Synthesis of Titania in Ethanol/Acetic Acid Mixture Solvents: Phase and Morphology Variations

The phase and morphology variations of titania prepared in ethanol/acetic acid mixture solvents have been systematically investigated. X-ray diffraction results and microscopy observations reveal that pure anatase aggregates consisted of small nanoparticles, pure rutile microspheres comprised of nanofibers, and their mixtures could be obtained by varying ratios of ethanol to acetic acid under solvothermal conditions. The contents of anatase and rutile in the mixed phases also vary with the ratios of ethanol to acetic acid. Field emission scanning electron microscopy and high resolution transmission electron microscopy results show that the two phases are separated from each other in final products and form aggregates with morphologies resembling to their pure phase products obtained under favorable conditions. The as-produced rutile nanofibers, either in pure phase or in mixed phases, tend to grow into hollow microspheres.

Self-assembled 3D flowerlike Lu2O3 and Lu2O3 : Ln(3+) (Ln = Eu, Tb, Dy, Pr, Sm, Er, Ho, Tm) microarchitectures: Ethylene glycol-mediated hydrothermal synthesis and luminescent properties

Three-dimensional flowerlike Lu2O3 and Lu2O3:Ln(3+) (Ln = Eu, Th, Dy, Pr, Sm, Er, Ho, Tm) microarchitectures have been successfully synthesized via ethylene glycol (EG)-mediated hydrothermal method followed by a subsequent heat treatment process. X-ray diffraction, Fourier transform infrared spectroscopy, energy-dispersive X-ray spectra, thermogravimetric and differential thermal analysis, elemental analysis, inductively coupled plasma atomic absorption spectrometric analysis, ion chromatogram analysis, X-ray photoelectron spectra, scanning electron microscopy, transmission electron microscopy, photoluminescence spectra as well kinetic decays, and cathodoluminescence spectra were used to characterize the samples. Hydrothermal temperature, EG, and CH3COONa play critical roles in the formation of the lutetium oxide precursor microflowers. The reaction mechanism and the self-assembly evolution process have been proposed. The as-formed lutetium oxide precursor could transform to Lu2O3 With their original flowerlike morphology and slight shrinkage in the size after postannealing process.

Optical spectroscopy properties of KMgF3 : Eu2+ nanocrystals and powder synthesized by microemulsion and solvothermal process

Nanocrystals and powders of KMgF3 doped with Eu2+ were synthesized by the microemulsion method and the solvothermal process, respectively. The emission and excitation spectra of KMgF3:Eu2+ phosphors were measured and compared with those of the samples synthesized through a solid. state reaction, Bridgman-Stockbarger method, and mild hydrothermal technique. The KMgF3: Eu2+ samples synthesized by means of the microemulsion method and the solvothermal process show only a sharp emission peak located at 360 nm, in the emission spectra, which arises from the f -> f(P-6(1/2)-> S-8(1/2)) transition of Eu2+. The broad emission bands appear at 420 nm,,which arises from Eu2+ <- O2- cannot be observed(in the mild hydrothermal and single crystal samples, the emission peak at 420 nm besides the emission of Eu2+ at 360 nm is observed). In the excitation spectrum of the KMgF3: Eu2+ samples synthesized by the microemulsion method and the solvothermal process, the excitation peaks show an intensive blue shift. The blue shift can he attributed to the lower oxygenic content in the KMgF3: Eu2+ samples synthesized by the microemulsion method and the solvothermal process.

Synthesis and structure of a novel open-framework zincophosphate with intersecting three-dimensional helical channels

A new open-framework zincophosphate, Zn-0.5(H2PO4).0.5H(2)O (denoted as FJ-13), possessing intersecting three-dimensional helical channels, has been synthesized under solvothermal conditions.

Synthesis and catalytic properties of layered double hydroxides pillared by heteropolyoxometalate

Layered double hydroxides (LDHs) pillared with heteropolyoxometalate have been synthesized via both restructuring of hydrotalcite-like compounds and direct anion exchange under microwave field. LDHs and their derivatives are both found to be efficient for alkylation of isobutane with butene with a higher butene conversion and selectivity towards C-8(0).

Fast formation of NaA zeolite membrane in the microwave field

NaA zeolite membrane was successfully synthesized on the porous alpha-Al2O3 support by microwave heating. The synthesis of NaA zeolite membrane in the microwave field only needs 15 min and the synthesis time is 10 times shorter than that by conventional heating. SEM characterization indicates that the zeolite crystals in the NaA zeolite membrane synthesized by microwave heating are uniform in size; the membrane thickness is about 4 mu m and is thinner than that of the NaA zeolite membrane synthesized by conventional heating. Gas permeation studies indicate that the permeances of the NaA zeolite membrane synthesized by microwave heating are 3-4 times higher than those of the NaA zeolite membrane synthesized by conventional heating, while their permselectivities are comparable.