La-2(Zr0.7Ce0.3)(2)O-7 - A new oxide ceramic material with high sintering-resistance

Oxide ceramics with high sintering-resistance above 1473 K have very important applications in thermal barrier coatings (TBCs), catalytic combustion and high-temperature structural materials. Lanthanum zirconate (La2Zr2O7, LZ) is an attractive TBC material which has higher sintering-resistance than yttria stabilized zirconia (YSZ), and this property could be further improved by the proper addition of ceria.

Sintering-resistant hollow fibers of LaMgAl11O19 prepared by electrospinning

Lanthanum magnesium hexaaluminate (LMA) is very important ceramic material for catalytic combustion of natural gas. The sintering-resistant hollow fibers of LMA with diameters ranging from 1 to 3 mu m were fabricated from alcoholic solutions containing polyvinyl pyrrolidone (PVP) and aqueous solution of lanthanum, magnesium and aluminum nitrates. The interaction between PVP and nitrates were studied by X-ray diffraction and Fourier transmission-infrared spectroscopy. The forming mechanism of hollow fibers and the sintering ability of hollow LaMgAl11O19 fibers were discussed.

Synthesis and high-pressure sintering of lanthanum magnesium hexaaluminate

Lanthanum magnesium hexaaluminate is a very important ceramic material for high temperature applications. In this paper lanthanum magnesium hexaaluminate has been synthesized directly by solid-state reaction. The forming mechanism was investigated by XRD. The SEM photographs show that the prepared powders are made of hexagonal plates. These powders can be well sintered at the high temperature (1600 degrees C) under the high pressure (4.5 GPa), and the relative density reaches 94.8%.

High-pressure sintering the novel light (W0.25Al0.75)C hard material without binder phase

A novel hard material of (W0.25Al75)C has been successfully prepared by the high-pressure sintering process without the addition of any binder phase. The high-pressure is a suitable and powerful technique for sintering the binderless hard material, the relative density of the hard material can reach 99.6% under high-pressure sintering. The density of the novel light hard material is only 6.2371 g cm(-3), which is much lighter than the normal hard material. The hardness of the light hard material can reach 18.89 GPa even the aluminum content get the astonished 75%.

High strength Ni based composite reinforced by solid solution W(Al) obtained by powder metallurgy

The solid-solution-particle reinforced W(Al)-Ni composites were successfully fabricated by using mechanical alloying (MA) and hot-pressing (HP) technique when the content of Ni is between 45 wt% and 55 wt%. Besides, samples of various original component ratio of Al50W50 to Ni have been fabricated, and the corresponding microcomponents and mechanical properties such as microhardness, ultimate tensile strength and elongation were characterized and discussed. The optimum ultimate tensile strength under the experiment conditions is 1868 MPa with elongation of 10.21 % and hardness of 6.62 GPa. X-ray diffraction (XRD), FE-SEM and energy dispersive analysis of X-rays (EDS) were given to analysis the components and morphology of the composite bulk specimens.

Fabrication, microstructure and mechanical properties of novel cemented hard alloy obtained by mechanical alloying and hot-pressing sintering

A novel cemented carbides alloy (W0.4Al0.6)C-0.65-Co were prepared by mechanical alloying and hot-pressing sintering in this work. Hot-pressing (HP) as a common technique was performed to fabricate the bulk bodies of the hard alloys. The hardness, bending strength, density of the novel hard alloy are also tested, and it has superior mechanical properties. The hardness of (W0.4Al0.6)C-0.65-Co hard alloy was very high, and the density, operate cost of the novel material were much lower than WC-Co, more important is the aluminum dissolving is not decrease the strength compared with the WC-Co system. There is almost no eta-phase in the (W0.4Al0.6)C-0.65-Co cemented carbides system even the carbon deficient reaches the astonishing value of 35%. This novel property will give us more choice to design and gain new materials that we needed.

