Study on the structure change and oxygen vacation shift for Ce1-xSmxO2-y solid solution

A series of solid electrolytes Ce1-xSmxO2-y (x=0similar to0.6) were prepared by sol-gel method. XRD measurement showed that single-phase solid solution was formed in all investigated ranges at 160 degreesC, which is a significantly lower synthesis temperature compared to traditional solid state reaction. High temperature X-ray, ESR, and Raman scattering were used to characterize the samples. ESR measurement showed that ESR with sample irradiated by high-energy particle is an effective way to study the defect structure. These changes in the Raman spectrum are attributed to O vacancies, which are introduced into the lattice when tetravalent Ce4+ is substituted by trivalent Sm3+.

Conductive hybrids from water-borne conductive polyaniline and (3-glycidoxypropyl)trimethoxysilane

Free-standing conductive films of organic-inorganic hybrids were prepared employing the sol-gel process of (3-glycidoxypropyl)trimethoxysilane (GPTMS) and water-borne conductive polyaniline (cPANI) in water/ethanol solution. The hybrids displayed a percolation threshold for electrical conductivity at a volume fraction of 2.1% polyaniline (PANI); the maximum conductivity of the hybrids reached 0.6 S/cm. GPTMS showed good compatibility with water-borne cPANI during the sol-gel process, and freestanding conductive films were obtained at room temperature. Transmission electron microscopy images of the hybrids indicated that the cPANI was dispersed in the inorganic phase in nanoscale. Because of good confinement of cPANI chains in the inorganic network, water resistance of the hybrid films was significantly improved compared with that of pure cPANI; the electrical conductivity of the films kept stable for 6-7 days soaking in water, whereas it decreased sharply for 1 day soaking for the pure cPANI.

Luminescent hybrid films obtained by covalent grafting of terbium complex to silica network

Luminescent hybrid thin films consisting of terbium complex covalently bonded to a silica-based network have been obtained in situ via a sol-gel approach. A new monomer, N-(4-benzoic acid-yl), N'-(propylthiethoxysilyl)urea (PABI), has been synthesized by grafting isocyanatopropyltriethoxysilane (ICPTES) to p-aminobenzoic acid and characterized by H-1 NMR IR and MS, The monomer acts as a ligand for Tb3+ ion and as a sol-gel precursor. Band emission front Tb3+ ion due to an efficient ligand-to-metal energy transfer was observed by UV excitation. The decay curves of Tb3+ in the hybrid films were measured. The energy difference between the triplet state energy of PABI and the D-5(4) level of Tb3+ ion falls in the exciting range to sensitize Tb3+ ion fluorescence.

A novel flow through optical fiber biosensor for glucose based on luminol electrochemiluminescence

A novel flow injection optical fiber biosensor for glucose based on luminol electrochemiluminescence (ECL) is presented. The sol-gel method is introduced to immobilize glucose oxidase (GOD) on the surface of a glassy carbon electrode. After optimization of the working conditions, glucose could be quantitated in the concentration ranges between 50 muM and 10 mM with a detection limit of around 26 muM. Signal reproducibility was about 3.62% relative standard deviation for 11 replicated measurements of 0.1 mM glucose. The ECL biosensor also showed good selectivity and operational stability. The proposed method can be applied to determination of glucose in soft drink samples.

Luminescence properties of lanthanide complexes doped in hybrid material from tetraethoxysilane and 3-glycidyioxyropyl-trimethoxysilane

Hybrid materials, containing in-situ synthesized lanthanide complexes with intense green light, have been prepared via sol-gel process. The luminescence properties and the decay times of as-synthesized samples were investigated. The excitation spectrum of the samples indicates the formation of complexes between terbium (III) and P-Sulfosalicylic acid. The hybrid materials that contain in-situ synthesized terbium complexes exhibit the characteristic emission bands of the rare earth ions. In addition, the effect of concentration of terbium on the luminescence properties as well as the thermal stability were also studied.

