Broadband amplification and upconversion luminescence properties of Er3+/Yb3+ co-doped fluorophosphate glass

Broadband and upconversion properties were studied in Er3+/Yb3+ co-doped fluorophosphate glasses. Large Omega(6) and S-ed/(S-ed + S-md) values and the flat gain profile over 1530-1585 nm indicate the good broadband properties of the glass system. And a premise of using Omega(6) as a parameter to estimate the broadband properties of the glasses is proposed for the first time to our knowledge. Results showed that fluorescence intensity, upconversion luminescence intensity, the intensity ratio of red/green light (656 nm/545 nm) are closely related to the Yb3+:Er3+ ratio and Er3+ concentration, and the corresponding calculated lifetime of F-4(9/2) and S-4(3/2) states for red and green upconversion samples proves this conclusion. The upconversion mechanism is also discussed. (c) 2005 Elsevier Ltd. All rights reserved.

Intense upconversion luminescence and effect of local environment for Tm3+/Yb3+ co-doped novel TeO2-BiCl3 glass system

We present the results of a study that uses theoretical and experimental methods to investigate the characteristics of the upconversion luminescence of Tm3+/Yb3+ codoped TeO2-BiCl3 glass system as a function of the BiCl3 fraction. These glasses are potentially important in the design of upconversion fiber lasers. Effect of local environment around Tm3+ on upconversion fluorescence intensity was analyzed by theoretical calculations. The structure and spectroscopic properties were investigated in the experiments by measuring the Raman spectra, IR transmission spectra, and absorption and fluorescence intensities at room temperature. The results indicate that blue luminescence quantum efficiency increases with increasing BiCl3 content from 10 to 60 mol%, which were interpreted by the increase of asymmetry of glass structure, decrease of phonon energy and removing of OH- groups. (c) 2005 Elsevier B.V. All rights reserved.

Space-selective co-precipitation of silver and gold nanoparticles in femtosecond laser pulses irradiated Ag+, Au3+ co-doped silicate glass

We report on space-selective co-precipitation of silver and gold nanoparticles in Ag+, Au3+ co-doped silicate glasses by irradiation of femtosecond laser pulses and subsequent annealing at high temperatures. The color of the irradiated area in the glass sample changed from yellow to red with the increase of the annealing temperature. The effects of average laser power and annealing temperature on precipitation of the nanoparticles were investigated. A reasonable mechanism was proposed to explain the observed phenomena. (c) 2006 Elsevier Ltd. All rights reserved.

Effect of lithium-sodium mixed-alkali on phase transformation kinetics in Er3+/Yb3+ co-doped aluminophosphate glasses

Er3+ doped aluminophosphate glasses with various Na2O/Li2O ratios were prepared at 1250 degrees C using a silica crucible to study mixed alkali effect (MAE). The effect of relative alkali content on glass transition temperature, crystallization temperature and thermal stability were investigated using differential scanning calorimetry (DSC). In addition, apparent activation energies for crystallization, E, were determined employing the Kissinger equation. The effect of Al2O3 content on the magnitude of MAE was also discussed. No mixed-alkali effect is observed on crystallization temperature. (c) 2006 Elsevier B.V. All rights reserved.

Planar waveguides formed in a new chemically stable Er3+/Yb3+ co-doped phosphate glass

A new Er(3+)/Yb(3+) co-doped phosphate glass has been prepared, which exhibits good chemical durability and spectralproperties. Planar graded index waveguides have been fabricated in the glass by (Ag+)-Na(+) ion exchange in a mixed melt of silver nitrate and potassium nitrate. Ion exchange is carried out by varying the process parameters such as temperature, diffusion time, and molten salt compositions. The diffusion parameters, diffusion coefficients, and activation energy are determined by the guidelines of fabricated waveguides, which are determined by the input prism coupling technique.

Effects of chloride substitution on the chemical and physical properties and the crystallization behavior in heavy metal fluoride glasses

Effect of the substitutions of chloride for fluoride on the chemical and physical properties and the crystallization behavior in heavy metal fluoride glasses has been investigated. The characteristic temperature of the glass does not changed obviously when the fluoride was taken place by chloride. Compared with samples of being free of ErF3, the doping samples are more inclined to be surface crystallization. Optical basicity in the glass system increases with increasing the negative charge provided by the chloride atoms and the absorption peak red shifted is observed in absorption spectra. XRD measurements show that not a single crystalline phase appears in the heated glass samples, which indicate the substitutions of chloride for fluoride with a variety of crystalline precipitation trends. (c) 2007 Elsevier B.V All rights reserved.

