Spectroscopic, and thermal studies of some new binuclear transition metal(II) complexes with hydrazone ligands containing acetoacetanilide and isoxazole

A new chelating ligand, 2-(2-(5-tert-butylisoxazol-3-yl)hydrazono)-N-(2,4-dimethylphenyl)-3-oxobutanamide (HL), and its four binuclear transition metal complexes, M-2(L)(2) (mu-OCH3)(2) [M = Ni(II), Co(II), Cu(II), Zn(II)], were synthesized using the procedure of diazotization, coupling and metallization. Their structures were postulated based on elemental analysis, H-1 NMR, MALDI-MS, FT-IR spectra and UV-vis electronic absorption spectra. Smooth films of these complexes on K9 glass substrates were prepared using the spin-coating method and their absorption properties were evaluated. The thermal properties of the metal(II) complexes were investigated by thermogravimetry (TG) and differential scanning calorimetry (DSC. Different thermodynamic and kinetic parameters namely activation energy (E

2-氨基-6-乙氧基苯并噻唑类偶氮染料及其金属鏊合物的合成及光学热学性能研究

合成了2-（2-氨基-6-乙氧基苯并噻唑基偶氮）-5-（N,N-二乙基氨基）三氟甲基磺酰苯胺偶氮染料（EBTDATFS）及其与乙酸镍、乙酸钴、乙酸铜、乙酸锌等金属盐鏊合的金属鏊合物。通过红外光谱、紫外-可见吸收光谱和MALDI质谱等对染料及其金属鏊合物进行了结构表征;使用旋涂方法在K9玻璃和抛光的单晶硅基片上制备薄膜;研究了镍金属鏊合物的热学性能;使用椭偏仪研究了Ni和Zn鏊合物的光学常数。结果表明：4种金属鏊合物薄膜最大吸收光谱为621-629nm,且长波边吸收峰陡峭;TGA-DSC测试结果表明镍金属鏊

新型多氮杂环金属配合物的合成及其光谱研究

采用溶液析出法,合成了以2-（2′-羟基-5′-甲基苯基）苯并三唑（HMPB）为配体的多氮杂环金属配合物M（HMPB）2（M=Co,Ni）,利用元素分析、激光解析飞行时间质谱等进行了表征,并研究了新配合物的红外特征光谱和紫外-可见电子吸收光谱。结果表明：HMPB配体通过N和O原子与中心金属以二齿形式配位,中心金属的配位数为4;配合物红外特征吸收谱带位于400～2 500 cm^-1,形成金属配合物后,2-（2′-羟基-5′-甲基苯基）苯并三唑的羟基的伸缩振动吸收、CN振动峰和C─O特征吸收有明显改变,同时确定了配位键M─N和M─O的特征峰位置;配合物在紫外区有强吸收,其最大吸收峰位于335～345 nm。

Preparation, characterization and gas sensing properties of nickel octa-iso-pentyloxynaphthalocyanine spin-coating films

Spin-coated films of nickel 1,6,10,15,19,24,28,33-octa-iso-pentyloxy-2,3-naphthalocyanine complex were obtained and characterized by UV-vis absorption spectroscopy. A linear relationship between the absorbance and solution concentration was observed. Low concentration solutions could afford smooth and homogeneous film surfaces as indicated by atomic force microscopy. The film structure was studied by small angle X-ray diffraction. The films were used for NO2 sensing experiments. The results indicate that the elevation of sensing temperature can shorten the response time and increase recovery ratio and response magnitude of the sensing films. High NO2 concentration can also shorten response time. (C) 2008 Elsevier B.V. All rights reserved.

Rare earth dibenzoylmethane complexes for potential application as high-density recordable optical recording materials

Three kinds of rare earth complexes derived from dibenzoylmethane (DBM) ligand were synthesized by reacting free ligand and different rare earth ions(La (3+), Sm3+ and Gd3+). Their contents and structures were postulated based on elemental analysis, LDI-TOF-MS, FT-IR spectra and UV-Vis spectra. Smooth films on K9 glass substrates were prepared using the spin-coating method. Their solubility in organic solvents, absorption and reflection properties of thin film and thermal stability of these complexes were evaluated. These complexes would be a promising recording material for high-density digital versatile disc-recordable (HD-DVD-R) system. (c) 2007 Elsevier B.V. All rights reserved.