Synthesis-dependent luminescence properties of Y3Al5O12 : Re3+ (Re=Ce, Sm, Tb) phosphors

By using metal nitrates and oxides as the starting materials, Y2Al5O12 (YAG) and YAG:Re3+ (Re = Ce, Sm, Th) powder phosphors were prepared by solid-state (SS), coprecipitation (CP) and citrate gel (CG) methods. The resulting YAG and YAG-based phosphors were characterized by XRD, FT-IR, SEM and photoluminescent excitation and emission spectra. The purified crystalline phases of YAG were obtained at 800 degreesC (CG) and 900 degreesC (CP, SS). At an identical annealing temperature and doping concentration, the doped rare-earth ions showed the stronger emission intensity in the CP- and SS-derived phosphors than the CG-derived YAG phosphors. The poor emission intensity for the CG-derived phosphors is mainly caused by the contamination of carbon impurities from citric acid in the starting materials.

Hybrid luminescent films obtained by covalent anchoring terbium complex to silica-based network

New monomer N-(4-carboxyphenyl)-NL-(propyltriethoxysilyl)urea (1) which acts as both a ligand for Th3+ ion and a sol-gel precursor has been synthesized and characterized by H-1 NMR, and MS. Hybrid luminescent thin films consisting of organoterbium covalently bonded to a silica-based network have been obtained in situ via a sol-gel approach. Strong line emission of Tb3+ ion was observed from the hybrid luminescent films under UV excitation.

Luminescence properties of transparent hybrid thin film covalently linked with lanthanide complexes

Novel hybrid thin films covalently doped with Eu3+ (Tb3+) have been prepared via direct routes involving co-condensation of tetraethoxysilane and phen-Si in the presence of Eu3+ (Tb3+) by spin-casting and their luminescence properties have been investigated in detail. Lanthanide ions can be sensitized by anchored phenanthroline in hybrid thin films. Excitation at the ligand absorption wavelength (272 nm) resulted in the strong emission of the lanthanide ions i.e. Eu3+ D-5(0)-F-7(J) (J=0, 1, 2, 3, 4) emission lines and Tb3+ D-5(4)-F-7(J) (J = 6, 5, 4, 3) due to the energy transfer from the ligands to the lanthanide ions.

Preparation and luminescence properties of hybrid materials containing europium(III) complexes covalently bonded to a silica matrix

A new kind of luminescent organic-inorganic hybrid material (denoted Hybrid I) consisting of europium 1,10-phenanthroline complexes covalently attached to a silica-based network was prepared by a sol-gel process. 1,10-Phenanthroline grafted to 3-(triethoxysilyl)propyl isocyanate was used as one of the precursors for the preparation of an organic-inorganic hybrid materials. For comparison purposes, the hybrid material (denoted Hybrid II) in which phenanthroline was not grafted onto the silica backbone of the frameworks was also prepared. Elemental analysis; NMR, FT-IR, UV/vis absorption, and luminescence spectroscopies, and luminescence decay analysis were used to characterize the obtained hybrid materials. It is shown that the homogeneity of Hybrid I is superior to that of Hybrid II, and a higher concentration europium can be incorporated into Hybrid I than Hybrid II. Excitation at the ligand absorption wavelength (283 nm) resulted in the strong emission of the Eu3+ D-5(0)-F-7(J) (J = 0-4) transition lines as a result of the efficient energy transfer from the ligands to the EU3+ in Hybrid I. The number of water molecules coordinated to the europium ion was estimated, and the structure of the as-synthesized Hybrid I was predicted on the basis of the experimental results.

Electrocatalytic performance of Pt-TiO2/C complex catalysts for oxidation of methanol

It is reported for the first time that the Pt-TiO2/C catalyst prepared with chemical reduction and sol-gel method showed the excellent electrocatalytic activity and stability for the electrooxidation of methanol. When the atom ratio of Ti to Pt in the catalysts is 1/2, the catalysts showed the best electrocatalytic properties. After the catalyst is treated at 500 degreesC, the performance is further improved. It is hopeful to use the catalyst in the pratical DMFC.

