Dispersion copolymerization of acrylamide with quaternary ammonium cationic monomer in aqueous salts solution

Dispersion copolymerization of acrylamide (AM) with 2-methylacryloylxyethyl trimethyl ammonium chloride (DMC) has been carried out in aqueous salts solution containing ammonium sulfate and sodium chloride with poly(acryloylxyethyl trimethyl ammonium chloride) (PDAC) as the stabilizer and 2,2'-azobis[2-(2-inidazolin-2-yl)propane]-dihydro chloride (VA-044) as the initiator. A new particle formation mechanism of the dispersion polymerization for the present system has been proposed. The effects of inorganic salts and stabilizer concentration on dispersion polymerization have been investigated. The results show that varying the salt concentration could affect the morphology and molecular weight of the resultant copolymer particles significantly. With increasing the stabilizer concentration, the particle size decreased at first and then increased, meanwhile the effect on the copolymer molecular weight was the contrary. These results had been rationalized based on the proposed mechanism.

Formation of mesophase mono-domains and micro-structures in thin films of a series of copolyethers containing both odd-numbered methylene units

The structural and morphological evolution of mono-domains in thin films has been investigated for a series of liquid crystalline (LC) copolyethers. The copolyethers studied were synthesized by the reaction of 1-(4-hydroxy-4 ' -biphenylyl)-2-(4-hydroxyl-phenyl)propane (TPP) with 1,7-dibromoheptane and 1,11-undecane at different compositions (coTPPs-7/11). In contrast to the solution-cast thin films without annealing, which exhibit the isotropic homogeneous molecular orientation, mono-domains with a homeotropic alignment were found in coTPP-7/11(5/5) after the thin films were annealed in the high-temperature columnar phase (Phi '). Similar to the nucleation process in polymer crystallization, transmission electron microscopic observations show that small mono-domains appear in the initial stage of annealing, where molecules form a uniaxial in-plane chain orientation. With increasing annealing time, the molecular orientation gradually became tilted with respect to the substrate surface, and finally, a uniaxial homeotropic molecular orientation was achieved after a prolonged annealing time. The lateral size of mono-domains was found to increase continuously with annealing time and grew into a circular shape, indicating an isotropic lateral growth scheme which implies a hexagonal molecular packing proved by the electron diffraction experiments.

Electrostatic-field-induced chain alignment of liquid crystalline copolyether TPP thin films

A liquid crystalline (LC) copolyether has been synthesized from 1-(4-hydroxy-4'-biphenyl)-2-(4-hydroxyphenyl)propane with 1,7-dibromoheptane and 1,11-dibromoundecane with a 50/50 (both in %) equal composition of the 7- and 11-methylene monomers [coTPP-7/11(5/5)]. A mono-domain with a homeotropic alignment can be induced by a thin film surface in the LC phase. When an electrostatic field is applied to the surface-induced mono-domains parallel to the thin film surface normal, the molecular alignment undergoes a change from the homeotropic to uniaxial homogeneous arrangement. However, when the field is applied to a direction perpendicular to the thin film surface normal. the molecular alignment is about 10 degrees -tilt with respect to the homeotropic alignment toward the a*-axis. This is because the permanent dipole moment of the copolyether is not right vertical to the molecular direction. The calculation of molecular dipoles indicates that the permanent dipole moment of this copolyether is about 70 degrees away from the molecular axis, which leads to a negative dielectric anisotropy. It is speculated that the 10 degrees- rather than 20 degrees -tilt is due to a balance between the alignment induced by the electrostatic field and the surface. In the electrostatic field, molecules are subjected to a torque tau, which is determined by the permanent dipole moment P and the electrostatic field E: tau = P x E. The molecular realignment in both parallel and perpendicular directions to the thin film surface normal is determined by satisfying the condition of tau = P x E = 0. (C) 2001 Elsevier Science Ltd. All rights reserved.

