Optical and Electrical Properties of GaN.Mg Grown by MOCVD

Mg-doped GaN layers prepared by metalorganic chemical vapor deposition were annealed at temperatures between 550 and 950℃. Room temperature （RT） Hall and photoluminescence （PL） spectroscopy measurements were performed on the as-grown and annealed samples. After annealing at 850℃, a high hole concentration of 8 × 10~(17) cm~(-3) and a resistivity of 0. 8lΩ·cm are obtained. Two dominant defect-related PL emission bands in GaN.. Mg are investigated; the blue band is centered at 2. 8eV （BL） and the ultraviolet emission band is around 3.27eV （UVL）. The relative intensity of BL to UVL increases after annealing at 550℃, but decreases when theannealing temperature is raised from 650 to 850℃, and finally increases sharply when the annealing temperature is raised to 950C. The hole concentration increases with increased Mg doping, and decreases for higher Mg doping concentrations. These results indicate that the difficulties in achieving high hole concentration of 10~(18)cm~(-3) appear to be related not only to hydrogen passivation, but also to self-compensation.

Influences of initial nitridation process on the optical and structural characterization of GaN layer grown on sapphire (0001) by metalorganic chemical vapor deposition

In this paper. we investigate the influences of the initial nitridation of sapphire substrates on the optical and structural characterizations in GaN films. Two GaN samples with and without 3 min nitridation process were investigated by photoluminescence (PL) spectroscopy in the temperature range of 12-300 K and double-crystal X-ray diffraction (XRD). In the 12 K PL spectra of the GaN sample without nitridation, four dominant peaks at 3.476, 3.409 3.362 and 3.308 eV were observed, which were assigned to donor bound exciton, excitons bound to stacking faults and extended structural defects. In the sample with nitridation, three peaks at 3.453, 3.365. and 3.308 eV were observed at 12 K, no peak related to stacking faults. XRD results at different reflections showed that there are more stacking faults in the samples without nitridation.

DFT/TDDFT Studies on the Electronic Structures and Spectral Properties of Rhenium(I) Pyridinybenzoimidazole Complexes

The electronic structures and spectral properties of three Re(I) complexes [Re(CO)(3)XL] (X = Br, Cl; L = 1-(4-5 '-phenyl-1.3,4-oxadiazolylbenzyl)-2-pyridinylbenzoimidazole (1), 1-(4-carbazolylbutyl)-2-pyridinylbenzoimidazole (2), and 2-(1-ethyl benzimidazol-2-yl)pyridi ne (3)) were investigated theoretically. The ground and the lowest lying triplet excited states were full optimized at the B3LYP/LANL2DZ and CIS/LANL2DZ levels, respectively. TDDFT/PCM calculations have been employed to predict the absorption and emission spectra starting from the ground and excited state geometries, respectively.

Ab initio study on the electronic, magnetic, and mechanical properties of CaCu3V4O12

The electronic, magnetic, and mechanical properties of CaCu3V4O12 are investigated by use of the density functional theory method. The calculated results indicate that CaCu3V4O12 is a half-metallic and ferrimagnetic compound. The magnetic coupling for Cu-V is antiferromagnetic, while those for Cu-Cu and V-V are ferromagnetic. The obtained elastic constants suggest that the compound is mechanically stable. The calculated oxidation states and density of states reveal the existence of a mixed valence for Cu and V. This supports the experimental observation of the mixed valence in Ca2+Cu2+Cu2+(V25+V24+)O-12.

Electronic structures and chemical bonding in diatomic ScX to ZnX (X = S, Se, Te)

Bond distances, vibrational frequencies, electron affinities, ionization potentials, dissociation energies, and dipole moments of the title molecules in neutral, positively, and negatively charged ions were studied using density functional method. Ground electronic state was assigned for each molecule. The bonding patterns were analyzed and compared with both the available data and across the series. It was found that, besides ionic component, covalent bonds are formed between the metal s, d orbitals, and the p orbital of S, Se, and Te. For neutral and cationic molecules, the covalent character increases from ScX to CrX and from FeX to CuX with an exception of decrease at MnX and ZnX, while for anionic molecules, the trend is not obvious. For both neutral and charged molecules, the sulfides have the shortest bond distance and largest vibrational frequency, while tellurides have the largest bond distance and smallest vibrational frequency. For neutral and anionic molecules, the dissociation energy of sulfides is the largest, that of tellurides is the smallest, while this only remains true for cationic molecules from ScX+ to FeX+.

