高硅氧发光玻璃的制备及其荧光性能

abstract {Silica glass is an attractive host matrix for the emission ions of rare earth and transition metal ions because it has small thermal expansion coefficient, strong thermal resistance, large fracture strength and good chemical durability and so on. However, a major obstacle to using it as the host matrix is a phenomenon of concentration quenching. In this paper, we introduces a novel method to restrain the concentration quenching by using a porous glass with SiO₂ content > 95% (in mass) and prepare intense fluorescence high-SiO₂ glasses and high-SiO₂ laser glass. The porous glass with high-SiO₂ content was impregnated with rare-earth and transition metal ions, and consequently sintered into a compact non-porous glass in reduction or oxidization atmospheres. Various intense fluorescence glasses with high emission yields, a vacuum ultraviolet-excited intensely luminescent glass, high silica glass containing high concentration of Er³⁺ ion, ultrabroad infrared luminescent Bi-doped high silica glass and Nd³⁺-doped silica microchip laser glass were obtained by this method. The porous glass is also favorable for co-impregnating multi-active-ions. It can bring effective energy transferring between various active ions in the glass and increases luminescent intensity and extend range of excitation spectrum. The luminescent active ions-doped high-SiO₂ glasses are potential host materials for high power solid-state lasers and new transparent fluorescence materials.}

Crystal growth and properties of Yb : FAP laser crystal

A large and transparent Yb:FAP crystal with dimensions up to circle divide 30 mm x 85 mm has been grown by the Czochralski method. The preparation of the raw material has been investigated. X-ray power diffraction studies of Yb:FAP crystal confirm that the as-grown crystal is isostructural with the FAP crystal. The crystalline quality has been studied using X-ray rocking curve analysis. The segregation coefficient of Yb3+ in the Yb:FAP crystal has been also determined. Linear thermal expansion coefficients in [001] and [100] directions have been measured in the 30-800 degrees C temperature range. (c) 2005 Elsevier B.V. All rights reserved.

In situ synthesis of ZrO2/ZrW2O8 composites with near-zero thermal expansion

In this paper, ZrO2 and WO3 were used as the raw materials to prepare ZrO2/ZrW2O8 composites by in situ reaction method and the thermal expansion property of the composites was studied. This novel method included a heating step up to 1473 K for 24 h, which combines the synthesizing and sintering of ZrW2O8. The result indicates that ZrO2/ZrW2O8 composite shows near-zero thermal expansion when the weight ratio of ZrO2 and WO3 is 2.5:1. Compared with composites prepared previously by non-reactive sintering of ZrO2 and ZrW2O8, the composites show higher relative density and lower porosity.

Thermal and electric conductivity of near-zero thermal expansion ZrW 2O8//ZrO2 composites

In this work, the microstructure, thermal and electric conductivity properties of near-zero thermal expansion ZrW2O8/ZrO2 and Al2O3 added ZrW2O8/ZrO2 composites were studied. Both the two composites exhibit very low thermal conductivity and the thermal conductivity decreases slightly as the temperature increases. The electric conductivity of the two composites increases with the increasing of the measurement temperature. The Al2O3 added ZrW2O8/ZrO2 composite has higher thermal and electric conductivity than ZrW2O8/ZrO2 composite. The most important factor which causes the difference of the thermal and electric conductivity of the composites is the porosity. (C) 2008 The Ceramic Society of Japan. All rights reserved.