Characterization of porous silicon nitride/silicon oxynitride composite ceramics produced by sol infiltration

Porous silicon nitride/silicon oxynitride composite ceramics were fabricated by silica sol infiltration of aqueous gelcasting prefabricated Si3N4 green compact. Silica was introduced by infiltration to increase the green density of specimens, so suitable properties with low shrinkage of ceramics were achieved during sintering at low temperature. Si2N2O was formed through reaction between Si3N4 and silica sol at a temperature above 1550 degrees C. Si3N4/Si2N2O composite ceramics with a low linear shrinkage of 1.3-5.7%, a superior strength of 95-180 MPa and a moderate dielectric constant of 4.0-5.0 (at 21-39 GHz) were obtained by varying infiltration cycle and sintering temperature. (C) 2010 Published by Elsevier B.V.

Heat capacity and thermodynamic properties of pyrimethanil myristic salt (C26H41N3O2)

Pyrimethanil myristic salt was synthesized and its heat capacities were measured with an automated adiabatic calorimeter over the temperature range from T = (79 to 360) K. The melting point, molar enthalpy, Delta(fus)H(m) and entropy, Delta(fus)S(m), of fusion of this compound were determined to be (321.84 +/- 0.05) K, (56.53 +/- 0.03) kJ . mol(-1) and (175.64 +/- 0.05) J . mol(-1) . K-1, respectively. The purity of the compound was calculated to be 98.99 mol% by using the fractional melting technique. The thermodynamic functions relative to the reference temperature, T = 298.15 K, were calculated based on the heat capacity measurements in the temperature ranges from T = (80 to 360) K. The TG-DTG results demonstrate that the mass loss of the sample takes place in one step with the maximum rate at T = 500 K, which was caused by evaporation of the sample. (C) 2004 Elsevier Ltd. All rights reserved.