression to obtain fatigue life curves (Delta S-N-f). The laws of corrosion fatigue in welded joints of test steel are discussed with reference to those of A(587) and A(131) steel. In these experiments, the fatigue damage occurring at all welded joints around the weld interface resulted in the cracks and fractures. The fatigue life of the specimens in seawater with cathodic protection is longer than that in seawater Without protection.

Characteristics of sulfide corrosion products on 316L stainless steel surfaces in the presence of sulfate-reducing bacteria

It has been found that microbial communities play a significant role in the corrosion process of steels exposed in aquatic and soil environments. Biomineralization influenced by microorganisms is believed to be responsible for the formation of corrosion products via complicated pathways of electron transfer between microbial cells and the metal. In this study, sulfide corrosion products were investigated for 316L stainless steel exposed to media with sulfate-reducing bacteria media for 7 weeks. The species of inorganic and organic sulfides in the passive film on the stainless steel were observed by epifluorescence microscope, environmental scanning electron microscope combined with energy dispersive spectroscopy and X-ray photoelectron spectroscopy. The transformation from metal oxides to metal sulfides influenced by sulfate-reducing bacteria is emphasized in this paper. (c) 2005 Elsevier B.V. All rights reserved.

Corrosion resistance of hot-dipped zinc and zinc alloy coated sheet steels under offshore atmospheric environment

The application of hot-dipped zinc and zinc-aluminum alloy coatings were introduced. Exposure tests of the steels with these coatings were conducted in the offshore atmosphere in Qingdao and Xiamen for 12 years separately. Effects of the coating thickness, alloy composition and atmospheric environment on the corrosion performance were studied. Results of the onsite exposure tests were compared with the results of a previous indoor salt spray accelerated corrosion tests. The study supports that zinc-aluminum alloy coatings are useful in providing better corrosion resistance and can be further developed for future applications.

Corrosion resistance of steel with hot-dipped galvanized zinc and zinc alloy coatings in seawater

Hot-dipped galvanized zinc and zinc alloy coatings were used as the hot-dipped low alloy zinc coatings (aluminum content less than protective metallic coatings for steel structures in seawater in Chi- or equal to 10 wt%) is equal to or even lower than that of the pure na. Corrosion of the two coatings immersed in sea water in Qingdao zinc sheet, while the performance of the hot-dipped high alloy zinc and Xiamen for 6 years were introduced and analyzed, which pro-coatings is higher than that of the pure zinc sheet. The hot-dipped vides a basis for further development and applications of these coat- high alloy zinc coatings can be further developed for optimal tings in China. Tests proved that the anti-corrosion performance of formance in the future.

Effect of sulfate-reducing bacteria on corrosion behavior of mild steel in sea mud

Microbiologically influenced corrosion (MIC) is very severe corrosion for constructions buried under sea mud environment. Therefore it is of great importance to carry out the investigation of the corrosion behavior of marine steel in sea mud. In this paper, the effect of sulfate-reducing bacteria (SRB) on corrosion behavior of mild steel in sea mud was studied by weight loss, dual-compartment cell, electronic probe microanalysis (EPMA), transmission electron microscopy (TEM).combined with energy dispersive X-ray analysis (EDX) and electrochemical impedance spectroscopy (EIS). The results showed that corrosion rate and galvanic current were influenced by the metabolic activity of SRB. In the environment of sea mud containing SRB, the original corrosion products, ferric (oxyhydr) oxide, transformed to iron sulfide. With the excess of the dissolved H2S, the composition of the protective layer formed of FeS transformed to FeS2 or other non-stoichiometric polysulphide, which changed the state of the former layer and accelerated the corrosion process.

Hydrogen permeation behavior and corrosion monitoring atmospheric of steel in cyclic wet-dry environment

Hydrogen permeation of 16Mn steel under a cyclic wet-dry condition was investigated by Devanathan-Stachurski's electrolytic cell with a membrane covered on the exit side by a nickel layer and the weight loss was measured for each wet-dry cycle. The results show that hydrogen permeation current change with different atmospheric environment: distilled water, seawater, and seawater containing 100 ppm H2S. The results show that seawater can induce an increase in the hydrogen permeation current due to the hydrolyzation reaction. And after the increase, equilibrium is reached due to the equilibrium of hydrolyzation reaction effect and the block of the rust layer. On the other hand, H2S contamination also can induce an increase in the maximum hydrogen permeation current due to the hydrolyzation reaction. And H2S contamination delays the time that hydrogen permeation is detected because of the formation of the FeS(1-x) film. The FeS(1-x) film can block the absorption of hydrogen onto the specimen surface. The surface potential change and the pH change of the metal surface control the hydrogen permeation current. And a clear linear correlation exists between the quantities of hydrogen permeated through the 16Mn steel and the weight loss. Based on the linear correlation, we monitored the corrosion rate by monitoring the hydrogen permeation current by a sensor outside. Good coherences were shown between results in laboratory and outside.

Formation and structure of composite coating of HDA and micro-plasma oxidation on A3 steel

Composite coatings were obtained on A3 steel by hot dipping aluminum(HDA) at 720 ℃ for 6 min and micro-plasma oxidation(MPO) in alkali electrolyte. The surface morphology, element distribution and interface structure of composite coatings were studied by means of XRD, SEM and EDS. The results show that the composite coatings obtained through HDA/MPO on A3 steel consist of four layers. From the surface to the substrate, the layer is loose Al2O3 ceramic, compact Al2O3 ceramic, Al and FeAl intermetallic compound layer in turn. The adhesions among all the layers are strengthened because the ceramic layer formed at the Al surface originally, FeAl intermetallic compound layer and substrate are combined in metallurgical form through mutual diffusion during HDA process.Initial experiment results disclose that the anti-corrosion performance and wear resistance of composite coating are obviously improved through HDA/MPO treatment.