Photoluminescence of organic-inorganic hybrid SiO2 xerogels

Organic-inorganic hybrid SiO2 xerogels were prepared by the sol-gel method under various preparation conditions and compositions by using tetraethoxysilane (TEOS), (3-aminopropyl) triethoxysilane (A-PS), (3-glycidoxypropyl) trimethoxysilane (GPS), organic acid (CH3COOH) and inorganic acids (HCl, HNO3, H2SO4) as the main precursors. Luminescence and FT-IR spectra were used to characterize the resulted hybrid SiO2 xerogels. The result of FT-IR spectrum shows that the xerogels are composed of non-crystalline -Si-O-Si- networks containing some organic groups such as -NH, -CH and -OH. Under the excitation of 365 nm, all the hybrid xerogels exhibit strong luminescence in the blue region, but the emission intensity and position depend on the starting precursor compositions to a large extent. Suitable amount of polyethylene glycol (PEG500 and PEG10000) in the hybrid xerogels can enhance the emission intensity. Additionally, the emission intensity of the hybrid xerogels increases with heat treatment temperature in the range of ambient to 200degreesC, and vacuum condition is also able to enhance the emission intensity.

A transparent thin film with hexagonal mesostructure containing rhodamine 6G

A transparent thin film was prepared by depositing the sol-get mixture for the synthesis of MCM-41 mesoporous molecular sieve doped with rhodamine 6G (R6G) dye on glass substrates. The film of silica-surfactant-R6G materials, which was identified to possess hexagonally ordered mesostructure, was composed of nanocrystallites about 35 nm in diameter and 1-10 mum in thickness. Cleanness of the substrates, concentration of the sol-gel mixture and rate of evaporation of the solvent were the key factors affecting transparency and homogeneity of the film. Moreover, optical change and lack in dye aggregation were observed to the R6G-functionalized MCM-41 thin film in contrast with that in ethanol solution.

Cupric hexacyanoferrate nanoparticle modified carbon ceramic composite electrodes

Graphite powder-supported cupric hexacyanoferrate (CuHCF) nanoparticles were dispersed into methyltrimethoxysilane based gels to produce a conducting carbon ceramic Composite, which was used as electrode material to fabricate surface- renewable CuHCF-modified electrodes. Electrochemical behavior of the CuHCF-modifled carbon ceramic composite electrodes was characterized using cyclic and square-wave voltammetry. Cyclic voltammograms at various scan rates indicated that peak currents were surface-confined at low scan rates. In the presence of glutathione, a clear electrocatalytic response was observed at the CuHCF-modified composite electrodes. In addition, the electrodes exhibited a distinct advantage of reproducible surface-renewal by simple mechanical polishing on emery paper, as well as ease of preparation, and good chemical and mechanical stability in a flowing stream.

Carbon ceramic electrodes modified with sub-micron particles of new methylene blue (NMB) intercalated alpha-zirconium phosphate

New methylene blue-intercalated a-zirconium phosphate (NMBZrP) was synthesized in the presence of n-butylamine and characterized by powder XRD, FTIR, TEM and elemental analysis. Sub-micron particles of NMBZrP in deionized water were apt to deposit onto the surface of graphite powder to yield graphite powder-supported NMBZrP, which was subsequently dispersed into methyltrimethoxysilane-derived gels to fabricate surface-renewable, stable, rigid carbon ceramic electrodes containing new methylene blue. Cyclic voltammetric studies revealed that peak currents of the NMBZrP-modified electrode were surface-confined at low scan rates but diffusion-controlled. at high scan rates. In addition, NMBZrP immobilized in a carbon ceramic matrix presented a two-electron, three-proton redox process in acidic aqueous solution in the pH range from 0.52 to 3.95.

Photoluminescent organic-inorganic composite films layer-by-layer self-assembled from the rare-earth-containing polyoxometalate Na-9[EuW10O36] and poly(allylamine hydrochloride)

Photoluminescent organic-inorganic composite films incorporating the rare-earth-containing polyoxometalate Na-9[EuW10O36] (EW) and poly(allylamine hydrochloride) (PAH) have been prepared by the layer-by-layer self-assembly method. UV-vis spectroscopy and ellipsometry were used to follow the fabrication process of the EW/PAH composite films. The experimental results show that the deposition process is linear and highly reproducible from layer to layer. An average EW/PAH bilayer thickness of ca. 2.1 nm was determined by ellipsometry. In addition, scanning electron microscopy and atomic force microscopy images of the EW/PAH composite films indicate that the film surface is relatively uniform and smooth. The photoluminescent properties of these films were investigated by fluorescence spectroscopy.