Preparation of A-type zeolite membranes on nonporous metal supports by using electrophoretic technique

A-type zeolite membranes were prepared on the nonporous metal supports by using electrophoretic technique. The as-synthesized membranes were characterized by XRD and SEM. The effect of the applied potential on the formation of the A-type zeolite membrane was investigated, and the formation mechanism of zeolite membrane in the electric field was discussed. The results showed that the negative charged zeolite particles could migrate to the anode metal surface homogenously and rapidly under the action of the applied electric field, consequently formed uniform and dense membranes in short time. The applied potential had great effect on the membrane formation, and more uniform and denser zeolite membranes were prepared on the nonporous metal supports with 1 V potential.

Controllable synthesis of VSB-5 micirospheres and microrods: Growth mechanism and selective hydrogenation catalysis

Nanoporous VSB-5 nickel phosphate molecular sieves with relatively well controllable sizes and morphology of microspheres assembled from nanorods were synthesized at 140 degrees C over a short time in the presence of hexamethylenetetramine (HMT) by a facile hydrothermal method. The pH value, reaction time, and ratio of HMT to NaHPO2-H2O crucially influence the morphology and quality of the final products.

Synthesis and structure of a novel open-framework zincophosphate with intersecting three-dimensional helical channels

A new open-framework zincophosphate, Zn-0.5(H2PO4).0.5H(2)O (denoted as FJ-13), possessing intersecting three-dimensional helical channels, has been synthesized under solvothermal conditions.

Oriented growth of MCM-22 zeolite films

MCM-22 zeolite films have been grown with layers vertical to the substrate under hydrothermal synthesis conditions, and characterized by X-ray diffraction and scanning electron microscopy.

Fast formation of NaA zeolite membrane in the microwave field

NaA zeolite membrane was successfully synthesized on the porous alpha-Al2O3 support by microwave heating. The synthesis of NaA zeolite membrane in the microwave field only needs 15 min and the synthesis time is 10 times shorter than that by conventional heating. SEM characterization indicates that the zeolite crystals in the NaA zeolite membrane synthesized by microwave heating are uniform in size; the membrane thickness is about 4 mu m and is thinner than that of the NaA zeolite membrane synthesized by conventional heating. Gas permeation studies indicate that the permeances of the NaA zeolite membrane synthesized by microwave heating are 3-4 times higher than those of the NaA zeolite membrane synthesized by conventional heating, while their permselectivities are comparable.

Synthesis and catalytic reactivity of MCM-22/ZSM-35 composites for olefin aromatization

A series of MCM-22/ZSM-35 composites has been hydrothermally synthesized and characterized by XRD, SEM, particle size distribution analysis, N-2 adsorption and NH3-TPD techniques. Pulse and continuous flow reactions were carried out to evaluate the catalytic performances of these composites in aromatization of olefins, respectively. It was found that MCM-22/ZSM-35 composites could be rapidly crystallized at 174 degrees C with an optimal gel composition of SiO2/Al2O3=25, Na2O/SiO2=0.11, HMI/SiO2=0.35, and H2O/SiO2=45 (molar ratio), of which the weight ratio of ZSM-35 zeolite in the composite relied on the crystallization time. The coexistence of MCM-22 and ZSM-35 in the composite (MCM-22/ZSM-35=45/55 wt/wt) was observed to exert a notable synergistic effect on the aromatization ability for butene conversion and FCC gasoline updating, possibly due to the intergrowth of some MCM-22 and ZSM-35 layers.