The influence of arrangement of St in MBS on the properties of PVC/MBS blends

Three series of MBS core-shell impact modifiers were prepared by grafting styrene and methyl methacrylate onto PB or SBR seed latex in emulsion polymerization. All the MBS modifiers were designed to have the same total chemical composition, and MMA/Bd/St equals 30/42/28, which is a prerequisite for producing transparent blends with PVC. Under this composition, there were three different ways of arrangement for styrene in MBS, which led to the different structure of MBS modifier. The concentration of MBS in PVC/MBS blends was kept at a constant value of 20 wt.%. The effects of arrangement of St in MBS on the mechanical and optical properties of PVC/MBS blends were studied. The notched Izod impact test results showed that the MBS with a PB homopolymer core grafted with St had a lowest brittle-ductile transition (BDT) temperature and BDT temperature increased with the amount of St copolymerized with Bd in the core of MBS. The transparency of blends also increased with the amount of St copolymerized with Bd in the core. TEM results showed that the arrangement of St in MBS influenced the deformation behavior. Two deformation modes were observed in the blends: cavitation and shear yielding.

Deformation mechanism of polystyrene toughened with sub-micrometer monodisperse rubber particles

Core-shell polybutadiene-graft-polystyrene (PB-g-PS) rubber particles with different ratios of polybutadiene to polystyrene were prepared by emulsion polymerization through grafting styrene onto polybutadiene latex. The weight ratio of polybutadiene to polystyrene ranged from 50/50 to 90/10. These core-shell rubber particles were then blended with polystyrene to prepare PS/PB-g-PS blends with a constant rubber content of 20 wt%. PB-g-PS particles with a lower PB/PS ratio (<= 570/30) form a homogeneous dispersion in the polystyrene matrix, and the Izod notched impact strength of these blends is higher than that of commercial high-impact polystyrene (HIPS). It is generally accepted that polystyrene can only be toughened effectively by 1-3 mu m rubber particles through a toughening mechanism of multiple crazings. However, the experimental results show that polystyrene can actually be toughened by monodisperse sub-micrometer rubber particles. Scanning electron micrographs of the fracture surface and stress-whitening zone of blends with a PB/PS ratio of 70/30 in PB-g-PS copolymer reveal a novel toughening mechanism of modified polystyrene, which may be shear yielding of the matrix, promoted by cavitation.

Synthesis and characterization of network liquid crystal elastomers and thermosets

A new series of network liquid crystal polymers were synthesized by graft copolymerization of the difunctional mesogenic monomer 4-allyloxy-benzoyloxy-4'-allyloxybiphenyl (M) upon polymethylhydrosiloxane (PMHS). Monomer M acted not only as a mesogenic unit but also as a crosslinker for the network polymers. The chemical structures of the polymers were confirmed by IR spectroscopy. DSC, TGA, and X-ray scattering were used to measure their thermal properties and mesogenic properties. The glass transition temperature (T-g) of these network liquid crystal polymers was increased when the monomer was increased, and T-d (temperature of 5% weight loss) at first went up and reached a maximum at P, then went down. The slightly crosslinked polymers (P, P,) show rubber-like elasticity, so it was called liquid-crystal elastomer. Network polymers will lose elasticity property with a highly crosslinked degree, and turn into thermosetting polymers (P-4, P-5). All polymers exhibited a smectic texture by X-ray scattering.

Effect of gamma-irradiation on brittle-tough transition of PBT/EPDM blends

Irradiation can be applied to crosslink the dispersed elastomer phase to increase the modulus and decrease the voiding ability of the elastomer, which results in increasing critical brittle-tough transition elastomer content at constant temperature. The experimental results show that at 25 degrees C the critical elastomer content of EPDM shifts to higher composition (shift of about 4 wt%) for PBT/EPDM blends after 100 kGy gamma-irradiation. (C) 1997 Elsevier Science Ltd.