Spectroscopic properties and thermal stability of Er3+/Yb3+-codoped fluorophosphate glasses

A comprehensive study on the thermal stability and spectroscopic properties of Er3+/Yb3+-codoped Al(PO3)(3)-based fluorophosphate glasses is reported of the 1.5μ m fibre amplifiers in this paper. From optical absorption spectra, the Judd-Ofelt parameters of Er3+ in the glasses and several important optical properties, such as the radiative transition probability, the branching ratio and the spontaneous emission probability, have been calculated by using Judd-Ofelt theory. The fluorophosphate glass exhibits broadband near-infrared emission at 1.53μ m with a full width at half-maximum over 63nm, and a large calculated stimulated-emission cross-section of 6.85 x 10(-21)cm(2).

Influence of TeO2, PbF2, ZnF2 on the spectroscopic and lasing properties of Yb3+ doped fluorophosphate glass

The influence of TeO2 on the crystallization stability, thermal stability, spectroscopic and lasing properties of Yb3+ doped fluorophosphate (FP) glass was studied. It is shown that 2 mol% TeO2 is the optimum doping amount which results in better spectroscopic and lasing properties as well as improve the crystallization and thermal stabilities of the glass. In order to enhance the physical and optical properties further, the effect of PbF2 and ZnF2 to the TeO2 contained FP glasses is also investigated, which shows that PbF2 has advantages in improving the crystallization properties while ZnF2 is preferable in enhancing spectroscopic and lasing properties. Results indicate that the co-existence of TeO2, PbF2 or ZnF2 is an effective way to enhance the spectroscopic, lasing and physical properties of Yb3+ doped FP glasses. (c) 2004 Published by Elsevier B.V.

Spectroscopic properties of Er3+-doped tellurite glass for 1.55 mu m optical amplifier

Er3+-doped TeO2-BaO (Li2O, Na2O)-La2O3 tellurite glass system was prepared and their density, characteristic temperatures and optical properties were determined and investigated. For the TeO2-BaO-La2O3-Er2O3 system, composition with 10 mol% BaO presented the highest thermal stability and good infrared transmittance. Intense and broad 1.53 mu m infrared fluorescence were observed under 977 nm diode laser excitation and the most full width at half-maximum (FWHM) is similar to 60nm. According to absorption spectrum, we calculated the optical parameters by means of Judd-Ofelt and McCumber theory such as the fluorescence lifetimes which are about 2.72-3.25 ms and the maximum emission cross-sections which are similar to 1.0pm(2) at 1.531 mu m. The sigma(e) x FWHM value of composition with 10 mol% BaO for gain bandwidth is similar to 600 exceeding those in silicon and phosphate glasses. Our results indicated this kind of tellurite glasses could be used as an ideal host glass for optical amplifier. (c) 2005 Elsevier B.V. All rights reserved.

Spectroscopic and fluorescence decay behaviors of Yb3+ -doped SiO2-PbO-Na2O-K2O glass

The spectroscopic and fluorescent decay behaviors of Yb3+-doped SiO2-PbO-Na2O-K2O glass is reported in this work. Yb2O3 contents of 1, 1.5 and 2mol% are added into the glass. Through the measurement of absorption and fluorescence spectra, and fluorescent decay rate at room temperature and at low temperature (18 K), it is found that the nonradiative decay rate of Yb3+ ions is mainly determined by the interaction between residual hydroxyl groups and Yb3+ ions. Concentration quenching effect can be omitted in this glass up to the Yb3+ ion concentration of 8.98 x 10(20)/cm(3). Multiphonon decay rate is also very small because of the large energy gap between F-2(5/2) and F-2(7/2) levels of Yb3+ ions. (c) 2004 Elsevier B.V. All rights reserved.

Spectroscopic properties of Er3+ doped TeO2-BaO (Li2O, Na2O)-La2O3 glasses for 1.5-mu m optical amplifiers

This paper reports on the optical spectroscopic properties and thermal stability of Er3+-doped TeO2-BaO (Li2O,NaO)-La2O3 glasses for developing 1.5-mu m fiber amplifiers. Upon excitation at 977 nm laser diode, an intense 1.53-mu m infrared fluorescence has been observed with a broad full width at half maximum (FWHM) of about 60 nm for the Er3+-doped TeO2-BaO (Li2O, Na2O)-La2O3 glass with 10 mol% of BaO. The calculated fluorescence lifetime and the emission cross-sections of the 1.53-mu m transition are 2.91 ms and similar to 9.97 x 10(-21) cm(2), respectively. It is noted that the gain bandwidth, a, x FWHM, of the TeO2-BaO-La2O3Er2O3 glass is about 600, which is significantly higher than that in silicate and phosphate glasses. Meanwhile, it is interesting to note that the TeO2-BaO-La2O3-Er2O3 glass has shown a high glass thermal stability and good infrared transmittance. As a result, TeO2-BaO (Li2O, Na2O)-La2O3 glass with 10 mol% of BaO has been considered to be more useful as a host for broadband optical fiber amplifier. (c) 2005 Elsevier B.V. All rights reserved.

Effect of F- ions on spectroscopic properties of Yb3+-doped zinc-tellurite glasses

this paper is retracted

Effect of bismuth oxide introduction on spectroscopic properties of Er3+/Yb3+ co-doped aluminophosphate glasses

The absorption spectra, emission spectra and infrared spectra of Er3+/Yb3+ co-doped xBi(2)O(3)-(65 - x)P2O5-4Yb(2)O(3)-11Al(2)O(3)-5BaO-15Na(2)O were measured and investigated. Spontaneous emission probability, radiative lifetime and branching ratios of Er3+ were calculated according to the Judd-Ofelt theory. The role of substitution of Bi2O3 for P2O5 on luminescence of Er3+/Yb3+ co-doped aluminophosphate glasses has been investigated. The calculated radiative lifetimes (tau(rad)) for I-4(13/2) and I-4(11/2) were decreasing with Bi2O3 content increases, whereas the measured total lifetime (tau(meas)) for I-4(13/2) showed linearly increasing trends. The effect of Bi2O3 introduction on OH- groups was also discussed according to the IR transmittance spectra of glasses. It was found that FWHM of glasses were not affected with the substitution of Bi2O3 for P2O5. The emission spectra intensity increased with Bi2O3 content due to the decreases of phonon energy and OH- content in glasses. (C) 2007 Elsevier B.V. All rights reserved.

Preparation and spectroscopic properties of Yb-doped and Yb-Al-codoped high silica glasses

Yb-doped and Yb-Al-codoped high silica glasses have been prepared by sintering nanoporous glasses. The absorption, fluorescent spectra and fluorescent lifetimes have been measured and the emission cross-section and minimum pump intensities were calculated. Codoping aluminum ions enhanced the fluorescence intensity of Yb-doped high silica glass obviously. The emission cross-sections of Yb-doped and Yb-Al-codoped high silica glasses were 0.65 and 0.82 pm(2), respectively. The results show that Yb-Al-codoped high silica glass has better spectroscopic properties for a laser material. The study of high silica glass doped with ytterbium is helpful for its application in Yb laser systems, especially for high-power and high-repetition lasers. (C) 2007 Elsevier B.V. All rights reserved.