Reduction property and catalytic activity of Ce1-XNiXO2 mixed oxide catalysts for CH4 oxidation

Ce1-XNiXO2 oxides with X varying from 0.05 to 0.5 were prepared by different methods and characterized by XRD and TPR techniques. Ce(0.7)Mi(0.3)O(2) sample prepared by sol-gel method shows the highest reducibility and the highest catalytic activity for methane combustion. Three kinds of Ni phases co-exist in the Ce1-XNiXO2 catalysts prepared by sol-gel method: (i) aggregated NiO on the support CeO2, (ii) highly dispersed NiO with strong interaction with CeO2 and (iii) Ni atoms incorporated into CeO2 lattice. The distribution of different Ni species strongly depends on the preparation methods. The highly dispersed NiO shows the highest activity for methane combustion. The NiO aggregated on the support CeO2 shows lower catalytic activity for methane combustion, while the least catalytic activity is found for the Ni species incorporated into CeO2. Any oxygen vacancy formed in CeO2 lattice due to the incorporating of Ni atoms adsorbs and activates the molecular oxygen to form active oxygen species. So the highest catalytic activity for methane combustion on Ce0.7Ni0.3O2 catalyst is attributed not only to the highly dispersed Ni species but also to the more active oxygen species formed. (C) 2002 Elsevier Science B.V. All rights reserved.

Preparation of highly dispersed gold microparticles and their electrocatalytic activity for the oxidation of formaldehyde

The electrochemical preparation of highly dispersed Au microparticles on the surfaces of glassy carbon (GC) electrodes and their electrocatalytic activities for the oxidation of formaldehyde were studied. It was found that the reduction of Au3+ to Au is controlled by diffusion and the formation mechanism of Au microparticles on the GC surfaces corresponds to an instantaneous nucleation and diffusion-controlled three dimensional growth process. The particle size is about 80-90 nm in diameter after the electrochemical ageing treatment. These highly dispersed Au microparticles have high surface areas and exhibit better electrocatalytic activity than that of bulk-form Au toward the electrochemical oxidation of formaldehyde in alkaline media.

Relationship between the structure and catalytic activity of La2-xSrxNiO4-lambda(0<=x<=1) mixed oxides for NH3 oxidation

A series of samples having the composition of La2-xSrxNiO4(0 less than or equal to x less than or equal to 1) were prepared and used as catalysts for NH3 oxidation. It was found that the La and oxygen vacancies exist in the La2-xSrxNiO4-lambda(0 less than or equal to x less than or equal to 1). The unit cell volume decreases with the increase of x. For bath c and a parameters there appeared a turning point at x = 0.5. Doping with a lower valence cation Sr2+ in the case of La2NiO4 resulted in an increase of Ni3+, consequently the formation of oxygen vacancies, the increase of reducing ability and the increase of catalytic activity. In the oxygen TPD of La2-xSrxNiO4(0 less than or equal to x less than or equal to 1) appeared three peaks, the alpha' peak at about 400K was attributed to the surplus oxygen desorption, the a peak at 700K which approaches to a maxium at x = 0.6 was attributed to the oxygen adsorbed at oxygen vacancies. The beta peak at about 1000K which depends closely on the x and favors the catalytic activity was attributed to the reduction of Ni3+. The catalytic activity of La-2-x SrxNiO4 mixed oxides in the NH3 oxidation in general could be attributed to the extent of the redox reaction: 2Ni(2+) + O-2 + V-0(..) reversible arrow 2Ni(3+) + 20(-) where V-0(..) representes the oxygen vacancies and O- the oxygen species adsorbed at the vacancies.