Electronic structures and chemical bonding in 4d transition metal monohalides

Bond distances, vibrational frequencies, dipole moments, dissociation energies, electron affinities, and ionization potentials of NIX (XM = Y-Cd, X = F, Cl, Br, I) molecules in neutral, positively, and negatively charged ions were studied by density functional method, B3LYP. The bonding patterns were analyzed and compared with both the available data and across the series. It was found that besides ionic component, covalent bonds are formed between the 4d transition metal s, d orbitals, and the p orbital of halogen. For both neutral and charged molecules, the fluorides have the shortest bond distance, iodides the longest. Although the opposite situation is observed for vibrational frequency, that is, fluorides have the largest value, iodides the smallest. For neutral and anionic species, the dissociation energy tends to decrease with the increasing atomic number from Y to Cd, suggesting the decreasing or weakening of the bond strength. For cationic species, the trend is observed from Y to Ag.

Novel soluble N-phenyl-carbazole-containing PPVs for light-emitting devices: Synthesis, electrochemical, optical, and electroluminescent properties

Novel PPV derivatives (PCA8-PV and PCA8-MEHPV) containing N-phenyl-carbazole units on the back-bone were successfully synthesized by the Wittig polycondensation of 3,6-bisformyl-N-(4-octyloxy-phenyl)carbazole with the corresponding tributyl phosphonium salts in good yields. The newly formed and dominant trans vinylene double bonds were confirmed by FT-IR and NMR spectroscopy. The polymers (with (M) over bar (w) of 6289 for PCA8-PV and 7387 for PCA8-MEHPV) were soluble in common organic solvents and displayed high thermal stability (T(g)s are 110.7 degreesC for PCA8-PV and 92.2 degreesC for PCA8-MEHPV, respectively) because of the incorporation of the N-phenyl-carbazole units. Cyclic voltammetry investigations (onsets: 0.8 V for PCA8-PV and 0.7 V for PCA8-MEHPV) suggested that the polymers possess enhanced hole injection/transport properties, which can be also attributed to the N-phenyl-carbazole units on the backbone. Both the single-layer and the double-layer light-emitting diodes (LEDs) that used the polymers as the active layer emitted a greenish-blue or bluish-green light (the maximum emissions located 494 nm for PCA8-PV and 507 nm for PCA8-MEHPV, respectively).

Substitution effect of nitrogen atoms with carbon atoms in porphyrin on the electronic structure and excited states properties

Density functional theory (DFT) electronic structure calculations were carried out to predict the structures and the absorption and emission spectra for porphyrin and a series of carbaporphyrins-carbaporphyrin, adj-dicarbaporphyrin, opp-dicarbaporphyrin, tricarbaporphyrin and tetracarbaporphyrin. The ground- and excited-state geometries were optimized at the B3LYP/6-31g(d) and CIS/6-31g(d) level, respectively. The optimized ground-state geometry and absorption spectra of porphyrin, calculated by DFT and time-dependent DFT (TDDFT), are comparable with the available experimental values. Based on the optimized excited-state geometries obtained by CIS/6-31g(d) method, the emission properties are calculated using TDDFT method at the B3LYP/6-31g(d) level. The effects of the substitution of nitrogen atoms with carbon atoms at the center positions of porphyrin are discussed. The results indicate that the two-pyrrole nitrogens are important to the chemical and physical properties for porphyrin.