Crystallographic and electrochemical characteristics of Ti45Zr35Ni17Cu3 quasicrystalline alloy ball-milled with nickel powder

Crystallographic and electrochemical characteristics of ball-milled Ti45Zr35Ni17Cu3 +xNi (x = 0, 5, 10, 15 and 20 mass%) composite powders have been investigated. The powders are composed of amorphous, I- and Ni-phases when x increases from 5 to 20. With increasing x, the amount of Ni-phase increases but the quasi-lattice constant decreases. The maximum discharge capacity first increases as x increases from 0 to 15 and then decreases when x increases further from 15 to 20. The high-rate dischargeability and cycling stability increase monotonically with increasing x. The improvement of the electrochemical characteristics is ascribed to the metallic nickel particles highly dispersed in the alloys, which improves the electrochemical kinetic properties and prevents the oxidation of the alloy electrodes, as well as to the mixed structure of amorphous and icosahedral quasicrystal line phases, which enhances the hydrogen diffusivity in the bulk of the alloy electrodes and efficiently inhibits the pulverization of the alloy particles.

Kinetic and electrochemical properties of icosahedral quasicrystalline Ti45Zr35Ni17Cu3 powder

Kinetic and electrochemical properties of icosahedral quasicrystalline Ti45Zr35Ni17Cu3 alloy powder as negative electrode material of Ni-MH battery have been investigated at different temperatures. The calculated results show that the apparent activation enthalpy of the charge-transfer reaction is 43.89 kJ mol(-1), and the activation energy of hydrogen diffusion is 21.03 kJ mol(-1). The exchange current density and the diffusion coefficient of hydrogen in the bulky electrode increase with increasing temperature, indicating that increasing temperature is beneficial to charge-transfer reaction and hydrogen diffusion. As a result, the maximum discharge capacity, activation property and high-rate dischargeability are greatly improved with increasing temperature. However, the charge retention and the cycling stability degrade with the increase of the temperature.

Preparation and mechanical properties of a bulk icosahedral quasicrystalline Ti45Zr35Ni17Cu3 alloy

A bulk Ti45Zr35Ni17Cu3 alloy, which consisted of the icosahedral quasicrystalline phase, was prepared by mechanical alloying(MA) and subsequent pulse discharge sintering. Ti45Zr35Ni17Cu3 amorphous powders (with particle size < 50 mu m) were obtained after mechanical alloying for more than 150 h from the mixture of the elemental powder. The transformation temperature range from amorphous phase to the quasicrystalline phase was from 400 K to 900 K. The mechanical properties of the bulk quasicrystalline alloy have been examined at room temperature. The Vickers hardness and compressive fracture strength were 620 +/- 40 and 1030 +/- 60 MPa, respectively. The bulk quasicrystalline alloy exhibited the elastic deformation by the compressive test. The fracture mode was brittle cleavage fracture.

Optical spectroscopy properties of KMgF3 : Eu2+ nanocrystals and powder synthesized by microemulsion and solvothermal process

Nanocrystals and powders of KMgF3 doped with Eu2+ were synthesized by the microemulsion method and the solvothermal process, respectively. The emission and excitation spectra of KMgF3:Eu2+ phosphors were measured and compared with those of the samples synthesized through a solid. state reaction, Bridgman-Stockbarger method, and mild hydrothermal technique. The KMgF3: Eu2+ samples synthesized by means of the microemulsion method and the solvothermal process show only a sharp emission peak located at 360 nm, in the emission spectra, which arises from the f -> f(P-6(1/2)-> S-8(1/2)) transition of Eu2+. The broad emission bands appear at 420 nm,,which arises from Eu2+ <- O2- cannot be observed(in the mild hydrothermal and single crystal samples, the emission peak at 420 nm besides the emission of Eu2+ at 360 nm is observed). In the excitation spectrum of the KMgF3: Eu2+ samples synthesized by the microemulsion method and the solvothermal process, the excitation peaks show an intensive blue shift. The blue shift can he attributed to the lower oxygenic content in the KMgF3: Eu2+ samples synthesized by the microemulsion method and the solvothermal process.

