WELL-WIDTH DEPENDENCE OF THE EXCITON LIFETIME IN GAAS/ALGAAS QUANTUM-WELLS

The dependence of the excitonic lifetime on the well width has been studied in conventional GaAs/AlGaAs quantum wells. Two clearly different variations of the measured excitonic lifetime have been observed. For wide well widths, we find a nearly linear decrease of the lifetime with decreasing well width. However, when the well is further decreased, a saturation and even increase of the lifetime with decreasing well width are observed. The experimental data are compared with the theory of radiative excitonic recombination, and show that well width dependence of the measured photoluminescence lifetime can be attributed mainly to the change of the excitonic effective volume and the overlap integral as well.

CONTROLLED FORMATION AND CHARACTERISTICS OF INTERFACES IN GAAS/ALGAAS SINGLE QUANTUM-WELLS

The influence of heterostructure quality on transport and optical properties of GaAs/AlGaAs single quantum wells with different qualities was studied. In a conventional sample-A, the transport scattering time and the quantum scattering time are small and close to each other. The interface roughness scattering is a dominant scattering mechanism. From comparison between theory and experiment, interface roughness with fluctuation height 2.5 Angstrom and the lateral size of 50-70 Angstrom were estimated. For samples introducing superlattices instead of AlGaAs layers or by utilizing growth interruption, both the transport and PL measurements showed that interfaces were rather smooth in the samples. The two scattering times are much longer. The interface roughness scattering is relegated to an unimportant position. Results demonstrated that it is important to control the formation of heterostructures in order to improve the interface quality.

OPTICAL CHARACTERISTICS OF GAAS/ALGAAS RIDGE-QUANTUM-WELL-WIRES GROWN BY MBE ON NONPLANAR SUBSTRATES

With conventional photolithography and wet chemical etching, we have realized GaAs/AlGaAs buried ridge-quantum-well-wires (RQWWs) with vertically stacked wires in lateral arrays promising for device application, which were grown in situ by a single-step molecular beam epitaxy growth and formed at the ridge tops of mesas on nonplanar substrates. Confocal photoluminescence (CPL) and polarization-dependent photoreflectance (PR) are applied to study optical characteristics of RQWWs. Lateral bandgap modulation due to lateral variation of QW layer thickness is demonstrated not only by CPL but also by PR. As one evidence for RQWWs, a large blue shift is observed at the energy level positions for electronic transitions corresponding to quantum wells (QWs) at the ridge tops of mesas compared with those corresponding to QWs on nonpatterned areas of the same sample. The blue shift is in contradiction with the fact that the GaAs QW layers at the tops of the mesas are thicker than those on nonpatterned areas. The other evidence for RQWWs, optical anisotropy is provided by the polarization-dependent PR, which results from lateral quantum size effect existing at the tops of the mesas.

DETERMINATION OF THE CONDUCTION-BAND OFFSET OF A SINGLE ALGAAS BARRIER LAYER USING DEEP-LEVEL TRANSIENT SPECTROSCOPY

The tunneling from an AlGaAs confined thin layer to a GaAs layer in the GaAs/Al0.33Ga0.67As/GaAs structure during the trapped electron emission from deep level in the AlGaAs to its conduction band has been observed by deep level transient spectroscopy. With the aid of the tunneling effect, the conduction-band offset DELTAE(c) was determined to be 0.260 eV, corresponding to 63% of DELTAE(g). A calculation was also carried out based on this tunneling model by using the experimental value of DELTAE(c) = E2 - E1 = 0. 260 eV, and good agreement between the experimental and calculated curves is obtained.

CBE GROWTH OF GAAS/GAAS, GAAS/SI AND ALGAAS/GAAS USING TEG, ASH3 AND AMINE-ALANE PRECURSORS

The growth of high quality AlGaAs by CBE bas been limited by the high levels of carbon and oxygen contamination. The use of alane based precursors offers a significant reduction in such contamination. We report for the first time the CBE growth of AlxGa1-xAs from triethylgallium, dimethylethylamine-alane and arsine, and compare with. growth from triethylgallium, trimethylamine-alane and arsine. Some preliminary results of work on the CBE growth of GaAs on silicon will also be reported.