Effects of gamma irradiation and air annealing on Yb-doped YAlO3 single crystals

The effects of gamma irradiation on as-grown 5 at% Yb:YAlO3 (YAP) and air annealing on gamma-irradiated 5 at% Yb: YAP have been studied by the difference in the absorption spectra before and after treatment. The gamma irradiation and air annealing led to opposite changes of the absorption properties of the Yb: YAP crystal. After air annealing, the gamma-irradiation effects were totally removed over the wavelength range 390-800 nm and the concentrations of Fe3+ and Yb3+ were slightly increased. For the first time, the gamma-irradiation-induced valence changes between Yb3+ and Yb2+ ions in Yb: YAP crystals have been observed. (c) 2005 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Raman spectroscopic investigation of pure and ytterbium-doped rare earth silicate crystals

Raman spectroscopy was used to study the molecular structure of a series of selected rare earth (RE) silicate crystals including Y2SiO5 (YSO), LU2SiO5 (LSO), (Lu0.5Y0.5)(2)SiO5 (LYSO) and their ytterbium-doped samples. Raman spectra show resolved bands below 500 cm(-1) region assigned to the modes of SiO4 and oxygen vibrations. Multiple bands indicate the nonequivalence of the RE-O bonds and the lifting of the degeneracy of the RE ion vibration. Low intensity bands below 500 cm(-1) are an indication of impurities. The (SiO4)(4-) tetrahedra are characterized by bands near 200 cm(-1) which show a separation of the components of nu(4) and nu(2), in the 500-700 cm(-1) region which are attributed to the distorting bending vibration and in the 880-1000 cm(-1) region which are attributed to the symmetric and antisymmetric stretching vibrational modes. The majority of the bands in the 300-610 cm(-1) region of Re2SiO5 were found to arise from vibrations involving both Si and RE ions, indicating that there is considerable mixing of Si displacements with Si-O bending modes and RE-0 stretching modes. The Raman spectra of RE silicate crystals were analyzed in terms of the molecular structure of the crystals, which enabled separation of the bands attributed to distinct vibrational units. Copyright (C) 2007 John Wiley & Sons, Ltd.

Preparation and characterization of DBSA doped polyaniline thin films

Stable monolayer of the polyaniline(PAn) doped with dodecyl benzenesulfonic acid(DBSA) can form on the pure water surface. The multilayer ultrathin film can be successfully deposited by Langmuir-Blodgett(LB) technique onto CaF2 substrate. The limiting mean molecular area and collapse pressure observed are 0.066 nm(2) and 35 mN m(-1), respectively. The multilayer LB film and casting film were all characterized by TR and UV-Vis-NIR spectroscopies.

Electrochromic effect in domain-inversion process LiNbO3 : Ru : Fe crystals

A reversible electrochromic effect accompanying domain-inversion during the electrical poling process in LiNbO3: Ru: Fe crystals at room temperature has been observed. In electrode area, both electrochromism and domain-inversion occur alternately, and electrochromism is also reversible during back-switch poling, which is experimentally verified and whose mechanism is briefly explained using a microstructure ferroelectric model. In addition, because of the enhancing elcctrochromic effect, different from the undoped LiNbO3 crystals, the coercive riled (21.0 kV/mm or so) measured in LiNbO3: Ru: Fe is lower than its breakdown field, thus providing a possible new technique for realizing the domain-inversion by constant electric field rather than a pulsed one.

Absorption characteristic and nonvolatile holographic recording in LiNbO3 : Cr : Cu crystals