Phase identification in a series of liquid crystalline TPP polyethers and copolyethers having highly ordered mesophase structures. 7. Phase structures in a series of copolyethers containing odd and even numbers of methylene units of different compositions

A series of liquid crystalline copolyethers have been synthesized from 1-(4-hydroxy-4'-biphenyl)-2-(4-hydroxyphenyl)propane with 1,7-dibromoheptane and 1,12-dibromododecene [coTPPs(7/12)], which represents copolyethers containing both odd and even numbers of methylene units. The molar ratio of odd to even methylene units in this series ranges from 1/9 to 9/1. The coTPPs(7/12) exhibit multiple phase transitions during cooling and heating in differential scanning calorimetry experiments. For all these thermal transitions, a small undercooling and superheating dependence is observed upon cooling and heating at different rates. Three types of phase behaviors can be classified in coTPPs(7/12) on the basis of the structural analyses by wide-angle X-ray diffraction on powder and fiber samples and by electron diffraction experiments in transmission electron microscopy. At room temperature, highly ordered smectic and smectic crystal (SC) phases are identified in coTPPs(7/12: 1/9 and 2/8), which is similar to the homopolymer TPP(m = 12). The coTPPs(7/12: 3/7, 4/6, and 5/5) possess a hexagonal columnar (Phi(H)) phase in which the molecular and columnar axes are parallel to the fiber direction and perpendicular to the hexagonal lateral packing. The coTPPs(7/12: 6/4, 7/3, and 8/2) possess a tilted hexagonal columnar (Phi(TH)) phase with a single tilt angle which increases with the increasing composition of the seven-numbered methylene units. However, in coTPP(7/12: 9/1), a Phi(TH) phase with multiple tilt angles is found. Upon heating, phase structures in most coTPPs(7/12) involving the columnar phases enter directly into the nematic (N) phase, while the coTPP(7/12: 1/9) exhibits a highly ordered smectic F (S-F) phase before it reaches the N phase. One exception is found in coTPP(7/12: 2/8), wherein the transformation from the S-F to Phi(H) occurs prior to the N phase. Combining the copolymer phase behaviors observed with the corresponding homopolymers TPP(n = 7) and TPP(m = 12), a phase diagram describing transition temperatures with respect to the composition can be constructed.

Phase identification in a series of liquid crystalline TPP polyethers and copolyethers having highly ordered mesophase structures. 6. Structure changes from smectic to columnar phases in a series of copolyethers containing odd and even numbers of methylene units in equal molar composition

A series of liquid crystalline copolyethers has been synthesized from 1-(4-hydroxy-4'-biphenyl)-2-(4-hydroxyphenyl)propane and different alpha,omega-dibromoalkanes [coTPP(n/m)]. In this report, coTPPs having n = 5, 7, 9, 11 and m = 12 are studied, which represent copolyethers having both varying odd number and a fixed even number of methylene units. The compositions were fixed at an equal molar ratio (50/50). These coTPPs(nlm) show multiple phase transitions during cooling and heating in differential scanning calorimetry experiments. The undercooling dependence of these transitions is found to be small, indicating that these transitions are close to equilibrium, Although the coTPPs possess a high-temperature nematic (N) phase, the periodicity order along the chain direction is increasingly disturbed when the length of the odd-numbered methylene units decreases from n 11 to 5. in the coTPPs(5/12, 7/12, and 9/12), wide-angle X-ray diffraction experiments at different temperatures show that, shortly after the N phase formation during cooling, the lateral molecular packing improves toward a hexagonal lattice, as evidenced by a gradual narrowing of the scattering halo. This process represents the possible existence of an exotic N phase, which serves as a precursor to the columnar (Phi(H)) phase. A further decrease in temperature leads to a (PH phase having a long-range ordered, two-dimensional hexagonal lattice. In coTPP(11/12), the phase structures are categorized as highly ordered and tilted, smectic and smectic crystal phases, similar to homoTPPs, such as the smectic F (S-F) and smectic crystal G (SCG) phases. An interesting observation is found for coTPP(9/12), wherein a structural change from the high-temperature Phi(H) phase to the low-temperature S-F phase occurs. It can be proven that, upon heating, the well-defined layer structure disappears and the lateral packing remains hexagonal. The overall structural differences in this series of coTPPs between those of the columnar and highly ordered smectic phases are related to the disorders introduced into the layer structure by the dissimilarity of the methylene unit lengths in the comonomers.

