Oxygen permeating properties of the mixed conducting membranes without cobalt

A new series of mixed conducting oxides, Sr10-n/2BinFe20Om (n = 4, 6, 8, 10), were synthesized by a solid state reaction method, and they have high oxygen permeability. The oxygen permeation rate at 1150 K is 0.41 ml(STD)/ cm(2).min for n = 6 and 0.90 ml(STD)/cm(2).min for n = 10, which is two times higher than that for Sr1-xBixFeO3 (x = 0.5). For the Sr1-xBixFeO3 (x = 0.1, 0.3, 0.5) series, the oxygen flux increases with increasing Bi content. (C) 1998 Elsevier Science Ltd.

Study on the Adsorption and Activation of NO and CO over Mixed Oxide Catalysts Containing Cu by Means of TPSR

Adsorption and activation of small molecules NO, CO and CO+ NO on LaSrCuO4, La2CuO4 and La1.7Th0.3CuO4 which are typical samples in the sence of nonstoichiometric oxygen(lambda) anrong the series of La2-x(SrTh)(x)CuO4 +/-lambda mixed oxide catalysts were studied by means of MS- TPD (TPSR ), XRD, chemical analysis and so on. It was shown that the adsorption amount of NO can be correlated with the content of oxygen vacancy while the types and strength of adsorption of NO could be related to the oxidation state of the metallic ion. It was also found that CO molecule was first converted into CO32- and then desorbed in the form of CO2 at high temperature during the adsorption and desorption of CO on the mixed oxide with oxygen vacancy. The fact that the profiles of TPD(TPSR) of NO in co-adsorption of NO+CO and in single NO adsorption are similar shows that the adsorption of NO molecule not only has some priority to that of CO but also is stronger than that of CO. It seems that the adsorption of NO plays a dominate role in the activation and decomposition of NO.

Electrochemical preparation of microelectrodes modified with non-stoichiometric mixed-valent molybdenum oxides

A compact non-stoichiometric molybdenum (VI, V) oxide of blue film was grown on carbon fiber (CF) microelectrode surface be cycling the potential between + 0.2V and - 0.70V in a freshly prepared Na2MoO4 solution containing 5 x 10(-3) mol/L H2SO4. The quantity-of the oxide is controlled by the charge passing the electrode. The electrochemical pretreatment of CF microelectrode not only mises the deposition velocity of molybdenum oxide on CF surface, but also improves greatly the cyclic voltammetric behavior of the molybdenum oxide film prior to the electrodeposition. The cathodic processes are believed to yield the hydrogen molybdenum oxide bronzes HxMoO3(0 < x < 2), or substoichiometric lower molybdenum oxides with the formula MoO3-y(0 < y < 1). The anodic response results from the reversible oxidation of molybdenum bronze/Mo(V) centers [or perhaps Mo(IV) in more reduced coatings], to Mo(VI). Further information was gained about the chemical composition and valent state of Mo from XPS and SEM.

PREPARATION, CRYSTAL-STRUCTURE, AND VIBRATIONAL-SPECTRA OF PEROVSKITE-TYPE MIXED OXIDES LAM(Y)M'(1-Y)O(3) (M,M'=MN, FE, CO)

Three series of samples LaMnyCo1-yO3+/-lambda, LaFeyMn1-yO3+/-lambda, and LaFeyCo1-yO3+/-lambda (y = 0.0 to 1.0) with Perovskite structure were prepared by an explosion method different from the generally used ceramic techniques. The variation of crystal

A HIGH-RESOLUTION SOLID-STATE NMR AND DSC STUDY OF MISCIBILITY AND CRYSTALLIZATION BEHAVIOR OF POLY(VINYL ALCOHOL)/POLY(N-VINYL-2-PYRROLIDONE) BLENDS

Blends of crystallizable poly(vinyl alcohol) (PVA) with poly(N-vinyl-2-pyrrolidone) (PVPy) were studied by C-13 cross-polarization/magic angle spinning (CP/MAS) n.m.r. and d.s.c. The C-13 CP/MAS spectra show that the blends were miscible on a molecular level over the whole composition range studied, and that the intramolecular hydrogen bonds of PVA were broken and intermolecular hydrogen bonds between PVA and PVPy formed when the two polymers were mixed. The results of a spin-lattice relaxation study indicate that blending of the two polymers reduced the average intermolecular distance and molecular motion of each component, even in the miscible amorphous phase, and that addition of PVPy into PVA has a definite effect on the crystallinity of PVA in the blends over the whole composition range, yet there is still detectable crystallinity even when the PVPy content is as high as 80 wt%. These results are consistent with those obtained from d.s.c. studies.

