Influence of Cr interlayer on the structure and optical properties of Ag films on glass substrate by magnetron sputtering

Optical properties and microstructure of Ag film on glass substrate with Cr intermediate layer were studied by using spectrophotometer and XRD. The spectra results showed that introducing Cr intermediate layer reduced the surface roughness and promoted the reflectivity of Ag film. The XRD analysis showed that the crystalline grains increased and the stress decreased. The adhesion was also improved by using the tape test method. (c) 2006 Published by Elsevier B.V.

Theoretical analysis of optical properties of dielectric coatings dependence on substrate subsurface defects

A model for refractive index of stratified dielectric substrate was put forward according to theories of inhomogeneous coatings. The substrate was divided into surface layer, subsurface layer and bulk layer along the normal direction of its surface. Both the surface layer (separated into N-1 sublayers of uniform thickness) and subsurface layer (separated into N-2 sublayers of uniform thickness), whose refractive indices have different statistical distributions, are equivalent to inhomogeneous coatings, respectively. And theoretical deduction was carried Out by employing characteristic matrix method of optical coatings. An example of mathematical calculation for optical properties of dielectric coatings had been presented. The computing results indicate that substrate subsurface defects can bring about additional bulk scattering and change propagation characteristic in thin film and Substrate. Therefore, reflectance, reflective phase shift and phase difference of an assembly of coatings and substrate deviate from ideal conditions. The model will provide some beneficial theory directions for improving optical properties of dielectric coatings via substrate surface modification. (c) 2005 Elsevier B.V. All rights reserved.

Theoretical analysis of influence of substrate microdefects on polarized light properties of dielectric coatings

A model for refractive index of stratified dielectric substrate was presented according to inhomogeneous coatings theories. The substrate was divided into surface layer, subsurface layer and bulk layer along the normal direction of its surface. The former two layers were equivalent to inhomogeneous coatings. Theoretical deduction was executed by employing the characteristic matrix method of optical coatings, and one mathematical calculation example was presented. The results indicate that reflectance, reflective phase shift and phase difference of polarized light deviate from ideal conditions. It shows that substrate microdefects can induce volume scattering and change propagation characteristic of light both in coatings and substrate. (c) 2005 Elsevier GmbH. All rights reserved.

Influence of substrate temperature on properties of MgF2 coatings

Thermal boat evaporation was employed to prepare MgF2 single-layer coatings upon both JGS1 and UBK7 substrates at different substrate temperatures. Microstructure, transmittance and residual stress of these coatings were measured by X-ray diffraction, spectrophotometer, and optical interferometer, respectively. Measurement of laser induced damage threshold (LIDT) of the samples was performed at 355 nm, 8 ns pulses. The results showed that high substrate temperature was beneficial to crystallization of the film. Above 244 degrees C, the refractive index increased gradually with the substrate temperature rising. Whereas, it was exceptional at 210 degrees C that the refractive index was higher than those deposited at 244 and 277 degrees C. The tensile residual stresses were exhibited in all MgF2 films, but not well correlated with the substrate temperature. In addition, the stresses were comparatively smaller upon JGS1 substrates. A tendency could be seen that the LIDTs reached the highest values at about 244 degrees C, and the films upon JGS1 had higher LIDTs than those upon UBK7 substrates at the same temperature. Meanwhile, the damage morphologies showed that the laser damage of the coating resulted from an absorbing center at the film-substrate interface. The features of the damages were displayed by an absorbing center dominated model. Furthermore, the reason of the difference in LIDT values was discussed in detail. (C) 2007 Elsevier B.V. All rights reserved.