Preparation and optical properties of Ag/PPy composite colloids

Ag/PPy (polypyrrole) composite colloids were prepared through the reaction of silver nitrate with pyrrole solution in DNIF either in the dark, or under the irradiation of femtosecond laser (fs) pulse or UV lamp. The UV-vis spectra of the nanocomposite colloid display an intense absorption band around 620 nm, accompanied by a weak one around 470 nm. The colors and optical absorption spectra of as-synthesized colloids can be reversibly tuned between blue and red, corresponding to absorption band of 620 urn and 526 urn, within few seconds by adding base and acid solutions or gases in turn into the composite colloid suspension. In addition, excess of H+ solution enhanced the absorption band around 470 nm and, at the same time, depressed that around 620 nm. The possible mechanism for the formation and optical absorption properties of the Ag/PPy composite colloid was proposed. (C) 2006 Elsevier B.V. All rights reserved.

Preparation and characterization of hybrid ZnO/ormosils films

Hybrid ZnO/ormosils Elms are prepared by the sol-gel method. A FT-IR spectrometer, 900 UV/VIS/NIR spectrophotometer, atomic force microscope, and ellipsometer are employed to investigate microstructure and optical properties of the films fired at different temperatures. The results show that the films with high transmittance and low surface roughness could be obtained at the heat-treatment temperature of 150 degrees C, the refractive index and thickness of the film are 1.413, 2.11 mu m, respectively. Higher temperatures (350 degrees C, 550 degrees C) change the Elm microstructure severely, and then decrease the transmittance of the films.

Preparation and spectroscopic properties of Yb-doped and Yb-Al-codoped high silica glasses

Yb-doped and Yb-Al-codoped high silica glasses have been prepared by sintering nanoporous glasses. The absorption, fluorescent spectra and fluorescent lifetimes have been measured and the emission cross-section and minimum pump intensities were calculated. Codoping aluminum ions enhanced the fluorescence intensity of Yb-doped high silica glass obviously. The emission cross-sections of Yb-doped and Yb-Al-codoped high silica glasses were 0.65 and 0.82 pm(2), respectively. The results show that Yb-Al-codoped high silica glass has better spectroscopic properties for a laser material. The study of high silica glass doped with ytterbium is helpful for its application in Yb laser systems, especially for high-power and high-repetition lasers. (C) 2007 Elsevier B.V. All rights reserved.

Preparation and spectroscopic properties of Er3+-doped high silica glass fabricated by sintering nanoporous glass

A compact nonporous high silica (SiO2 % > 96%) glass containing 3400 ppm Er3+ ions, which was about ten times higher than that in Er-doped silica fiber amplifier (EDSFA), was synthesized by sintering porous glass immersed into erbium nitrate solution. The 1532 nm fluorescence has a FWHM (Full Width at Half Maximum) of 45 nm wider than that of EDSFA and possesses the glass with potential application in broadband fiber amplifiers. The Judd-Ofelt theoretical analysis reflects that Er3+ ions are located in a higher covalent environment which are comparable to those of aluminosilicate glass. (c) 2005 Elsevier B.V. All rights reserved.

Preparation of crystalline beta barium borate thin films on Sr2+-doped alpha barium borate substrates by liquid phase epitaxy

Thin films of beta barium borate have been prepared by liquid phase epitaxy on Si2+-doped alpha-BaB2O4 (alpha-BBO, the high temperature phase of barium berate) (001) and (110) substrates. The results of X-ray diffraction indicate that the films show highly (001) preferred orientation on (001)-oriented substrates while the films grown on (110) substrates are textured with (140) orientation. The crystallinity of these films was found to depend on growth temperature, rotation rate, dip time and orientation of substrate. Growth conditions were optimized to grow films with (001) orientation on (001) substrates reproducibly. The films show second harmonic generation of 400 nm light upon irradiation with 800 nm Ti: Sapphire femtosecond laser light. (c) 2005 Elsevier B.V. All rights reserved.

