Layer-by-layer assembly of multilayer films composed of streptavidin and biotinylated antibody by real-time biomolecular interaction analysis

Layer-by-layer assembly of multilayer films of streptavidin and biotinylated antibody was completed on the streptavidin coated surface. Real-time biomolecular interaction analysis (BIA) based on surface plasmon resonance technique was used to monitor the multilayer assembly in solution continuously. The results indicate that the uniform multilayer film can be fabricated successfully based on the strong interaction between streptavidin and biotin. The mean surface mass concentration of each adsorption layer is 1. 32 ng/mm(2) for biotinylated antibody, 2. 93 ng/mm(2) for streptavidin, according to the correlation of SPR response with surface concentration.

Fabrication and electrochemical behaviors of multilayers composed of heteropholyanions and poly(diallyldimethylammonium chloride) on 4-aminothiophenol modified gold electrodes

Multilayer films composed of heteropolyanions (HPAS, SiMo11 VO405-) and cationic polymer poly(diallyldimethylammonium chloride) on 4-aminothiophenol self-assembled-monolayer were fabricated by electrochemical growth. Growth processes of the composite films were characterized by cyclic voltammetry. The results prove the third redox peak of Mo increases more rapidly, otherwise the other Mo redox peaks increase very slowly when the number of layers of heteropolyanions is greater. The peak potentials of composite films shift linearly to negative position with higher pH, which implies that protons are involved in the redox processes of HPA. The investigation of electrocatalytic behaviors of composite films shows a good catalytic activity for the reductions of HNO2 and BrO3-. Catalytic currents increase with increasing number of layers of heteropolyanions, moreover, the catalytic currents have a good linear relationship with the concentrations of BrO3-.

Synthesis and properties of novel random and block copolymers composed of phthalimidine- and perfluoroisopropylidene-polyarylether-sulfones

A series of novel polyarylethersulfone (AB)(n) block copolymers with different segment lengths have been synthesized by nucleophilic solution polycondensation of phenoxide-terminated and fluorine-terminated oligomers; random copolymers have been prepared over the whole composition ranges. The structures of the resultant copolymers have been confirmed by FTIR, C-13 NMR spectra and differential scanning calorimetry (DSC). Compared with two homopolymers and random copolymers, the block copolymers of this study possess excellent thermal stability (5% thermal decomposition under nitrogen atmosphere above 500 C) and high glass transition temperatures, and have a wide melt-processing temperature range. They may become a new class of mouldable high performance thermoplastics. (C) 2001 Society of Chemical Industry.

Preliminary investigations on polymerization catalysts composed of lanthanocene and methylaluminoxane

The polymerization of butadiene(Bd), isoprene(Ip) and styrene(St) has been examined using the six catalyst systems composed of lanthanocene, (C5H9Cp)(2)NdCl(I), (C5H9Cp)(2)SmCl(II), (MeCp)(2)SmOAr'(III), (Ind)(2)NdCl(IV), Me2Si(Ind)(2)NdCl(V) and (Flu)(2)NdCl(VI), and methylaluminoxane(MAO) respectively. All of them can be used to form the polyisoprene with molecular weights of 1 to 10 thousand and cis-1,4-unit contents of 41 to 47%. (I), (II) and (III) of them can be also used to form the polybutadiene with molecular weights of 10 to 20 thousand and cis-1,4-unit contents of 62 to 78%. In addition, the catalysts from (II) to (V) are still active for St polymerization and (II) of them gives a syndio -rich random polystyrene. It is noteworthy that (II) and (III) are active for homopolymerization of Bd, Ip and St in the same polymerization condition.

