Compatibilizing effect of polystyrene-block-poly(4-vinylpyridine) for poly(2,6-dimethyl-1,4-phenyleneoxide) chlorinated polyethylene blends

The compatibilizing effect and mechanism of compatibilization of the diblock copolymer polystyrene-block-poly(4-vinylpyridine) P(S-b-4VPy) on immiscible blends of poly(2,6-dimethyl-1,4-phenylene oxide) (PPO)/chlorinated polyethylene (CPE) were studied by means of scanning electron microscopy (SEM), differential scanning calorimetry (DSC), mechanical properties and FTIR measurements. The block copolymer was synthesized by sequential anionic polymerization and melt-blended with PPO and CPE. The results show that the P(S-b-4VPy) added acts as an effective compatibilizer, located at the interface between the PPO and the CPE phase, reducing the interfacial tension, and improving the interfacial adhesion. The tensile strength and modulus of all blends increase with P(S-b-4VPy) content, whereas the elongation at break increases for PPO-rich blends, but decreases for CPE-rich blends. The polystyrene block of the diblock copolymer is compatible with PPO, and the poly(4-vinylpyridine) block and CPE are partially miscible.

Structure and Conformation of 2,3,6, 7,10,11-hexakispentyloxytriphenylene by TEM and Computer Simulation

Experimental electron diffraction patterns and high resolution images were used to determine the space group and unit cell dimensions of 2,3,6,7,10,11-hexakispentyloxytriphenylene. Subsequently the molecular conformation was calculated by energy minimized package in Cerius2. Using this method, we got the HPT crystal structure: space group: P6/mmm; lattice type: hexogonal; the lattice parameters are a = b = 20.3 angstrom, c = 3.52 angstrom, = = 90 degrees, = 120 degrees. The core of HPT is not perpendicular to the column. The angle between a axis and HPT core plane is 9 degrees which cannot be seen in b-c projection. The simulated ED patterns and HREM images are good agreement with the experimental ED patterns and HREM images.

In-situ microscopic FTIR spectroelectrochemical study of the reduction of K3Fe(CN)(6) in polymer electrolyte

Cyclic voltammetry and in-situ microscopic FTIR spectroelectrochemistry were used for the electrochemical and vibrational characterizations of the reduction process of K3Fe (CN)(6) in polyethylene glycol(PEG) with LiClO4 as supporting electrolyte at a Pt microelectrode. The rate of electron transfer is a function of the concentration of the supporting electrolyte. The redox potentials and cyclic voltammetric currents vary with Li/O molar ratio. The bl-situ spectroelectrochemistry shows that the infrared spectra are influenced by the concentration of LiClO4. The bridging cyanide groups with a structure Fe-I-C drop N ... Fe-I-C drop N are formed during the reduction process of K3Fe (CN)(6). There may be an activated complex between the Lif cation and the complex anion.

Synthesis, properties and crystal structure of organic-inorganic radical salt (DBTTF)(6)HPMo12O40 center dot 2H(2)O

Organic-inorganic radical salt (DBTTF)(6)PMo12O40 . 2H(2)O was synthesized by electrocrystallization and characterized by IR spectrum, electronic spectrum and ESR technology, Its magnetic property, conductivity and crystal structure were determined. The title compound crystallized in a triclinic system with P1 space group, a = 1.378 7(7), b = 1.420 4 (2), c = 1.570 2(2) nm, alpha = 104.57(1)degrees, beta = 103.41(2)degrees, gamma = 95.80(2)degrees, V = 2.853(2) nm(3) Z = 1 and a final R = 0.072 7.

Synthesis and characterization of the side chain liquid crystalline poly(monoester {6-[4-(p-nitrophenyl)azo]phenoxy-1-hexyloxy} of maleic anhydride)

The poly(monoester (6-[4-(p-nitrophenyl) azo]phenoxy-1-hexyloxy) of maleic anhydride) shows a smectic phase with a focal conic fan texture. With the decrease of the monoestering degree the phase transition temperature decreases and the mesomorphic temperature range becomes narrow. The hydrogen bonding between two carboxylic acid groups was found to play a very important role in forming the smectic phase structure. The smectic bilayer structure has been built through self-assembly via. intermolecular hydrogen bonding.

(+/-)-7,7,9,9-Tetramethyl-2,3 : 4,5-dinaphthol,6,8-trioxa-7,9-disilacyclonona-2,4-diene

The title compound, C24H24O3Si2, is a twofold symmetric silicocrown ether with the two dimethylsilyl groups attached to the O atoms of 1,1'-bi-2-naphthol, and bridged by another O atom.

Studies on biodegradable poly(hexano-6-lactone) fibers 1. Structure and properties of drawn poly(hexano-6-lactone) fibers

Using high molecular weight (M-n=80,000) Poly(hexano-6-lactone) (PCL'), tough and high tenacity PCL monofilaments with various draw ratios (undrawn to 9 times drawn) were prepared by melt-spinning. The relationship between microstructure and properties of the PCL fibers is described in this current IUPAC Technical Report. Analysis of microstructure of the drawn PCL fibers by wide-angle X-ray diffraction revealed typical c-axis orientation with an increase in crystallinity. It was also supported by sonic velocity measurements. The thermal, mechanical, and dynamic mechanical properties of the PCL fibers were affected significantly by draw ratio. DSC thermograms showed that the melting temperature and the enthalpy of fusion increased with draw ratio. The temperature dependence curves of dynamic viscoelasticity showed that the temperature at tan delta peak of alpha dispersion corresponding to the glass transition temperature shifted toward higher temperature and the peak value of tan delta decreased with draw ratio. The dynamic storage modulus and the sonic modulus increased with draw ratio. These results are due to the increase in crystallinity and molecular orientation with drawing, and are responsible for an increase in tensile tenacity as well as knot tenacity of the PCL fibers.