Nickel(II) and copper(II) complexes containing 2-(2-(5-substitued isoxazol-3-yl)hydrazono)-5,5-dimethylcyclohexane-1,3-dione ligands: Synthesis, spectral and thermal characterizations

Two new hydrazone chelating ligands, 2-(2-(5-methylisoxazol-3-yl)hydrazono)-5,5-dimethylcyclohexane-1,3-dione (HL1) and 2-(2-(5-tert-butylisoxazol-3-yl)hydrazono)-5,5-dimethylcyclohexane- 1,3-dione (HL2), and their nickel(II) and copper(II) complexes were synthesized using the procedure of diazotization, coupling and metallization. Their structures were postulated based on elemental analysis, H-1 NMR, ESI-MS, FT-IR spectra and UV-vis electronic absorption spectra. Smooth films of these complexes on K9 glass substrates were prepared using spin-coating and their absorption properties were evaluated. The thermal properties of the metal(II) complexes were investigated by thermogravimetry (TG) and differential thermogravimetry (DTG). Different thermodynamic and kinetic parameters namely activation energy (E

Formation, thermal, optical and physical properties of GeS2-Ga2S3-AgCl novel chalcohalide glasses

Novel GeS2-Ga2S3-AgCl chalcohalide glasses had been prepared by melt-quenching technique, and the glass-forming region was determined by XRD, which indicated that the maximum of dissolvable AgCl was up to 65 mol%. Thermal and optical properties of the glasses were studied by differential scanning calorimetry (DSC) and Visible-IR transmission, which showed that most of GeS2-Ga2S3-AgCl glasses had strong glass-forming ability and broad region of transmission (about 0.45-12.5 mu m). With the addition of AgCl, the glass transition temperature, Tg decreases distinctly, and the short-wavelength cut-off edge (lambda(vis)) of the glasses also shifts to the long wavelength gradually. However, the glass-forming ability of the glass has a complicated evolutional trend depended on the compositional change. In addition, the values of the Vickers microhardness, H (v) , which decrease with the addition of AgCl, are high enough for the practical applications. These excellent properties of GeS2-Ga2S3-AgCl glasses make them potentially applied in the optoelectronic field, such as all-optical switch, etc.

Preparation and optical properties of Ag/PPy composite colloids

Ag/PPy (polypyrrole) composite colloids were prepared through the reaction of silver nitrate with pyrrole solution in DNIF either in the dark, or under the irradiation of femtosecond laser (fs) pulse or UV lamp. The UV-vis spectra of the nanocomposite colloid display an intense absorption band around 620 nm, accompanied by a weak one around 470 nm. The colors and optical absorption spectra of as-synthesized colloids can be reversibly tuned between blue and red, corresponding to absorption band of 620 urn and 526 urn, within few seconds by adding base and acid solutions or gases in turn into the composite colloid suspension. In addition, excess of H+ solution enhanced the absorption band around 470 nm and, at the same time, depressed that around 620 nm. The possible mechanism for the formation and optical absorption properties of the Ag/PPy composite colloid was proposed. (C) 2006 Elsevier B.V. All rights reserved.

Effect of processing parameters on the optical properties of TiO2/ormosil planar waveguide

Hybrid TiO2/ormosil waveguiding films have been prepared by the sol-gel method at low thermal treatment temperature of 150° C. The influence of processing parameters including the molar ratios of titanium butoxide (Ti(OBu)(4))/3-glycidoxypropyltrimethoxysilane (GLYMO) and H2O/Ti(OBu)(4) (expressed as R), especially aging of sot on the optical properties was investigated. The optical properties of films were measured with scanning electron microscope (SEM), UV/VIS/NIR spectrophotometer (UV-Vis), m-line and the scattering-detection method. The results indicate that the film thickness increases with the increase of sol aging time, but the variation of refractive index as a function of sot aging time depends on the relative ratios of GLYMO to Ti(OBu)(4). Higher transmittance and lower attenuation of the planar waveguide can be obtained in the sol with lower Ti(OBu)(4) contents and shorter aging time.

Optical and surface properties of hybrid TiO2/ormosil planar waveguide prepared by the sol-gel process

Two kinds of silanes, 3-glycidoxypropyltrimethoxysilane (GLYMO) and 3-trimethoxysililpropylmethacrylate (TMSPM), were used to prepare ormosil waveguide films by the sol-gel method. Thirty percent Ti(OBu)(4) and 70% silane were contained in the precursor sets. The properties of films were measured by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), UV/VIS/NIR spectrophotometer (UV-vis), atomic force microscopy (AFM), m-line and scattering-detection method. The films from GLYMO and TMSPM precursors exhibit similar thickness (2.58 mu m for GLYMO, 2.51 mu m for TMSPM) and refractive index (1.5438 for GLYMO, 1.5392 for TMSPM, lambda=632.8 nm), but the film from TMSPM precursor has higher propagation loss (1.024 dB/cm, lambda=632.8 nm) than the film prepared from GLYMO (0.569 dB/cm, lambda=632.8 nm). Furthermore, the film prepared from TMSPM is easy to be opaque and cracks during coating whereas the same phenomenon was not found for the film prepared with GLYMO. It is confirmed that GLYMO is a better precursor than TMSPM for waveguide film preparation. (C) 2005 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Effect of water content in sol on optical properties of hybrid sol-gel derived TiO2/SiO2/ormosil film

