Preparation and Luminescence Properties of Gd2MoO6:Eu3+ Nanofibers and Nanobelts by Electrospinning

Gd2MoO6:Eu3+ nanofibers and nanobelts have been prepared by a combination method of the sol-gel process and electrospinning. X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), high resolution transmission electron microscopy, photoluminescence, and low voltage cathodoluminescence as well as kinetic decays were used to characterize the resulting samples. The results of XRD and FTIR indicate that the Gd2MoO6:Eu3+ samples have crystallized at 600 degrees C with the monoclinic (alpha) structure. The SEM and TEM results indicate that the as-formed precursor fibers and belts are uniform and that the as-prepared nanofibers and nanobelts consist of nanoparticles. Gd2MoO6:Eu3+ phosphors show their strong characteristic emission under UV excitation (353 nm) and low voltage electron-beam excitation (3 kV), making the materials have potential applications in fluorescent lamps and field-emission displays.

Nanocrystalline LaAlO3:Sm3+ as a Promising Yellow Phosphor for Field Emission Displays

Nanocyrstalline LaAlO3:Sm3+ phosphors were prepared through a Pechini-type sol-gel process. X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), photoluminescence, and cathodoluminescence (CL) spectra were utilized to characterize the synthesized phosphors. XRD results reveal that the sample begins to crystallize at 600 degrees C, and pure LaAlO3 phase can be obtained at 700 degrees C. FE-SEM images indicate that the Sm3+-doped LaAlO3 phosphors are composed of aggregated spherical particles with sizes ranging from 40 to 80 nm. Under the excitation of UV light (245 nm) and low-voltage electron beams (1-3 kV), the Sm3+-doped LaAlO3 phosphors show the characteristic emissions of the Sm3+ ((4)G(5/2)-H-6(5/2), H-6(7/2), H-6(9/2) transitions) with a yellow color. The CL intensity (brightness) of the Sm3+-doped LaAlO3 phosphor is higher than that of the commercial product [Zn(Cd)S:Ag+] (yellow) to some extent.

Direct patterning of negative nanostructures on self-assembled monolayers of 16-mercaptohexadecanoic acid on Au(111) substrate via dip-pen nanolithography

Both bare and self-assembled monolayer (SAM) protected gold substrate could be etched by allyl bromide according to atomic force microscopy (AFM), x-ray photoelectron spectroscopy (XPS) and inductively coupled plasma mass spectrometric (ICPMS) analysis results. With this allyl bromide ink material, negative nanopatterns could be fabricated directly by dip-pen nanolithography (DPN) on SAMs of 16-mercaptohexadecanoic acid (MHA) on Au(111) substrate. A tip-promoted etching mechanism was proposed where the gold-reactive ink could penetrate the MHA resist film through tip-induced defects resulting in local corrosive removal of the gold substrate. The fabrication mechanism was also confirmed by electrochemical characterization, energy dispersive spectroscopy (EDS) analysis and fabrication of positive nanopatterns via a used DPN tip.

水溶性聚合物和两亲聚合物23.两亲聚合物PAMC_(16)S对螺口恶嗪化学和物理行为的影响

研究了两亲聚合物聚 (2 -丙烯酰胺基十六烷磺酸 ) (PAMC16S)存在下 1 -乙基 -3 ,3 -二甲基螺 [吲哚啉 -萘并口恶嗪 ](SO -E)在水溶液中的增溶作用及PAMC16S对SO -E化学和光化学性质的影响。PAMC16S明显增加了SO -E在水相的溶解性 ,SO -E的最大增溶浓度随PAMC16S浓度增加呈线性增加规律。在PAMC16S存在下 ,新配制的SO -E溶液显示可逆的光致变色性 ,显色体呈红色 ,最大吸收峰位于 5 2 0nm ,在室温下的消色反应速度明显慢于无PAMC16S存在下的兰色显色体。SO -E/PAMC16S溶液是不稳定的 ,配制后较长时间即失去SO -E的正常光致变色性质。盐酸具有与PAMC16S相似的作用 ,SO -E/PAMC16S体系的不稳定性可用氨水中和的方法解决。1H -NMR结果表明SO -E在酸性介质中发生了不可逆的化学反应。

