大尺寸Ce：Lu1.6Y0.4SiO5闪烁晶体的生长和光谱特性

采用中频感应提拉法生长出尺寸为Ф60mm×110mm的Ce：Lu1.6Y0.4SiO5（LYSO）晶体,与LSO晶体相比,LYSO晶体的优势是提高了晶体质量、降低了熔点和原料成本等.在室温下测试了LYSO晶体的透过光谱、激发光谱和发射光谱,结果表明Y的加入使LSO晶体的吸收边向短波方向偏移.Ce^3＋的4f^1→5d^1跃迁吸收导致紫外区产生三个吸收带.发射光谱具有Ce^3＋典型的双峰特征,经Gaussian多峰值拟合,双峰395nm和418nm归属于Ce1发光中心,而435nm的发光峰与Ce2发光中心有

Growth and its spectroscopic properties of Sm : YAP crystal

Sm3+-doped yttrium aluminum perovskite (YAP) single crystal was grown by Czochralski (CZ) method. The absorption and fluorescence spectra along the crystallographic axis b were measured at room temperature. Judd-Ofelt theory was used to calculate the intensity parameters (Omega(t)), the spontaneous emission probability, the branching ratio and the radiative lifetime of the state (4)G(5/2). The peak emission cross-sections were also estimated at 567, 607, and 648 nm wavelengths. (c) 2006 Elsevier B.V. All rights reserved.

Luminescence studies of Ce : YAG using vacuum ultraviolet synchrotron radiation

Photoluminescence spectrum of Ce:YAG single crystal was studied employing vacuum ultraviolet (VUV) synchrotron radiation. Intrinsic absorption edge at about 52,000 cm(-1) was observed in the absorption spectrum. From the VUV excitation spectrum, the energy of the highest d-component of 53,191 cm(-1) (188 nm) for the Ce3+ ions in YAG was obtained at 300 K. The disappearance of the third 5d level at 37,735 cm(-1) (265 nm) in absorption and excitation spectra in our samples may be due to the impurity Fe3+ ions absorption. (C) 2006 Elsevier Ltd. All rights reserved.

Structural and optical properties of YAG : Ce3+ phosphors by sol-gel combustion method

High-quality Ce3+-doped Y3Al5O12 (YAG:Ce3+) phosphors were synthesized by a facile sol-gel combustion method. In this sol-gel combustion process, citric acid acts as a fuel for combustion, traps the constituent cations and reduces the diffusion length of the precursors. The XRD and FT-IR results show that YAG phase can form through sintering at 900 degrees C for 2 h. This temperature is much lower than that required to synthesize YAG phase via the solid-state reaction method. There were no intermediate phases such as YAlO3 (YAP) and Y4Al2O9 (YAM) observed in the sintering process. The average grain size of the phosphors sintered at 900-1100 degrees C is about 40 nm. With the increasing of sintering temperature, the emission intensity increases due to the improved crystalline and homogeneous distribution of Ce3+ ions. A blue shift has been observed in the Ce3+ emission spectrum of YAG:Ce3+ phosphors with increasing sintering temperatures from 900 to 1200 degrees C. It can be explained that the decrease of lattice constant affects the crystal field around Ce3+ ions. The emission intensity of 0.06Ce-doped YAG phosphors is much higher than that of the 0.04Ce and 0.02Ce ones. The red-shift at higher Ce3+ concentrations may be Ce-Ce interactions or variations in the unit cell parameters between YAG:Ce3+ and YAG. It can be concluded that the sol-gel combustion synthesis method provides a good distribution of Ce3+ activators at the molecular level in YAG matrix. (c) 2005 Elsevier B.V. All rights reserved.

铝酸镧单晶体中Ce^3＋的能级结构和荧光特性

采用提拉法成功生长了纯LaAlO3和掺铈的LaAlO3单晶体，测试了它们的远红外吸收谱，紫外吸收谱，荧光谱，根据吸收光谱确定了晶体中Ce^3+的能级结构，利用这一能级结构模型较好地解释了Ce：LaAlO3晶体的荧光光谱。

Effect of air annealing on the spectral properties of Ce : Y3Al5O12 single crystals grown by the temperature gradient technique

Five absorption hands, at 227, 300 340, 370 and 457nm, were observed in the optical absorption spectrum of Ce:Y3Al5O12 (Ce:YAG) crystals grown by the temperature gradient technique (TGT). The absorption bands at 227, 340, and 457 nm were identified Lis belonging to the Ce3+ -ion in the YAG crystal. A near UV optical emission band at 398nm was observed. with an excitation spectrum containing two bands, at 235 and 370nm. No fluorescence was detected under 300 nm excitation. The pair of absorption bands at 235 and 370 nm and the absorption band at 300 nm were attributed to the F- and F+-type color centers, respectively. The color centers model was also applied to explain the spectral changes in the Ce:YAG (TGT) crystal, including the reduction in the Ce 31 -ion absorption intensity, after annealing in an oxidizing atmosphere (air). (C) 2004 Elsevier B.V. All rights reserved.

Three-photon-excited upconversion luminescence of Ce3+: YAP crystal by femtosecond laser irradiation

Infrared to ultraviolet and visible upconversion luminescence was demonstrated in trivalent cerium doped YAlO3 crystal (Ce3+: YAP) under focused infrared femtosecond laser irradiation. The fluorescence spectra show that the upconverted luminescence comes from the 5d-4f transitions of trivalent cerium ions. The dependence of luminescence intensity of trivalent cerium on infrared pumping power reveals that the conversion of infrared radiation is dominated by three-photon excitation process. It is suggested that the simultaneous absorption of three infrared photons pumps the Ce3+ ion into upper 5d level, which quickly nonradiatively relax to lowest 5d level. Thereafter, the ions radiatively return to the ground states, leading to the characteristic emission of Ce3+. (c) 2005 Optical Society of America.