Preparation of Y1.84La0.16O3 nanopowders by oxalate co-precipitation method

Nanopowder of Y(1.84)mLa(0.16)O(3) was prepared by oxalate co-precipitation method. The powder was characterized by TG-DTA, XRD and TEM. The results show that the precursor is Re-2 (NO3)(2) (C2O4)(2)center dot 2H(2)O (Re=Y, La), and the Y1.84La0.16O3 nanopowders produced by calcining the precursor at 1000 degrees C for 4 h are 20 similar to 40 nm spherical particles and well dispersed. The powders were with high sintering activity and could be fabricated to transparent ceramic without additive at 1450 similar to 1550 degrees C in H-2 atmosphere for 3 hours. The total transmission of the transparent ceramic could reach 80%.

大尺寸高质量γ-LiAlO2晶体的制备研究

采用提拉法快速（6mm／h）生长了透明、φ45mm×50mm完整的铝酸锂晶体，但晶体中下部出现了一个树状、乳白色的核芯．分别从透明和乳白色核芯部位取样，研磨作粉末X射线衍射测试，发现两个样品所有的衍射峰均可以用γ-LiAlO2指标化．双晶摇摆曲线显示晶体透明和乳白色部位的半高宽分别为116．9arcsec和132．0axcsec，结晶质量较差．通过三步气相传输平衡法（简称VTE）处理后，透明部位半高宽值（FWHM）降至44．2arcsec，乳白色部位FWHM值降至53．3arcsec．结合快速生长和VTE

Preparation and optical properties of silicate glasses containing Pd nanoparticles

We report the space selective precipitation of Pd nanoparticles in Pd2+ -doped silicate glass by ultrashort laser pulses irradiation and further annealing. Absorption spectra, transmission electron microscopy, refractive index measurement and Z-scan technique demonstrated that metallic Pd nanoparticles were precipitated in the glass sample after irradiation by an 800-nm femtosecond laser and subsequent annealing at 600 degrees C. We discuss a refractive index change and nonlinear absorption that combines the precipitation of Pd nanoparticles. Crown Copyright (c) 2005 Published by Elsevier B.V. All rights reserved.

Edge-defined, film-fed growth (EFG) technique for the preparation of alpha-Al2O3 : C crystal with highly sensitive thermoluminescence response

In this work, alpha-Al2O3:C, a highly sensitive thermoluminescence dosimetry crystal, was grown by the EFG method in which a graphite heating unit and shield acted as the carbon source during the growth process. The optical, luminescent properties and dosimetric characteristics of the crystal were investigated. The as-grown crystal shows a single glow peak at 536 K, which is associated with Cr3+ ions. After annealing in H-2 at 1673 K for 80 h, the crystal shows a single glow peak at 460 K and a blue emission band at 415 nm. The thermoluminescent response of the annealed crystal shows linear-sublinear-saturation characteristics in the dose range from 5 x 10(-6) to 100 Gy.

Preparation of high laser induced damage threshold antireflection film using interrupted ion assisted deposition

Single layers and antireflection films were deposited by electron beam evaporation, ion assisted deposition and interrupted ion assisted deposition, respectively. Antireflection film of quite high laser damage threshold (18J/cm(2)) deposited by interrupted ion assisted deposition were got. The electric field distribution, weak absorption, and residual stress of films and their relations to damage threshold were investigated. It was shown that the laser induced damage threshold of film was the result of competition of disadvantages and advantages, and interrupted ion assisted deposition was one of the valuable methods for preparing high laser induced damage threshold films. (c) 2007 Optical Society of America

Preparation and characterization of nanostructured ZrO2 thin films by glancing angle deposition

ZrO2 films were prepared by electron beam evaporation with glancing angle deposition (GLAD) technique. The as-deposition and annealed ZrO2 films are all amorphous, different from that deposited at normal incidence. Due to the shadowing effect, a highly orientated structure composed of slanted columns formed, and the obtained films became the mixture of slanted columns and voids. The relationship among the effective refractive index, packing density and flux incident angle was investigated. The refractive index and packing density of ZrO2 films decrease with the increase of the incident angle. The in-plane birefringence of GLAD ZrO2 films was calculated. At the packing density of 0.576, the maximum birefringence is 0.037. (c) 2006 Elsevier B.V. All rights reserved.