The absorption characteristic of lithium niobate crystals doped with chromium and copper (Cr and Cu) is investigated. We find that there are two apparent absorption bands for LiNbO3:Cr:Cu crystal doped with 0.14 wt.% Cr2O3 and 0.011 wt.% CuO; one is around 480 nm, and the other is around 660 nm. With a decrease in the doping composition of Cr and an increase in the doping composition of Cu, no apparent absorption band in the shorter wavelength range exists. The higher the doping level of Cr, the larger the absorbance around 660 nm. Although a 633 nm red light is located in the absorption band around 660 nm, the absorption at 633 nm does not help the photorefractive process; i.e., unlike other doubly doped crystals, for example, LiNbO3:Fe:Mn crystal, a nonvolatile holographic recording can be realized by a 633 nm red light as the recording light and a 390 nm UV light as the sensitizing light. For LiNbO3:Cr:Cu crystals, by changing the recording light from a 633 nm red light to a 514 nm green light, sensitizing with a 390 nm UV light and a 488 nm blue light, respectively, a nonvolatile holographic recording can be realized. Doping the appropriate Cr (for example, N-Cr = 2.795 X 10(25)m(-3) and N-Cr/N-Cu = 1) benefits the improvement of holographic recording properties. (c) 2005 Optical Society of America.

Wavelength dependence of light-induced domain nucleation in MgO-doped congruent LiNbO3 crystal

Within the wavelength range from 351 to 799 nm, the different reductions of nucleation field induced by the focused continuous laser irradiation are achieved in the 5 mol % MgO-doped congruent LiNbO3 crystals. The reduction proportion increases exponentially with decreasing irradiation wavelength and decreases exponentially with increasing irradiation wavelength. At one given wavelength, the reduction proportion increases exponentially with increasing irradiation intensity. An assumption is proposed that the reduction of nucleation field is directly related to the defect structure of crystal lattice generated by the complex coaction of incident irradiation field and external electric field. (c) 2007 American Institute of Physics.

Broadband near-infrared emission from transparent Ni2+-doped silicate glass ceramics

Transparent Ni2+-doped MgO-Al2O3-TiO2-SiO2 glass ceramics were prepared, and the optical properties of Ni2+-doped glass ceramics were investigated. Broadband emission centered at 1320 nm was observed by 980 nm excitation. The longer wavelength luminescence compared with Ni2+-doped Li2O-Ga2O3-SiO2 glass ceramics is ascribed to the low crystal field hold by Ni2+ in MgO-Al2O3-TiO2-SiO2 glass ceramics. The change in optical signals at the telecommunication bands with or without 980 nm excitation was also measured when the seed beam passes through the bulk gain host.(C) 2007 American Institute of Physics.

Devitrification of TeO2-doped fluoroaluminate glass

Crystallization behavior of the glass system AlF3-MgF2-CaF2-SrF2-BaF2-YF3-TeO2 (AMCSBY-TeO2) Was studied by the nonisothermal method using differential thermal analysis. The activation energy E and Avrami exponent n were determined by nonisothermal method. It is found that the value of E varies with increasing TeO2 and reaches a minimum at 10 mol fraction TeO2, while n decreases from 3.65 to 1.78 with the addition of TeO2. X-ray diffraction shows that Ba2Te3O8, MgTe2O5, and SrTeO3 phase formed when the glasses were reheated. The addition of TeO2 changes the crystallization mechanism and improves the stability of the fluoroaluminate glass.

Upconversion luminescence in Yb3+-doped yttrium aluminum garnets

In this paper, we present results on upconversion luminescence performed on Yb3+-doped yttrium aluminum garnets under 940 nm excitation. The upconversion luminescence was ascribed to Yb3+ cooperative luminescence and the presence of rare earth impurity ions. The cooperative luminescence spectra as a function of Yb concentration were measured and the emission intensity variation with Yb concentration was discussed. Yb3+ energy migration quenched the cooperative luminescence of Yb:YAG crystals with doping level over 15 at%. (c) 2004 Elsevier B.V. All rights reserved.

Codoping Na+ to modulate the spectroscopy and photoluminescence properties of Yb3+ in CaF2 laser crystal

kinds of Yb3+- and Na+-codoped CaF2 laser crystal with different Na:Yb ratios of 0, 1.5, and 10 are grown by the temperature gradient technique. Room-temperature absorption, photoluminescence spectra, and fluorescence lifetimes belonging to the transitions between ground state F-2(7/2) and excited state F-2(5/2) of Yb3+ ions in the three crystals are measured to study the effect of Na+. Experimental results show that codoping Na+ ions in different Na:Yb ratios can modulate the spectroscopy and photoluminescence properties of Yb3+ ions in a CaF2 lattice in a large scope. (c) 2005 Optical Society of America