Irreversible capacity loss of graphite electrode in lithium-ion batteries

The irreversible capacity loss of the carbon electrode in lithium-ion batteries at the first cycle is caused mostly by surface film growth. We inspected an unknown irreversible capacity loss (UICL) of the natural graphite electrodes. The charge/discharge behavior of graphite and meso-phase carbon microbeads heat-treated at 2800 degrees C (MCMB28) as the materials of the carbon anode in the lithium-ion battery were compared. It was found that the capacity loss of the natural graphite electrode in the first cycle is caused not only by surface film growth, but also by irreversible lithium-ion intercalation on the new formed surface at the potential range of lithium intercalation, while the capacity loss of the MCMB28 electrode is mainly originated from surface film growth. The reason for the difference of their irreversible capacity losses of these two kinds of carbon material was explained in relation to their structural characteristics. (C) 1997 Published by Elsevier Science S.A.

Study on diffusion of electroactive species in polyelectrolyte polyethylene glycol lithium perchlorate by chronoamperometry at a microdisk electrode

The mass transport dynamics of Ferrocene in polyelectrolyte polyethylene glycol lithium perchlorate (PEG . LiClO4) was studied by using chronoamperometry at a microdisk electrode. Chronoamperometry is a powerful method for the study of mass transport in polyelectrolyte, it has many advantages over the conventional methods at a microelectrode and the steady-state method at an ultramicroelectrode. By using this method the apparent diffusion coefficient D-app and concentration C-a of the electroactive species, can be estimated from a single experiment without previous knowledge of either one. We have estimated D-app and C-a of ferrocene in PEG . LiClO4 polyelectrolyte from 25 degrees C to 75 degrees C. The dependence on the concentration of electroactive species was observed. The diffusion coefficients decrease with increasing ferrocene concentration and decreasing temperature. The mass transport mechanism is explained, by using a free volume model.

Electrochemical behaviour of spinel LiMn2O4 as positive electrode in rechargeable lithium cells

The spinel, lithium intercalation compound LiMn2O4 is prepared and studied using the techniques of a.c. impedance and cyclic voltammetry. The impedance behaviour of the LiMn2O4 electrode varies as lithium ions are intercalated or de-intercalated. The reversible behaviour of lithium ions in the LiMn2O4 electrode is confirmed by the results of cyclic voltammetry.

A study of cokes used as anodic materials in lithium ion rechargeable batteries

A variety of cokes pretreated at different temperatures are used as anodic materials and their electrochemical characteristics are examined by cyclic voltammetry. It is found that for some cokes such as petroleum coke (preheated at 1300 degrees C), pitch coke (1300 degrees C), needle coke (1900 degrees C), metallurgical coke (1900 degrees C), high capacity and cyclic efficiency are achieved. Needle coke (1900 degrees C) and metallurgical coke (1900 degrees C) in particular give a capacity of over 200 mAh/g and a cyclic efficiency of nearly 100%, whereas poor performance is exhibited by those pretreated at higher or lower temperatures, e.g., petroleum cokes (500 degrees C, 2800 degrees C), pitch coke (500 degrees C) and needle coke (2800 degrees C). The cyclic voltammograms show two electrochemical processes, one at about 0.1 V vs. Li+/Li which is electrochemically reversible, and may be attributed to the intercalation/deintercalation of lithium ions while the other, at about 0.6 V vs. Li+/Li, is electrochemically irreversible and may be assigned to the decomposition of the electrolyte solvent, which leads to formation of the passive film on the anode surface. The experimental results strongly suggest that the pretreatment temperature of cokes and of the solvent are determining factors for the growth, structure and properties of the passive film.

Lithium ion conducting polymer electrolytes based on alternating maleic anhydride copolymer with oligo-oxyethylene side chains

A comb polymer with oligo-oxyethylene side chains of the type -(CH2CB2O)(12)CH3 was prepared from methyl vinyl ether/maleic anhydride copolymer and poly (ethylene glycol) methyl ether. The polymer can dissolve LiClO4 salt to form homogeneous amorphous polymer electrolyte. The ac ion conduction was measured using the complex impedance method, and conductivities were investigated as functions of temperatures and salt concentration. The complexes were first found to have two classes of glass transition which increase with increasing salt content, The optimum conductivity attained at 25 degrees C is in the order of 5.50 x 10(-6)Scm(-1). IR spectroscopy was used to study the cation-polymer interaction.