Color centers and charge state change in Ce : YAG crystals grown by temperature gradient techniques

Color centers and impurity defects of Ce:YAG crystals grown in reduction atmosphere by temperature gradient techniques have been investigated by means of gamma irradiation and thermal treatments. Four absorption bands associated with color centers or impurity defects at 235, 255, 294 and 370 nm were observed in as-grown crystals. Changes in optical intensity of the 235 and 370 nm bands after gamma irradiation indicate that they are associated with F+-type color center. Charge state change processes of Fe3+ impurity and Ce3+ ions take place in the irradiation process. The variations of Ce3+ ions concentration clearly indicate that Ce4+ ions exist in Ce:YAG crystals and gamma irradiations could increase the concentration of Ce3+ ions. Annealing treatments and the changes in optical density suggest that a heterovalent impurity ion associated with the 294 nm band seems to be present in the crystals. (c) 2005 Elsevier B.V. All rights reserved.

Color centers and charge state recharge in gamma-irradiated Yb : YAP

Gamma-ray irradiation induced color centers and charge state recharge of impurity and doped ion in 10 at.% Yb:YAP have been studied. The change in the additional absorption (AA) spectra is mainly related to the charge exchange of the impurity Fe2+, Fe3+ and Yb3+ ions. Two impurity color center bands at 255 and 313 nm were attributed to Fe3+ and Fe2+ ions, respectively. The broad AA band centered at 385 nm may be associated with the cation vacancies and F-type center. The transition Yb3+ -> Yb2+ takes place in the process of gamma-irradiation. Oxygen annealing and gamma-ray irradiation lead to an opposite effect on the absorption properties of the Yb:YAP crystal. In the air annealing process, the transition Fe2+ -> Fe3+ and Yb2+ -> Yb3+ take place and the color centers responsible for the 385 nm band was destroyed. (c) 2005 Elsevier B.V. All rights reserved.

Ce：Lu2Si2O7闪烁晶体的结构和光谱特性

采用中频感应提拉法生长出Ce：Lu：Si2O7(Ce：LPS)晶体．通过x射线粉末衍射分析，晶体结构属单斜晶系的C21m空间群·光学显微镜下可观测到晶体的(110)解理．在室温下测试了Ce：LPS晶体的吸收光谱、激发光谱和发射光谱。结果表明，Ce：LPS晶体的吸收峰只有两个，分别位于302和349nm，且与激发峰的位置一致，归因于Ce^3+的4f^1→5d^1跃迁的特征吸收所致．发射光谱具有Ce^3+典型的双峰特征，经Gaussian多峰值拟合，带状谱是由384和407nm两个发射峰叠加而成，且后者的强度

Gamma-irradiation effects on Ce-doped YAG crystals grown by Cz and TGT method

Gamma-rays radiation effects on Ce:YAG crystals grown by Czochralski (Cz) and temperature gradient techniques (TGT) have been studied by means of optical absorption and luminescence spectra. Valence of Ce3+ ion changes during the gamma-ray irradiation process and this result indicates Ce4+ ion may exist in both Cz-Ce:YAG and TGT-Ce:YAG crystals. Thermally stimulated luminescence measurements reveal intense thermoluminescence peaks in gamma-irradiated Ce:YAG crystals and trap parameters were calculated by general-order kinetics expression. (C) 2006 Elsevier B.V. All rights reserved.

室温下光纤耦合二极管泵浦Tm：YAP激光器

为实现室温下小型化、高效率的1.9μm激光输出,采用793.5 nm激光二极管泵浦Tm：YAP晶体,晶体采用热电制冷及风冷的方式控制在18℃,采用1∶1的聚焦耦系统,获得功率为2.2 W、中心波长为1928 nm的激光输出,光光转换效率为31%,斜率效率达41%。对影响激光输出的耦合输出率、腔型、腔长、晶体工作温度等因素进行了实验分析,实验结果表明：输出功率的变化与温度基本成线性关系,当增加激光谐振腔长时,由于高阶模式损耗加大以及晶体热透镜效应的加重导致腔内损耗加大,输出功率和斜率效率都有所下降。

Spectroscopic properties of Yb:YAP crystal

The 10at% Yb-YAP crystal has been grown by the Czochralski method. The absorption and emission spectra and fluorescence lifetime of Yb:YAP crystal at room temperature were studied. There is a strong absorption band centered at 959 nm and the absorption cross-section of 1.51 × 10^-20 cm². The emission cross-section at 1040 nm is 0.6 × 10^-20 cm² and the fluorescence lifetime is about 1.2 ms. The effects of O₂-annealing on the spectral properties were studied. The spectroscopic properties strongly depended on the axis direction and b axis was the best direction for laser output. The spectrum parameters of Yb:YAP and Yb:YAG crystal were compared.}

激光二极管抽运Tm：YAP激光器获得5W连续波输出

2μm波长激光对人眼安全，在相干探测风切变、非线性频率转换等方面有重要应用。2μm波长激光还可应用到激光医疗，由于其吸收深度浅，手术精度高于发射1μm波长的激光。

高效室温下激光二极管泵浦Tm:YAP激光器

文章报道了室温下二极管泵浦Tm：YAP激光器，最大输出功率5.2瓦，波长为1981nm，斜率效率是30％。实验测量800nm左右晶体的吸收谱以及1800nm附近的荧光发射谱。此外，讨论了输出功率随晶体工作温度关系。