Phase transformation and photoluminescence properties of nanocrystalline ZrO2 powders prepared via the Pechini-type sol-gel process

Nanocrystalline ZrO2 fine powders were prepared via the Pechini-type sol-gel process followed by annealing from 500 to 1000 degrees C. The obtained ZrO2 samples were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), electron paramagnetic resonance (EPR), and photoluminescence spectra (PL), respectively. The phase transition process from tetragonal (T) to monoclinic (M) was observed for the nanocrystalline ZrO2 powders in the annealing process, accompanied by the change of their photoluminescence properties. The 500 degrees C annealed ZrO2, powder with tetragonal structure shows an intense whitish blue emission (lambda(max) = 425 nm) with a wide range of excitation (230-400 nm). This emission decreased in intensity after being annealed at 600 degrees C (T + M-ZrO2) and disappeared at 700 (T + M-ZrO2), 800 (T + M-ZrO2), and 900 degrees C (M-ZrO2). After further annealing at 1000 degrees C (M-ZrO2), a strong blue-green emission appeared again (lambda(max) = 470 nm).

Synthesis of Ruthenium Dioxide Nanoparticles by a Two-Phase Route and Their Electrochemical Properties

Dissolvable, size- and shape-controlled ruthenium dioxide nanoparticles are successfully achieved through a two-phase route. The influence of reaction time, temperature, and monomer concentration and the nature of capping agents on the morphologies of nanoparticles are studied through transmission electron microscopy (TEM). A possible mechanism for the formation and growth of nanoparticles is also involved. X-ray powder diffraction (XRD) confirms the amorphous structure for as-prepared ruthenium dioxide nanoparticles. Samples are immobilized by simple dip-coating on a current collector, and the cyclic voltammetry measurement is utilized to investigate their electrochemical properties. The specific capacitance of one sample can teach as high as 840 F g(-1), which reveals the promising application potential to electrochemical capacitors.

Phase Behavior and dewetting for polymer blend films studied by in situ AFM and XPS: From thin to ultrathin films

In this work, the film thickness (l(0)) effect on the phase and dewetting behaviors of the blend film of poly(methyl methacrylate)/poly (styrene-ran-acrylonitrile) (PMMA/SAN) has been studied by in situ atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). The thinner film shows the more compatibility of the blend, and the phase separation of the film occurs at l(0) > 5R(g) (radius of gyration). An initially time-independent q*, the characteristic wavenumber of the phase image, which is in good agreement of Cahn's linearized theory for the early stage of spinodal decomposition, has been obtained in real space and discussed in detail. For 5R(g) > l(0) > 3R(g), a "pseudo-dewetting/(phase separation + wetting)" behavior occurs, where the pseudo-wetting is driven by the concentration fluctuation mechanism. For 10 < 3R(g), a "real dewetting/(phase separation + wetting)" behavior occurs.

Phase conversion and spectral properties of long lasting phosphor Zn-3 (PO4)(2): Mn2+, Ga3+

A red long lasting phosphor Zn-3(PO4)(2): Mn2+ Ga3+ (ZPMG) was prepared by ceramic method, and phase conversion and spectral properties were investigated. Results indicated that the phase conversion from alpha-Zn-3(PO4), beta-Zn-3(PO4)(2) to gamma-Zn-3(PO4)(2) occurs with different manganese concentration incorporated and sinter process. The structural change induced by the phase transformation results in a remarkable difference in the spectral properties. The possible luminescence mechanism for this red LLP with different forms has been illustrated.

The influence of hard-segments on two-phase structure and shape memory properties of PCL-based segmented polyurethanes

Poly(epsilon-caprolactone)-based segmented polyurethanes (PCLUs) were prepared from poly(epsilon-caprolactone) diol, diisocyanates (DI), and 1,4-butanediol. The DIs used were 4,4'-diphenylmethane diisocyanate (MDI), 2,4-toluenediisocyanate (TDI), iso-phorone diisocyanate (IPDI), and hexamethylene diisocyanate (HDI). Differential scanning calorimetry, small-angle X-ray scattering, and dynamic mechanical analysis were employed to characterize the two-phase structures of all PCLUs. It was found that HDI- and MDI-based PCLUs had higher degree of microphase separation than did IPDI- and TDI-based PCLUs, which was primarily due to the crystallization of HDI- and MDI-based hard-segments. As a result, the HDI-based PCLU exhibited the highest recovery force up to 6 MPa and slowest stress relaxation with increasing temperature. Besides, it was found that the partial damage in hard-segment domains during the sample deformation was responsible for the incomplete shape-recovery of PCLUs after the first deformation, but the damage did not develop during the subsequent deformation.

Phase transition and conformational variation of N-alkylated branched poly(ethyleneimine) comblike polymer

A series of branched poly(ethyleneimine) (PEI) derived polymers with different lengths of n-alkyl side chains, denoted as PEI(n)Cs (n = 12, 14, 16, 18, 20, number of carbon atoms in alkyl side group), have been prepared by a N-alkylation method, and systematically characterized by differential scanning calorimertry (DSC) and wide-angle X-ray diffraction (WARD) as well as Fourier transform infrared spectroscopy (FTIR). The side chains grafted on these comblike polymers are long enough to form crystalline phase composed of paraffin-like crystallites. The crystallization of the side chains forces the branched poly(ethyleneimine) molecules to pack into layered structure, between which the crystallites are located. The melting temperatures of the side chain crystallites increase from -12.36 to +51.49 degreesC with increasing the length of the side chains from n. = 12 to n = 20, which are a little bit lower than the corresponding pristine n-alkanes. PEI18C was taken as an example in this work for the investigation of phase transition and conformational variation of the side chains with temperature changing.