Carbon materials for lithium ion batteries

The preliminary work indicated that passive film is the most important factor influencing cell performance of carbon anode, and the carbon and solvent used govern cell performance by forming the passive film of different properties. A in situ XRD result is also presented.

The conductivity behavior of a polymer gel electrolyte

A new kind of polymer gel electrolyte which is composed of polytriethylene glycol dimethacrylate(PTREGD), propylene carbonate(PC) and LiPF6 has been prepared by thermal polymerization. The conductivity was measured as a function of temperature, and it was found that the Arrhenius equation was held very well through out the salt concentration studied. Maximum room temperature conductivity of 4.95 x 10(-4) S/cm, as well as a minimum activation energy value of 18.90 kJ/mol were obtained at the same salt concentration of 0.22 mol/L.

TRIS(TERT-BUTYLCYCLOPENTADIENYL)NEODYMIUM-MU-CHLORO-TRIS(TETRAHYDROFURAN)LITHIUM, [ND(ETA(5)-(T)BUCP)3(MU-CL)LI(THF)3]

The title complex, tris[2(eta5)-tert-butylcyclopentadi-enyl]-mu-chloro-1:2kappa2Cl-tris(tetrahydrofuran-1kappaO)lithiumneodymium, [Nd(C9H13)3(mu-Cl)Li(C4H8O)3], consists of the neutral moiety ((t)BuCp)3Nd linked to the cation [Li(thf)3]+ by a mu-Cl bridge

Role of Lithium in Multicomponent Oxide Catalysts for Oxidative Coupling of Methane

The effect of Li content in a series of multicomponent oxides LixLa0.5Ti0.5 For methane oxidative coupling has been studied. The catalytic activities of LiLa0.5Ti0.5 catalyst before and after washing with boiling water have been compared. The surface and

IMPEDANCE STUDY OF THE INTERFACES BETWEEN LITHIUM, POLYANILINE, LITHIUM-DOPED MNO2 AND MODIFIED POLY(ETHYLENE OXIDE) ELECTROLYTE

Impedance study was carried out for the interfaces between lithium, polyaniline (PAn), lithium-doped MnO2 and modified poly(ethylene oxide) (PEO) electrolyte under various' conditions. The interfacial charge-transfer resistances R(ct) on PEO/PAn, R(ct) on PEO/LiMn2O4 increase with depth-of-discharge and decrease after the charge of the cell containing modified PEO as electrolyte. The charge-transfer resistance R(ct) on PEO/PAn is higher than R(ct) on PEO/LiMn2O4 under the same condition, since inserted species and mechanism are different for both cases. In the case of PAn, an additional charge-transfer resistance might be related to the electronic conductivity change in discharge/charge potential range, as it was evident from a voltammetry curve. With increasing cycle numbers, the charge-transfer resistance increases gradually. The impedance results also have shown that at low frequency the diffusion control is dominant in the process of the charge and discharge of Li/PEO/PAn or Li/PEO/LiMn2O4 cell. The diffusion coefficients have been calculated from impedance data.

STUDIES OF SPINEL LICRXMN2-XO4 FOR SECONDARY LITHIUM BATTERY

X-ray and electrochemical studies of spinel-related manganese chromium oxides, LiCrxMn2-xO4 (0 less-than-or-equal-to x less-than-or-equal-to 1) were carried out in a lithium nonaqueous cell. X-ray diffraction spectra indicated that the substitution of manganese in LiMn2O4 by trivalent transition metals (Cr3+) cause the linear decrease of lattice parameter with the x in the LiCrMn2-xO4. Some discharge-capacity loss was obtained due to the lattice contraction of LiCrMn2-xO4, but it has a better rechargeability than LiMn2O4. Cyclic voltammetry and electrochemical impedance experiments have shown that the excellent rechargeability of LiCrxMn2-xO4 may be attributed to the good reversibility of the change in its crystal structure for the insertion and extraction of lithium ions.