Atom space distance and computing of molecular similarity

A mathematical model on computation of molecular similarity was suggested, The algorithmic techniques for measuring the degree of similarity between pairs of three-dimensional chemical molecules was represented by modified interatomic distance matrices. Current work was carried out on Indigo 2 work station with Sybyl software. Four groups of molecules were used to compute the molecules similarity to testing the mathematical model with satisfactory results.

The role of Li-O bonds in calculations of nonlinear optical coefficients of LiXO3-type complex crystals

The second-order nonlinear optical (NLO) tenser coefficients of LiXO3 (X = I; Nb or Ta) type complex crystals have been calculated using the chemical bond theory of complex crystals. Contributions of each type of bond to the total second-order NLO coefficient d(ij) and the linear susceptibility X are quantitatively determined. All tensor values thus calculated are in good agreement with experimental data. The Li-O bonds are found to be an important group in the contributions to the total NLO tenser coefficient, especially for those in LiNbO3 and LiTaO3. The importance of Li-O bonds depends on the environment of Li atom in these crystals.

OPTICAL AND STRUCTURAL INVESTIGATION OF KMGLA(PO4)(2) PHOSPHATE DOPED WITH EUROPIUM

A new compound KMgLa(PO4)(2), isotypic with monoclinic LaPO4, is reported. Its cell parameters have been determined from X-ray powder diffraction data. Crystallization occurs in the monoclinic space group P2(1)/n (No. 14) with a = 6.839(3) Angstrom, b = 7.066(1) Angstrom, c = 6.523(3) Angstrom, beta = 103.42(4)degrees, and Z = 2. It was found that the KMgLa(PO4)(2) phase was isostructural with monoclinic LaPO4. The difference between them was that half of the La atoms in LaPO4 were couplingly substituted with the same amount of Mg and K atoms. This isomorphous substitution was confirmed by IR and Eu3+-doped excitation and emission spectra and by elemental analysis of single crystals. The spectroscopic data were compared with those of LaPO4:Eu3+. (C) 1995 Academic Press, Inc.

THE OPTICAL AND ELECTRICAL-PROPERTIES OF DYSPROSIUM AND YTTERBIUM MONOPHOSPHIDES

Dysprosium and ytterbium monophosphides have been prepared by the solid state reaction. The optical and electrical properties have been studied. Evidence that DyP and YbP are semiconductors has been obtained from the study of the absorption spectrum, the negative temperature coefficient of resistance and the rectifying effect. Their energy gaps are determined as 1.15 eV for DyP and 1.30 eV for YbP, electric conduction type is n-type, resistivities are about 10(-2) ohm cm and Hall mobility is 8.5-80 cm2/Vs. The p-n junction is formed on the LnP/Si.

BIOMIMITICS OF OXIDASE AND OXYGENASE THE ELECTRONIC SPECTRA AND THE OXYGEN UPTAKE KINTICS FOR MPc AND MTPP (M = Fe, Co, Cu, Pc AND TFP - ARE DIANIONS OF PHTHALOCYANIN AND TETRAPHENYLPORPHYRINE, RESPECTIVELY)

The reaction rates of MTPP with oxygen in air are Inas than that with pure oxygen, the ratio is roughly the same as to the partial presence of imygen in air, The influences of S-ligand etbanethiol and O- litand Vc on the above Systems have also been investigated, the former makes the MP hands having more changes and the reaction rate constants becoming greater, the latter has less influence.

ELECTRONIC-STRUCTURE AND CHEMICAL BONDING OF EUROPIUM NITRATE COMPLEX WITH AZACROWN (2, 2)

The electronic structure and bond character of europium nitrate complex with azacrown (2, 2)(1, 7, 10, 16-tetraoxa-4, 13-diazacyclooctadecane), [Eu(NO_3)_2(2, 2)] NO_3, have been studied by means of XPS and INDO method. The data of electronic binding energies and charge distribution of atoms in the complex showed that chemical shift of less electronegative nitrogen N1s binding energy was larger than that of more electronegative oxygen O1s binding energy in coordinating atoms, and that charge transfer from N...