MOLECULAR-GEOMETRY AND CHAIN ENTANGLEMENT - PARAMETERS FOR THE TUBE MODEL

The tube diameter in the reptation model is the distance between a given chain segment and its nearest segment in adjacent chains. This dimension is thus related to the cross-sectional area of polymer chains and the nearest approach among chains, without effects of thermal fluctuation and steric repulsion. Prior calculated tube diameters are much larger, about 5 times, than the actual chain cross-sectional areas. This is ascribed to the local freedom required for mutual rearrangement among neighboring chain segments. This tube diameter concept seems to us to infer a relationship to the corresponding entanglement spacing. Indeed, we report here that the critical molecular weight, M(c), for the onset of entanglements is found to be M(c) = 28 A/([R2]0/M), where A is the chain cross-sectional area and [R2]0 the mean-square end-to-end distance of a freely jointed chain of molecular weight M. The new, computed relationship between the critical number of backbone atoms for entanglement and the chain cross-sectional area of polymers, N(c) = A0,44, is concordant with the cross-sectional area of polymer chains being the parameter controlling the critical entanglement number of backbone atoms of flexible polymers.

A HIGH-RESOLUTION SOLID-STATE NMR-STUDY OF THE MISCIBILITY, MORPHOLOGY, AND TOUGHENING MECHANISM OF POLYSTYRENE WITH POLY(2,6-DIMETHYL-1,4-PHENYLENE OXIDE) BLENDS

An extended Goldman-Shen pulse sequence was used to observe indirectly the proton spin diffusion in the blends of polystyrene (PS) with poly(2,6-dimethyl-1,4-phenylene oxides) (PPO). The results indicate that the average distance between PS and PPO is less than 5 angstrom in the intimately mixed phase, but there are heterogeneous domains on a 100-angstrom scale. The data of spin relaxation of carbons, T1(C), for homopolymers and their blends suggest that there is a strong pi-pi electron conjugation interaction between the aromatic rings of PS and those of PPO, while the aromatic rings of PPO drive the aromatic rings of PS to move cooperatively. It is the cooperative motion that markedly improves the impact strength of PS.

Performance of a mixed-conducting ceramic membrane reactor with high oxygen permeability for methane conversion

A mixed-conducting perovskite-type Ba0.5Sr0.5Co0.8Fe0.2O3-delta (BSCFO) ceramic membrane reactor with high oxygen permeability was applied for the activation of methane. The membrane reactor has intrinsic catalytic activities for methane conversion to ethane and ethylene. C-2 selectivity up to 40-70% was achieved, albeit that conversion rate were low, typically 0.5-3.5% at 800-900 degreesC with a 50% helium diluted methane inlet stream at a flow rate of 34 ml/min. Large amount of unreacted molecular oxygen was detected in the eluted gas and the oxygen permeation flux improved only slightly compared with that under non-reactive air/He experiments. The partial oxidation of methane to syngas in a BSCFO membrane reactor was also performed by packing LiLaNiO/gamma -Al2O3 with 10% Ni loading as the catalyst. At the initial stage, oxygen permeation flux, methane conversion and CO selectivity were closely related with the state of the catalyst. Less than 21 h was needed for the oxygen permeation flux to reach its steady state. 98.5% CH4 conversion, 93.0% CO selectivity and 10.45 ml/cm(2) min oxygen permeation flux were achieved under steady state at 850 degreesC. Methane conversion and oxygen permeation flux increased with increasing temperature, No fracture of the membrane reactor was observed during syngas production. However, H-2-TPR investigation demonstrated that the BSCFO was unstable under reducing atmosphere, yet the material was found to have excellent phase reversibility. A membrane reactor made from BSCFO was successfully operated for the POM reaction at 875 degreesC for more than 500h without failure, with a stable oxygen permeation flux of about 11.5 ml/cm(2) min. (C) 2001 Elsevier Science B.V. All rights reserved.

Electrochemical performance of mixed ionic-electronic conducting oxides as anodes for solid oxide fuel cell

Mixed ionic-electronic conducting (MIEC) oxides, SrFeCo0.5Ox, SrCo0.8Fe0.2O3-delta and La0.6Sr0.4Fe0.8Co0.2O3-delta have been synthesized and prepared on yttria-stabilized zirconia as anodes for solid oxide fuel cells. Power output measurements show that the anodes composed of such kinds of oxides exhibit modest electrochemical activities to both H-2 and CH4 fuels, giving maximum power densities of around 0.1 W/cm(2) at 950 degrees C. Polarization and AC impedance measurements found that large activation overpotentials and ohmic resistance drops were the main causes for the relative inferior performance to the Ni-YSZ anode. While interlayered with an Ni-YSZ anode, a significant improvement in the electrochemical performance was observed. in particular, for the SrFeCo0.5Ox oxide interlayered Ni-YSZ anode, the maximum power output reaches 0.25 W/cm2 on CH,, exceeding those of both SrFeCo0.5Ox and the Ni-YSZ, as anodes alone. A synergetic effect of SrFeCo0.5Ox and the Ni-YSZ has been observed. Future work is needed to examine the long-term stability of MIEC oxide electrodes under a very reducing environment. (C) 1999 Elsevier Science B.V. All rights reserved.