Lanthanide coordination polymers with dicarboxylate-like ligands: crystal structures of polymeric lanthanum(III) and terbium(III) complexes with flexible double betaines

Four novel polymeric lanthanide(III) complexes of two new double betaine derivatives have been synthesized and structurally determined. In [{La-2(L-1)(2)(H2O)(9)}(n)]Cl-6n. 2nH(2)O (1) and [{Tb(L-1)(H2O)(4)}(n)]Cl-3n. nH(2)O (2) (L-1 =4,4'-trimethylenedipyridinio-N,N'-diacetate), the lanthanide(III) ions form a two-dimensional layer in which each pair of lanthanide(III) ions is bridged by two syn-anti mu-carboxylato-O,O' groups. Adjacent layers are cross-linked through hydrogen bonds among aqua ligands, lattice water molecules and chloride ions, to form a three-dimensional network. Isomorphous [{Ln(L-1)(H2O)(4)}(n)]Cl-3n. 5nH(2)O (Ln=La, 3; Ln=Tb, 4; L-2=1,3 bis(pyridinio-4-carboxylato)-propane) each contain a centrosymmetric paddle-wheel-like dimeric unit in which each pair of adjacent metal atoms is bridged by four syn-syn mu-carboxylato-O,O' groups that are oriented nearly perpendicular to each other about the metal-metal axis. Neighboring dimeric subunits are bridged by a pair of flexible LL ligands into a polymeric chain. Adjacent chains are inter-linked by hydrogen bonds among aqua ligands, lattice water molecules and chloride ions into a three-dimensional network. (C) 1999 Elsevier Science Ltd. All rights reserved.

Synthesis, crystal structure and luminescence studies of a lanthanide coordination polymer with a new double betaine ligand

A novel europium(III) coordination polymer with a new double betaine derivative, {[Eu(L')(NO3)(H2O)(3)](NO3)(2). 3.5H(2)O}(n) (L-1 = 1,3-bis(pyridinio-4-carboxylato)-propane) has been synthesized and its structure determined. Its luminescence properties have also been studied. The title metal carboxylate coordination polymer contains centrosymmetric dimeric units in which each pair of metal ions is linked by a pair of syn-anti carboxylato-O,O' groups, and each pair of such dimeric units is bridged by the backbones of L-1 ligands to form infinite double chains in the b direction. These metal carboxylate chains are further cross-linked by hydrogen bonds among both coordinated and discrete nitrate anions, aqua ligands and lattice water molecules to form a three-dimensional network. Luminescent data show that the L-1 ligand is a good energy donor and the complex has a relatively long luminescent lifetime.

ARYLIDENE COPOLYETHER SULFONES .2. SYNTHESIS END CHARACTERIZATION OF SOME NEW COPOLYETHER SULFONES CONTAINING DIBENZYLIDENE CYCLOHEXANONE MOIETIES

New copolyether sulfones containing 2,6-bis(p-oxo-benzylidene)cyclohexanone and 2,6-bis(o,p-dioxo-benzylidene)cyclohexanone moieties were prepared in the conventional literature manner by condensing the dipotassium salts of 2,6-bis(p-hydroxybenzylidene)cyclohexanone (III), 2,6-bis(o,p-dihydroxybenzylidene)-cyclohexanone (V), and 2,2-bis(p-hydroxyphenyl)propane (Bisphenol A, VII) with 4,4'-dichlorodiphenyl sulfone (VI), or by condensing the dipotassium salts of III and VII with a new benzylidene cyclohexanone sulfone macromer (X). Finally, the polycondensation reaction of sulfonyl bis(p-benzaldehydeoxo-p-phenylene) (IX) with cyclohexanone leads to an unsaturated copolymer (XVI). The resulting copolyether sulfones were confirmed by IR, H-1-NMR, viscometry, elemental analysis, thermooptical (TOA), x-ray, and thermogravimetric (TGA) measurements.