Infrared spectra and VUV excitation properties of BaLnB(9)O(16): Re (Ln = La, Gd; Re = Eu, Tb)

The infrared spectra of BaLnB(9)O(16):Re, along with the VUV excitation spectra, have been measured. The spectra were tentatively interpreted in terms of the data on absorptions of the borate groups and band structure. It was observed that there are absorption due to BO3 and BO4 groups, indicating that there are BO3 and BO4 groups in BaLnB(9)O(16). It is found that absorption of the borate groups is located in the range from 120 to 170 mn. This result reveals that there is an energy transfer from host to the rare earth ions. It also observed that the energy of charge transfer band, the host absorption, the total crystal field splitting of d-levels of Tb3+ increase with the decrease in the Ln(3+) radius. (C) 2001 Elsevier Science B.V. All rights reserved.

Preparation of stable mesoporous silica FSM-16 from water glass in the presence of cetylpyridium bromide

The synthesis and characterization of the mesoporous materials FSM-16 (folded sheets mesoporous materials) with highly ordered structure in open-vessel by using cetylpyridium bromide (CPBr) and the single-layered polysilica Kanemite as new template and silicon source, respectively, has been investigated systematically. The hexagonal arrangements of uniformly size pores were characterized by FTIR. XRD. nitrogen adsorption. TG-DTA. SEM and TEM. Especially, the porous products with higher surface areas show remarkable thermal stability up to 1000 C. The potential application as carrier of catalysts or host-guest materials is anticipated. (C) 2001 Elsevier Science B.V. All rights reserved.

碳酸乙烯酯(EC)增塑的(PEO)_(16)LiClO_4聚电解质电导率的研究

采用差示扫描量热法 (DSC)和交流阻抗方法对EC增塑的 (PEO) 16 LiClO4 聚电解质进行了研究。结果表明 (PEO) 16 LiClO4 /EC体系的玻璃化转变温度 (tg)及PEO的结晶度 (Xc)降低 ,电导率 (б)增加 ,且б与温度 (T)的关系符合Arrhenius行为。提出了离子导电聚电解质 /不锈钢 (SS)这种结构的界面双层结构和交流阻抗谱图的模拟等效电路

BaLaB_9O_(16)∶Eu,Tb的真空紫外光谱特性

采用高温固相反应法合成了 BaLaB9O1 6 ∶RE (RE =Eu ,Tb)等离子荧光体 ,测量了它们的真空紫外激发光谱和 14 7nm激发下的发射光谱。结果表明 ,硼氧阴离子基团基质吸收带位于 15 0nm附近 ,Eu3+ 电荷迁移带位移 2 5 0nm附近 ,Tb3+ 的 4f 5d吸收位于 15 0～ 2 60nm的区域内 ,相关数据表明 ,基质与稀土离子之间存在能量传递。

16-and 18-electron Cp*Rh complexes with 1,2-dicarba-closo-dodecabofane(12)-1,2-dichalcogenolato ligands, as studied by multinuclear magnetic resonance

The reaction of [Cp*RhCl2](2) 1 with dilithium 1,2-dicarba-closo-dodecaborane(12)-1,2-dithiolate (a) and -diselenolate (b) afforded the 16-electron rhodium(III) half-sandwich complexes Cp*Rh[E2C2(B10H10)] [E=S (3a), Se (3b)]. The 18-electron trimethylphosphane rhodium(III) half-sandwiches Cp*Rh(PMe3)[E2C2(B10H10)] 4a-c were prepared from the reaction of Cp*RhCl2(PMe3) 2 with the same dichalcogenolates, including the ditelluride (c). The complexes 4a,b could also be obtained from the reaction of 3a,b with trimethylphosphane. The molecular geometry of 4b was determined by X-ray structural analysis. The 16-electron complexes 3 an monomeric in solution as shown by multinuclear magnetic resonance (H-1-, B-11-, C-13-, P-31- Se-77-, Rh-103-, Te-125-NMR). also in comparison with the data for the trimethylphosphane analogues 4a-c and for 6a in which the rhodium bears the eta(5)-1,3-C5H3 Bu-t(2) ligand. The Rh-103 nuclear shielding is reduced by 831 ppm (3a) and 1114 ppm (3b) with respect to the 18-electron complexes 4a,b. Similarly, the Se-77 nuclear shielding in 3b is reduced by 676.4 ppm with respect to that in 4b. (C) 1999 Elsevier Science S.A. All rights reserved.