Sol-gel derived TiO2/SiO2/ormosil hybrid planar waveguides have been deposited on soda-lime glass slides and silicon substrates, films were heat treated at 150 degreesC for 2 h or dried at room temperature. Different amounts of water were added to sols to study their impacts on microstructures and optical properties of films. The samples were characterized by m-line spectroscopy, Fourier transform infrared spectroscopy (FT-IR), UV/VIS/NIR spectrophotometer (UV-vis), atomic force microscopy (AFM), thermal analysis instrument and scattering-detection method. The refractive index was found to have the largest value at the molar ratio H2O/OR = 1 in sol (OR means -OCH3, -OC2H5 and -OC4H9 in the sol), whereas the thickest film appears at H2O/OR = 1/2. The rms surface roughness of all the films is lower than 1.1 nm, and increases with the increase of water content in sol. Higher water content leads to higher attenuation of film. (C) 2004 Elsevier B.V. All rights reserved.

Preparation and characterization of hybrid ZnO/ormosils films

Hybrid ZnO/ormosils Elms are prepared by the sol-gel method. A FT-IR spectrometer, 900 UV/VIS/NIR spectrophotometer, atomic force microscope, and ellipsometer are employed to investigate microstructure and optical properties of the films fired at different temperatures. The results show that the films with high transmittance and low surface roughness could be obtained at the heat-treatment temperature of 150 degrees C, the refractive index and thickness of the film are 1.413, 2.11 mu m, respectively. Higher temperatures (350 degrees C, 550 degrees C) change the Elm microstructure severely, and then decrease the transmittance of the films.

熔制条件对铋酸盐玻璃性质的影响

采用传统的玻璃熔融法制备了组成为60Bi2O3-20B2O3-15SiO2-5La2O3(mol%)的铋酸盐玻璃， 系统研究了不同工艺过程对玻璃性能的影响. 分析了样品ICP的成分，扫描电镜，X-射线衍射谱， 差热分析和紫外-可见-近红外透过光谱测试. 结果表明：使用刚玉坩埚能提高玻璃的抗析晶稳定性 和透过率，陶瓷坩埚和白金坩埚均受到严重腐蚀，玻璃组分也随之发生很大变化. 当熔制温度从1 100 ℃变化到1 300 ℃时，玻璃的颜色从浅黄色变到深红棕色. 尤其是白金粒子被腐蚀进入玻璃液 后，玻璃中很容易形成纳米颗粒或者团聚形成胶体粒子，在玻璃中形成色散源，加深玻璃的颜色， 降低透过率. 1 300 ℃下，白金粒子起到晶核剂的作用，生成Bi2Pt2O7和BiB3O6晶相，导致玻璃失透.

Extended bidirectional reflectance distribution function for polarized light scattering from subsurface defects under a smooth surface

By introducing the scattering probability of a subsurface defect (SSD) and statistical distribution functions of SSD radius, refractive index, and position, we derive an extended bidirectional reflectance distribution function (BRDF) from the Jones scattering matrix. This function is applicable to the calculation for comparison with measurement of polarized light-scattering resulting from a SSD. A numerical calculation of the extended BRDF for the case of p-polarized incident light was performed by means of the Monte Carlo method. Our numerical results indicate that the extended BRDF strongly depends on the light incidence angle, the light scattering angle, and the out-of-plane azimuth angle. We observe a 180 degrees symmetry with respect to the azimuth angle. We further investigate the influence of the SSD density, the substrate refractive index, and the statistical distributions of the SSD radius and refractive index on the extended BRDF. For transparent substrates, we also find the dependence of the extended BRDF on the SSD positions. (c) 2006 Optical Society of America.

Effects of annealing on microstructure and optical properties of TiO2 sculptured thin films

The evolution of microstructure and optical properties of TiO2 sculptured thin films under thermal annealing is reported. XRD, field emission SEM, UV-Vis-NIR spectra are employed to characterize the microstructural and optical properties. It is found that the optimum annealing temperature for linear birefringence is 500 degrees C. The maximum of transmission difference for linear birefringence is up to 18%, which is more than twice of that in as-deposited thin films. In addition, the sample annealed at 500 degrees C has a minimum of column angle about 12 degrees C. The competitive process between the microstructural and optical properties is discussed in detail. Post-annealing is a useful method to improve the linear birefringence in sculptured thin films for practical applications.