Surface amorphous and crystalline microstructure by alloying zirconium using Nd : YAG pulsed laser

A novel composite coating was synthesized by laser alloying of zirconium nanoparticles on an austenite stainless steel surface using a pulsed Nd:YAG laser. The coating contained duplex microstructures comprising an amorphous phase and an austenitic matrix. A discontinuous zirconium-containing region formed at a depth of 16 mum below the surface. The amorphous phase was present in the zirconium-rich region, with the composition of zirconium ranging from 7.8 to 14.5 at. pet. The formation of the amorphous phase was attributed to the zirconium addition. The hardness, corrosion, and wear-corrosion resistance of the irradiated coating were evidently enhanced compared to those of the stainless steel.

Ultrasonic Tomography and Its Applications in oilfield

UTT (Ultrasonic Tomography Tool) is widely used in the oil industry and can be used to inspect corrosion, casing wall damage, casing breakoff, and casing distortion in the well borehole with the maximum environment temperature being 125 °C, and the pressure being 60 MPa. UTT consists of tool head, upper centralization, electronic section, lower centralization, transmitters, and receivers. Its outer diameter is 4.6 cm and length is 320 cm. The measured casing diameter ranges from 60 mm to 254 mm. The tomography resolution is 512×512. The borehole measurement accuracy is 2 mm. It can supply 3D pipe tomography, including horizontal and vertical profile. This paper introduces its specification, measurement principle, and applications in oilfield.damage, casing breakoff, and casing distortion in the well borehole with the maximum environment temperature being 125 °C, and the pressure being 60 MPa. UTT consists of tool head, upper centralization, electronic section, lower centralization, transmitters, and receivers. Its outer diameter is 4.6 cm and length is 320 cm. The measured casing diameter ranges from 60 mm to 254 mm. The tomography resolution is 512×512. The borehole measurement accuracy is 2 mm. It can supply 3D pipe tomography, including horizontal and vertical profile. This paper introduces its specification, measurement principle, and applications in oilfield.

钢基身管内镀铬层下的激光淬火基体界面腐蚀与铬层剥落

钢基身管镀铬层在高温腐蚀性气体中服役,采用YAG激光器对身管内表面作螺旋线状离散淬火预处理后再电镀铬的复合工艺,形成了基体界面呈激光淬火区/激光未处理区周期性变化的铬层/基体结构.对该身管进行高温腐蚀介质为火药气体的靶场实验.对实验后的基体界面腐蚀形貌与铬层剥落的关系研究表明:次界面裂纹的形成是基体界面高温气体腐蚀的根本原因,基体界面腐蚀的结果是形成基体烧蚀坑,烧蚀坑上的铬层以断裂形式剥落.激光淬火预处理钢基体通过抑制次界面裂纹的形成避免了基体界面高温气体腐蚀损伤,提高了铬层的抗剥落能力.

Novel Fe70Zr10Ni6Al4Si6B4 thick metallic glass coating produced by laser cladding

A novel multicomponent thick metallic glass coating has been synthesised by laser cladding. The maximum coating thickness was I mm. The clad cooling rate restrained the epitaxial growth of dendrites in the metallic glass coating. The metallic glass had high glass forming ability with a wide supercooled liquid region ranging from 59 to 70 K. The metallic glass coating also revealed high hardness and good corrosion resistance.

Damage Evolution In Cement Mortar Due To Erosion Of Sulphate

Ultrasonic technique is used to detect the velocity change of stress wave propagated in the cement mortar immersed in the solution of sodium sulfate for 425 days. Also the density change of specimens at different erosion time is measured. By curve fitting, the effect of solutions' concentration and water/cement ratio on the damage evolution is analyzed. The SEM observation on the growth of delayed ettringite is also performed. It shows that the damage evolution of specimens attacked by sulphate solution is dominantly induced by the nucleation and growth of delayed ettringite, and the average size of microvoids in cement mortar affects the damage evolution significantly. (c) 2008 Elsevier Ltd. All rights reserved.

Electrochemical Impedance Spectroscopy Of Peo Coating On Aluminum Alloy In Nacl Solution

Various Plasma Electrolytic Oxidation (PEO) ceramic coatings were prepared on LY12 aluminum alloy by adjusting the concentration of sodium silicate solution. Optical microscope (OM), XRD and EIS were used to study their morphology, composition and anti corrosion behavior in NaCl solution. Increasing concentration of sodium silicate leads to the increase of the total coating thickness while too high and too low concentration lead to the decrease of inner dense layer. The main composition of PEO coatings prepared in 20, 40 and above 60g/L concentration solution are correspondingly alumina, alumina with mullite, and amorphous phase. The corrosion resistance is determined by the inner dense layer. Increasing the thickness of inner dense layer can improve the anti-corrosion performance. PEO coating's corrosion resistance in acidic, alkaline and neutral NaCl solution is proved and the corrosion mechanism involved is also discussed.

Interface Fracture Property Of Peo Ceramic Coatings On Aluminum Alloy

This paper combines the four-point bending test, SEM and finite element method to study the interface fracture property of PEO coatings on aluminum alloy. The interface failure mode of the coating on the compression side is revealed. The ceramic coating crack firstly along the 45 degrees to the interface, then the micro crack in the coating deduces the interface crack. The plastic deformation observed by SEM shows excellent adhesion property between the coating and substrate. The plastic deformation in the substrate is due to the interfacial crack extension, so the interface crack mode of PEO coatings is ductile crack. The results of FEM show that the compression strength is about 600 MPa. (C) 2008 Elsevier B.V. All rights reserved.