Energy transfer between Cr3+ and Ni2+ in transparent silicate glass ceramics containing Cr3+/Ni2+ co-doped ZnAl2O4 nanocrystals

The emission intensity of Ni2+ at 1200 nm in transparent ZnO-Al2O3-SiO2 glass ceramics containing ZnAl2O4 nanocrystals is improved approximately 8 times by Cr3+ codoping with 532 nm excitation. This enhanced emission could be attributed to an efficient energy transfer from Cr3+ to Ni2+, which is confirmed by time-resolved emission spectra. The energy transfer efficiency is estimated to be 57% and the energy transfer mechanism is also discussed. (C) 2008 Optical Society of America.

Investigations on bismuth and aluminum co-doped germanium oxide glasses for ultra-broadband optical amplification

The broadband luminescence covering 1.2-1.6 mu m was observed from bismuth and aluminum co-doped germanium oxide glasses pumped by 808 nm laser at room temperature. The spectroscopic properties of GeO2:Bi,Al glasses strongly depend on the glass compositions and the pumping sources. To a certain extent, the Al3+ ions play as dispersing reagent for the infrared-emission centers in the GeO2:Bi,Al glasses. The broad infrared luminescence with a full width at half maximum larger than 200 nm and a lifetime longer than 200 mu s possesses these glasses with the potential applications in broadly tunable laser sources and ultra-broadband fiber amplifiers in optical communication field. (c) 2005 Elsevier B.V. All rights reserved.

Preparation of Y1.84La0.16O3 nanopowders by oxalate co-precipitation method

Nanopowder of Y(1.84)mLa(0.16)O(3) was prepared by oxalate co-precipitation method. The powder was characterized by TG-DTA, XRD and TEM. The results show that the precursor is Re-2 (NO3)(2) (C2O4)(2)center dot 2H(2)O (Re=Y, La), and the Y1.84La0.16O3 nanopowders produced by calcining the precursor at 1000 degrees C for 4 h are 20 similar to 40 nm spherical particles and well dispersed. The powders were with high sintering activity and could be fabricated to transparent ceramic without additive at 1450 similar to 1550 degrees C in H-2 atmosphere for 3 hours. The total transmission of the transparent ceramic could reach 80%.

Co^2＋，Er^3＋：Y3Al5O12晶体的生长及其吸收特性

应用中频感应提拉法成功生长出新型的Co^2＋，Er^3＋：Y3Al5O12晶体。研究了室温下晶体的吸收光谱性能。结合Er^3＋：Y3Al5O12晶体的光谱，并利用调Q判据对Co^2＋，Er^3＋：Y3Al5O12晶体调Q特性进行了简单的分析。结果表明Co^2＋，Er^3＋：YAG晶体是一种很有潜力的白调Q激光晶体。

Synthesis and characterization of room-temperature ferromagnetism in Fe- and Ni-co-doped In2O3

Observation of room-temperature ferromagnetisin in Fe- and Ni-co-doped In2O3 samples (In0.9Fe0.1-xNix)(2)O-3 (0 <= x <= 0.1) prepared by citric acid sol-gel auto-igniting method is reported. All of the samples with intermediate x values are ferromagnetic at roomtemperature. The highest saturation magnetization (0.453 mu B/Fe + Ni ions) moment is reached in the sample with x = 0.04. The highest solubility of Fe and Ni ions in the In2O3 lattice is around 10 and 4 at%, respectively. The 10 at% Fe-doped sample is found to be weakly ferromagnetic, while the 10at% Ni-doped sample is paramagnetic. Extensive structure including Extended X-ray absorption fine structure (EXAFS), magnetic and magneto-transport including Hall effects studies on the samples indicate the observed ferromagnetism is intrinsic rather than from the secondary impurity phases. (c) 2007 Elsevier Ltd. All rights reserved.