Effect of Single- and co-Dopant on TL of Sr2Mg(BO3)(2) Phosphor

Sr2Mg(BO3)(2) thermoluminescence (TL) phosphor was synthesized by a high temperature solid state reaction and the effect of Li+, Bi3+, Gd3+ or Ti4+ as a codopant on TL of Sr2Mg(BO3)(2) : Dy was investigated. The results show that Li+ as a codopant improves the emission intensity of high temperature TL peak of Sr2Mg(BO3)(2) : Dy phosphor whereas the addition of Bi3+, Gd3+ or Ti3+ leads to the decrease of TL intensity. The TL emission bands of Sr2Mg(BO3)(2) : Dy phosphors with Li+, Bi3+, Gd3+ or Ti4+ as a codopant are situated at 480, 579, 662 and 755 nm, which were attributed to the characteristic F-4(9/2)-> H-6(15/2), F-4(9/2)-> H-6(13/2), F-4(9/2)-> H-6(11/2) and F-4(9/2)-> H-6(9/2) transitions of Dy3+ ion, consistent with the emission of Sr2Mg(BO3)(2) : Dy phosphors. The kinetics parameters of 234 degrees C TL peak of Sr2Mg(BO3)(2) Dy-0.04(3+), (Li-0.04(+)) phosphor with the values of trap depth E=1.1 eV, frequency factor s=6.3 x 10(9) s(-1) were estimated by a peak shape method, which obey the second order kinetics.

Effect of Single- and co-Dopant on TL of Sr2Mg(BO3)(2) Phosphor(单掺杂与共掺杂离子对Sr_2Mg(BO_3)_2磷光体热释发光的影响)

Sr2Mg(BO3)(2) thermoluminescence (TL) phosphor was synthesized by a high temperature solid state reaction and the effect of Li+, Bi3+, Gd3+ or Ti4+ as a codopant on TL of Sr2Mg(BO3)(2) : Dy was investigated. The results show that Li+ as a codopant improves the emission intensity of high temperature TL peak of Sr2Mg(BO3)(2) : Dy phosphor whereas the addition of Bi3+, Gd3+ or Ti3+ leads to the decrease of TL intensity. The TL emission bands of Sr2Mg(BO3)(2) : Dy phosphors with Li+, Bi3+, Gd3+ or Ti4+ as a codopant are situated at 480, 579, 662 and 755 nm, which were attributed to the characteristic F-4(9/2)-> H-6(15/2), F-4(9/2)-> H-6(13/2), F-4(9/2)-> H-6(11/2) and F-4(9/2)-> H-6(9/2) transitions of Dy3+ ion, consistent with the emission of Sr2Mg(BO3)(2) : Dy phosphors. The kinetics parameters of 234 degrees C TL peak of Sr2Mg(BO3)(2) Dy-0.04(3+), (Li-0.04(+)) phosphor with the values of trap depth E=1.1 eV, frequency factor s=6.3 x 10(9) s(-1) were estimated by a peak shape method, which obey the second order kinetics.

Long lasting phosphorescence in Eu3+ and Ce3+ co-doped strontium borate glasses

Long lasting phosphorescence (LLP) was observed in Eu2+, Ce3+ co-doped strontium borate glasses prepared under the reducing atmosphere due to the emission of both Eu2+ and Ce3+. The methods of photoluminescence, thermoluminescence and phosphorescence were used to study the samples, and possible mechanism was suggested. The co-doping of Ce3+ ions poisoned the phosphorescence emission of Eu2+ because of the competition to obtain the trapped electron. The phosphorescence of Ce3+ in the sample decays more quickly than that of Eu2+, which is suggested for the reason that the emission energy of Ce3+ is higher or the distance between Ce3+ and electron traps of the glasses is longer.

Luminescence properties of CdSiO3 : Mn2+ phosphor

A novel long-lasting phosphor CdSiO3:Mn2+ is reported in this paper. The Mn2+-doped CdSiO3 phosphor emits orange light with CIE chromaticity coordinates x = 0.5814 and y = 0.4139 under 254 nm UV light excitation. In the emission spectrum of 1% Mn2+-doped CdSiO3 phosphor, there is a broad emission band centered at 575 nm which can be attributed to the,pin-forbidden transition of the d-orbital electron associated with the Mn2+ ion. The phosphorescence can be seen by the naked eyes in the dark clearly even after the 254 nm UV irradiation have been removed for about 1 h. The mechanism of the origin of the long-lasting phosphorescence was discussed using the thermoluminescence curves.

Effect of samarium on Mn activated zinc borosilicate storage glasses

Samarium and manganese co-doped zinc borosilicate storage glasses were prepared by high temperature solid state method. The effect of doping samarium on the defect of Mn activated sample was studied by means of thermoluminescence spectra. It was found that the shallower traps of the sample predominate with the addition of samarium, as a result, the phosphorescence and storage properties of the manganese doped zinc borosilicate glasses were greatly changed.

STUDY ON ION-IMPLANTATION OF EUROPIUM INTO CAF2 SINGLE-CRYSTAL

CaF_2 single crystal is very useful as optical host materials. It has been systematically studied and widely used in thermoluminescence that rare earth ions were doped into CaF_2 single crystal with chemical methods. However, the ion implan-