On improving the phase stability and thermal expansion coefficients of lanthanum cerium oxide solid solutions

The phase stability of lanthanum cerium oxide (La2Ce2O7), which is stable up to 1400 degrees C, and the thermal expansion coefficient of La2Ce2O7 doped with Ta2O5 or WO3 were studied. The thermal expansion coefficient of La2Ce2O7 below 400 degrees C was increased by adding more CeO2 or doping with either Ta2O5 or WO3.

Phase structure and transition behavior of a liquid crystal 5-{[(4 '-heptoxy-4-biphenylyl)oxy]carbonyl}-1-pentyne

The phase structures and transition behaviors of a novel liquid crystal compound containing biphenylyl mesogen, 5-{[(4'-heptoxy-4-biphenytyl) oxy]carbonyl}-1-pentyne (A3E'O7), have been investigated by differential scanning calorimetry (DSC), polarizing optical microscopy (POM) and wide angle X-ray diffraction (WAXD). In contrast to the published compound 5- {[(4'-heptoxy-4-biphenyl-yl)carbonyl]oxy}-1-pentyne (A3EO7), in which the ester bridge between the mesogenic core and the flexible spacer has different linkage order, A3E'O7 shows strikingly different phase structure and transition behaviors. Overall, A3E'O7 has better packing order and higher transition temperatures. It undergoes three enantiotropic stable liquid crystalline phases which are associated to smectic A (S-A) phase (100.2-98.2 degrees C), smectic C (S-C) phase (98.2-87.2 degrees C) and highly ordered smectic X (S-X) phase (87.2-63.3 degrees C), respectively, till eventual crystallization takes place upon cooling from isotropic state to room temperature. However, A3EO7 only shows monotropic SA (72.4-53.6 degrees C) phase and the metastable monotropic S-C phase provided that the same thermal treatment is applied.

Phase transition and transition kinetics of a thermotropic poly(amide-imide) derived from 70% pyromellitic dianhydride, 30% terephthaloyl chloride, and 1,3-bis[4-(4 '-aminophenoxy)cumyl]benzene

The phase transition and transition kinetics of a liquid crystalline copoly(amide-imide) (PAI37), which was synthesized from 70 mol% pyromellitic dianhydride, 30 mol% terephthaloyl chloride, and 1,3-bis[4-(4'-aminophenoxy)cumyl]benzene, was characterized by differential scanning calorimetry, polarized light microscopy, X-ray diffraction, and rheology. PAI37 exhibits a glass transition temperature at 182 degreesC followed by multiple phase transitions. The crystalline phase starts to melt at similar to 220 degreesC and forms smectic C (S-C) phase. The Sc phase transforms into smectic A (S-A) phase when the temperature is above 237 degreesC. The S-C to S-A transition spans a broad temperature range in which the S-A phase vanishes and forms isotropic melt. The WARD fiber pattern of PAI37 pulled from the anisotropic melt revealed an anomalous chain orientation, which was characterized by its layer normal perpendicular to the fiber direction. The transition kinetics for the mesophase and crystalline phase formation was also studied.

Phase structure and transitions in a poly(methyloctadecylsilane) oligomer

A poly(methyloctadecylsilane) oligomer was synthesized by a typical Wurtz coupling reaction. Upon cooling, three transitions were observed at temperatures of 39.9, 37.5 and 33.9 degreesC at a rate of 2.5 degreesC/min in differential scanning calorimetry (DSC). The first transition, with enthalpy change of 0.47 kT/mol and supercooling of 0.2 degreesC, was characteristic of the conformational change in the Si-Si backbone into an all-trans conformation, which was detected by temperature-dependent Fourier transform infrared (FT-FR) spectroscopy. The second and the third transitions with large supercooling were identified as the formation of two-dimensional hexagonal crystal packing and three-dimensional two-chain orthorhombic crystal packing, respectively. The crystal structure was determined by the combination of WAXD and transmission electron microscopy (TEM) experiments. (C) 2000 Elsevier Science Ltd. All rights reserved.

The phase inversion and morphology of nylon 1010 polypropylene blends

Noncompatibilized and compatibilized blends of nylon 1010/PP blends having five different viscosity ratios were prepared by melt extrusion. Glycidyl methacrylate-grafted-polypropylene (PP-g-GMA) was used as the compatibilizer to enbance the adhesion between the two polymers and to stabilize the blend morphology. The effect of the viscosity ratio on the morphology of nylon 1010/polypropylene blends was investigated, with primary attention to the phase-inversion behavior and the average particle size of the dispersed phase. The relationship between the mechanical properties and the phase-inversion composition was investigated as well. Investigation of the morphology of the blends by microscopy indicated that the smaller the viscosity ratio (eta(PP)/eta(PA)) the smaller was the polypropylene concentration at which the phase inversion took place and polypropylene became the continuous phase. The compatibilizer induced a sharp reduction of particle size, but did not have a major effect on the phase-inversion point. An improvement :in the mechanical properties was found when nylon 1010 provided the matrix phase. (C) 1996 John Wiley & Sons, Inc.

EFFECT OF V, NB, AND TA DOPING ON THE 2223 PHASE-FORMATION AND THE CRYSTAL-STRUCTURE IN THE BISRCACUO SYSTEM

X-ray diffraction and electrical and diamagnetic analyses revealed that the 2223 phase was significantly enhanced by high-valence cation (V5+, Nb5+, Ta5+, etc.) doping in BiSrCaCuO samples. The optimum nominal composition was Bi1.6M0.4Sr2Ca2Cu3 O(y)(M =