Preparation and AFM characterization of self-ordered porous alumina films on semi-insulated gaas substrate

Self-ordered porous alumina films on a semi-insulated GaAs substrate were prepared in oxalic acid aqueous solutions by three-step anodization. The I-t curve of anodization process was recorded to observe time effects of anodization. Atomic force microscopy was used to investigate structure and morphology of alumina films. It was revealed that the case of oxalic acid resulted in a self-ordered porous structure, with the pore diameters of 60-70 nm, the pore density of the order of about 10(10) pore cm(-2), and interpore distances of 95-100nm. At the same time the pore size and shape change with the pore widening time. Field-enhanced dissolution model and theory of deformation relaxation combined were brought forward to be the cause of self-ordered pore structure according to I-t curve of anodization and structure characteristics of porous alumina films. (c) 2006 Elsevier Ltd. All rights reserved.

TEMPERATURE EFFECT ON POROUS SILICON LUMINESCENCE

A theoretical surface-state model of porous-silicon luminescence is proposed. The temperature effect on the PhotoLuminescence (PL) spectrum for pillar and spherical structures is considered, and it is found that the effect is dependent on the doping concentration, the excitation strength, and the shape and dimensions of the Si microstructure. The doping concentration has an effect on the PL intensity at high temperatures and the excitation strength has an effect on the PL intensity at low temperaturs. The variations of the PL intensity with temperature are different for the pillar and spherical structures. At low temperatures the PL intensity increases in the pillar structure, while in the spherical structure the PL intensity decreases as the temperature increases, at high temperatures the PL intensities have a maximum for both models. The temperature, at which the PL intensity reaches its maximum, depends on the doping concentration. The PL spectrum has a broader peak structure in the spherical structure than in the pillar structure. The theoretical results are in agreement with experimental results.

LUMINESCENCE-CENTERS IN POROUS SILICON

Photoluminescence studies on porous silicon show that there are luminescence centers present in the surface states. By taking photoluminescence spectra of porous silicon with respect to temperature, a distinct peak can be observed in the temperature range 100-150 K. Both linear and nonlinear relationships were observed between excitation laser power and the photoluminescence intensity within this temperature range. In addition, there was a tendency for the photoluminescence peak to red shift at low temperature as well as at low excitation power. This is interpreted as indicating that the lower energy transition becomes dominant at low temperature and excitation power. The presence of these luminescence centers can be explained in terms of porous silicon as a mixture of silicon clusters and wires in which quantum confinement along with surface passivation would cause a mixing of Gamma and X band structure between the surface states and the bulk. This mixing would allow the formation of luminescence centers.

Characterization of porous silicon nitride/silicon oxynitride composite ceramics produced by sol infiltration

Porous silicon nitride/silicon oxynitride composite ceramics were fabricated by silica sol infiltration of aqueous gelcasting prefabricated Si3N4 green compact. Silica was introduced by infiltration to increase the green density of specimens, so suitable properties with low shrinkage of ceramics were achieved during sintering at low temperature. Si2N2O was formed through reaction between Si3N4 and silica sol at a temperature above 1550 degrees C. Si3N4/Si2N2O composite ceramics with a low linear shrinkage of 1.3-5.7%, a superior strength of 95-180 MPa and a moderate dielectric constant of 4.0-5.0 (at 21-39 GHz) were obtained by varying infiltration cycle and sintering temperature. (C) 2010 Published by Elsevier B.V.

Template-assisted syntheses of two novel porous zirconium methylphosphonates

Two porous zirconium methylphosphonates (designated as ZMPmi and ZMPme respectively) were synthesized by using dibutyl methylphosphonate (DBMP) as a template. Two efficient post-synthetic treatments were developed to remove the incorporated template without destroying the hybrid structures. The materials were characterized by SEM, EPMA, TG, DTA, FTIR, and NMR. Specific surface area and porosity were evaluated by BET, alpha(s)-plots and DFT methods based on N-2 adsorption-desorption isotherms. The specific surface areas of ZMPmi and ZMPme are determined to be 279 and 403 m(2) g(-1) and the maxima of pore size distributions are at 0.7 and 1.3 nm respectively. (c) 2005 Elsevier Inc. All rights reserved.

Strings of interconnected hollow carbon nanoparticles with porous shells prepared using simple solid-phase synthesis

Strings of interconnected hollow carbon nanoparticles with porous shells were prepared by simple heat-treatments of a mixture of resorcinol-formaldehyde gel and transition-metal salts. The sample was characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction and nitrogen adsorption. Results show that the sample consisted of relatively uniform hollow particles with sizes ranging from 70 to 80 nm forming a strings-of-pearls-like nanostructure. The material with porous shells possessed well-developed graphitic structure with an interlayer (d(002)) spacing of 0.3369 nm and the stack height of the graphite crystallites of 9 nm.

Removal of Cr(III, VI) by quaternary ammonium and quaternary phosphonium ionic liquids functionalized silica materials

A series of silica-based organic–inorganic hybrid materials were prepared by the sol–gel process for Cr(III) and Cr(VI) adsorption. These silica materials generally had high surface areas, good physical–chemical stability and high thermal stability. Trialkylmethylammonium bis 2,4,4-trimethylpentylphosphinate ([A336][C272]) and trihexyl(tetradecyl)phosphonium bis 2,4,4-trimethylpentylphosphinate (Cyphos IL 104) were explored as porogens to prepare porous silica and as extractants to extract chromium ions. Cyphos IL 104 and [A336][C272] functionalized silica sorbents (SG-2, SG-5) can be effectively used for the removal of Cr(III) and Cr(VI) from aqueous solutions by adjusting pH values, whereas trialkylmethylammonium chloride (Aliquat 336) and bis(2,4,4-trimethylpentyl)phosphinic acid (Cyanex 272) functionalized silica sorbents (SG-3, SG-4) can only be used for the removal of the single chromium species, Cr(VI) or Cr(III).

Novel acidic porous clay heterostructure with highly ordered organic-inorganic hybrid structure: one-pot synthesis of mesoporous organosilica in the galleries of clay

A new class of organic-inorganic hybrid porous clay heterostructures (HPCHs) have been prepared through the surfactant-directed assembly of organosilica in the galleries of montmorillonite. The reaction involved hydrolysis and condensation of phenyltriethoxysilane and tetraethoxysilane in the presence of intragallery surfactant templates (dodecylame and cetyltrimethylammonium ion). The surfactant templates were removed from the pores by solvent-extraction. The products were characterized by X-ray diffraction (XRD), N-2 adsorption, solid-state Si-29 and C-13 NMR, and FTIR. XRD patterns indicated a regular interstratification of the clay layers for HPCHs. Depending on loading of phenyl groups, HPCHs had BET surface areas of 390-771 m(2) g(-1), pore volumes of 0.3-0.59 cm(3) g(-1), and the framework pore sizes in the supermicropore to small mesopore range (1.2-2.6 nm). HPCHs were hydrophobic and acidic.