PENDANT FUNCTIONAL-GROUP COPOLYETHER SULFONES .1. SYNTHESIS AND CHARACTERIZATION OF NEW COPOLYETHER SULFONES WITH PENDANT ALDEHYDE GROUPS MODIFIED INTO PHENOLIC AZOMETHINE GROUPS

New functional copolyether sulfones with pendant aldehyde groups were synthesized by the classical polycondensation reaction between 4,4' -dichlorodiphenyl sulfone (I) and various bisphenols such as 5,5'-methylene bis-salicylaldehyde (II-2), 2,2-bis( 4-hydroxyphenyl)propane (III), and 2,6-bis(4-hydroxybenzylidene)cyclohexanone (IV). Condensation reaction with 4-aminophenol led to pendant phenolic azomethine groups containing copolyether sulfones. The structures of the resulting polymers were confirmed by IR, H-1-NMR spectra, and elemental analyses. The polymers were characterized by reduced viscosity, solubility, thermal stability, DSC, and x-ray diffraction measurements.

ARYLIDENE COPOLYETHER SULFONES .1. SYNTHESIS AND CHARACTERIZATION OF SOME NEW COPOLYETHER SULFONES CONTAINING DIBENZYLIDENE CYCLOPENTANONE MOIETIES

New copolyether sulfones containing 2,5-bis(4-oxo-benzylidene)-cyclopentanone moieties were prepared in the conventional literature manner by condensing the dipotassium salts of 2,5-bis(4-hydroxybenzylidene)cyclopentanone (I) and 2,2-bis(4-hydroxyphenyl)propane (Bisphenol A, III) with 4,4'-dichlorodiphenyl sulfone (II), or by condensing the dipotassium salts of I with chlorine-terminated Bisphenol A-4,4'-dichlorodiphenylsulfone copolymers (V). The resulting copolyether sulfones were confirmed by IR, viscometry, DSC measurements, thermooptical analysis (TOA), and thermogravimetric analysis (TGA).

A gas chromatographic analysis of light hydrocarbons on a column packed with modified silica gel

A one-meter long column packed with silica gel is used to separate light hydrocarbons. The silica gel has been modified with several kinds of gas chromatography stationary phases. Among these, PEG 2000 shows fairly good effect when using 80-100 meshes silica gel for the separation of mixture of methane, ethane, ethylene, acetylene, propane, propylene and n-, i-butane. The different behavior of silica gel between batch to batch is also found. When silica gel is coated with a small amount of Al2O3 prepared with sol-gel method, better resolution has been observed on a 2-meter column compared with the non-modified silica gel.

Development and application of oxygen permeable membrane in selective oxidation of light alkanes

In this paper, oxygen permeable membrane used in membrane reactor for selective oxidation of alkanes will be discussed in detail. The recent developments for the membrane materials will be presented, and the strategy for the selection of the membrane materials will be outlined. The main applications of oxygen permeable membrane in selective oxidation of light alkanes will be summarized, which includes partial oxidation of methane (POM) to syngas and partial oxidation of heptane (POH) to produce H-2, oxidative coupling of methane (OCM) to C-2, oxidative dehydrogenation of ethane (ODE) to ethylene and oxidative dehydrogenation of propane (ODP) to propylene. Achievements for the membrane material developments and selective oxidation of light alkanes in membrane reactor in our group are highlighted.