Hydrothermal synthesis and crystal structure of sandwich-like heteropolymolybdophosphates

Sandwich-like heteropoly molybdochromophosphates of supermolecular compound [NH3(CH2)(6)NH3](2)H-3{Cr[Mo6O15(HPO4)(H2PO4)(3)](2)}. 4H(2)O has been hydrothermally synthesized and the single crystal structure has been determined by X-ray diffraction. The crystal data are has follows: triclinic, space group P (1) over bar a=12.156(2), b=12.809(3), c=13.530(3) Angstrom, alpha=102.46(3)degrees, beta=93.67(3)degrees, gamma=93.46(3)degrees, V=2046.9(7) Angstrom(3), Z=1, M-r=2768.69, D-c=2.246 g/cm(-3), F(000)=1337, mu=2.162 mm(-1). The structure has been refined to R=0.0666 and wR=0.1745 by full-matrix least-squares method. The title compound is composed of 1, 6-diaminohexane, water molecules, and {Cr[Mo6O15(HPO4)(H2PO4)(3)](2)}(7-) anion which consists of six oxygen atoms from two [Mo6P4] units with a sandwich-like transition metal atom Cr located at the center of symmetry.

Calculation of second-order nonlinear optical coefficients of KTiOPO4 and KTiOAsO4

The second-order nonlinear optical tensor coefficients of both KTiOPO4 (KTP) and KTiOAsO4 (KTA) are calculated from the chemical bond viewpoint. All constituent chemical bonds of both crystals are considered, and contributions of each type of bond to the total linearity and nonlinearity are determined. Calculated results agree satisfactorily with experimental data in both signs and numerical values. The calculation shows that though TiO6 groups and P(1)O-4 or As(1)O-4 groups have relatively larger linear contributions, they can only produce an advantageous environment for KOx (x = 8, 9) groups and P(2)O-4 or As(2)O-4 groups in nonlinear optical contributions. The origin of nonlinearity of KTP family crystals comes from the KOx (x = 8, 9) and P(2)O-4 groups in their crystal structures. Furthermore, the difference in optical nonlinearities of KTP type crystals is analyzed, based on the detailed calculation of nonlinearities of both KTP and KTA. (C) 1999 Academic Press.

BaLaB_9O_(16):Re(Re=Eu,Tb)的真空紫外光谱特性的研究

近几十年来,人们对稀土离子的发光已进行了大量的研究,这些研究主要集中在紫外可见波段,对真空紫外区的光谱与能级研究的较少,相关光谱与能级缺乏足够的认识。近年来,随着大屏幕PDP的发展,寻找新型高效真空紫外激发的荧光体(等离子荧光体)已成为目前发光领域的研究热

Intel 8279芯片在8位和16位米字LED显示电路中的应用

本文简要介绍了16段米字LED字符管的动态扫描，以及通用显示和键盘接口器件Intel8279芯片的显示接口结构和功能，讨论了通过一定的附加电路来扩展Intel8279的显示功能，使之控制8位和16位的米字LED字符管的动态显示，并结合两种具体的硬件电路和程序，说明了两种方案的实现方法和工作原理。

CRYSTAL-STRUCTURES OF LN(NO3)(3) (LN=EU,LU) COMPLEXES WITH A CROWN-ETHER (16-CROWN-5)

The crystal structures of Ln(NO3)(3)(Ln = Eu,Lu) complexes with 16-crown-5 are reported. In [Eu(NO3)(2)(CH3CN)(16-crown-5)][Eu(NO3)(4)(H2O)2].1/2(16-crown-5) one Eu-III ion is coordinated to two bidentate nitrate ions, one acetonitrile molecule and five o