Sintering of nanopowders of amorphous silicon nitride under ultrahigh pressure

Nanopowders of amorphous silicon nitride were densified and sintered without additives under ultrahigh pressure (1.0-5.0 GPa) between room temperature and 1600 degrees C. The powders had a mean diameter of 18 nm and contained similar to 5.0 wt% oxygen that came from air-exposure oxidation, Sintering results at different temperatures were characterized in terms of sintering density, hardness, phase structure, and grain size. It was observed that the nanopowders can be pressed to a high density (87%) even at room temperature under the high pressure. Bulk Si3N4 amorphous and crystalline ceramics (relative density: 95-98%) were obtained at temperatures slightly below the onset of crystallization (1000-1100 degrees C and above 1420 degrees C, respectively. Rapid grain growth occurred during the crystallization leading to a grain size (>160 nm) almost 1 order of magnitude greater than the starting particulate diameters, With the rise of sintering temperature, a final density was reached between 1350 and 1420 degrees C, which seemed to be independent of the pressure applied (1.0-5.0 GPa), The densification temperature observed under the high pressure is lower by 580 degrees C than that by hot isostatic pressing sintering, suggesting a significantly enhanced low-temperature sintering of the nanopowders under a high external pressure.

Influence of the size of ultrafine CaCO3 powder on PP crystallization

The effects of CaCO3 on the crystallization behavior of polypropylene (PP) were studied by means of DSC and WAXD. The average sizes of the CaCO3 powders used were 0.1 mum (UC) and 0.5 mum (GC), respectively. The PP/CaCO3 composites at compositions of 1 phr and 10 phr were investigated. The results showed that the addition of CaCO3 reduced the supercooling, the rate of nucleation and the overall rate of crystallization (except for the 10 phr UC/PP sample). The crystallinity of PP was increased and the size distribution of the crystallites of alpha -PP; was: broadened. On the other hand,the crystallization rate of 10 phr UC/PP is 1.5 times higher than that of neat PP. It has an overall rate of crystallization 2 times as much as that of the neat PP and has the maximum crystallinity. The sizes of crystallites and the unit cell parameters of alpha -PP were varied by the addition of CaCO3. beta -PP was formed by addition of Ge and was not detected by addition of UC. The differences of crystallization behaviors of PP might be attributed to the combined effects of the content and size of CaCO3 filled.

Local similarity in organic crystals and the non-uniqueness of X-ray powder patterns

Two new concepts for molecular solids, 'local similarity' and 'boundary-preserving isometry', are defined mathematically and a theorem which relates these concepts is formulated. 'Locally similar' solids possess an identical short-range structure and a 'boundary-preserving isometry' is a new mathematical operation on a finite region of a solid that transforms mathematically a given solid to a locally similar one. It is shown further that the existence of such a 'boundary-preserving isometry' in a given solid has infinitely many 'locally similar' solids as a consequence. Chemical implications, referring to the similarity of X-ray powder patterns and patent registration, are discussed as well. These theoretical concepts, which are first introduced in a schematic manner, are proved to exist in nature by the elucidation of the crystal structure of some diketopyrrolopyrrole (DPP) derivatives with surprisingly similar powder patterns. Although the available powder patterns were not indexable, the underlying crystals could be elucidated by using the new technique of ab initio prediction of possible polymorphs and a subsequent Rietveld refinement. Further ab initio packing calculations on other molecules reveal that 'local crystal similarity' is not restricted to DPP derivatives and should also be exhibited by other molecules such as quinacridones. The 'boundary-preserving isometry' is presented as a predictive tool for crystal engineering purposes and attempts to detect it in crystals of the Cambridge Structural Database (CSD) are reported.