Improved surface morphology of stacked 1.3 mu m InAs/GaAs quantum dot active regions by introducing annealing processes

The authors report a simple but effective way to improve the surface morphology of stacked 1.3 mu m InAs/GaAs quantum dot (QD) active regions grown by metal-organic chemical vapor deposition (MOCVD), in which GaAs middle spacer and top separate confining heterostructure (SCH) layers are deposited at a low temperature of 560 degrees C to suppress postgrowth annealing effect that can blueshift emission wavelength of QDs. By introducing annealing processes just after depositing the GaAs spacer layers, the authors demonstrate that the surface morphology of the top GaAs SCH layer can be dramatically improved. For a model structure of five-layer QDs, the surface roughness with the introduced annealing processes (IAPs) is reduced to about 1.3 nm (5x5 mu m(2) area), much less than 4.2 nm without the IAPs. Furthermore, photoluminescence measurements show that inserting the annealing steps does not induce any changes in emission wavelength. This dramatic improvement in surface morphology results from the improved GaAs spacer surfaces due to the IAPs. The technique reported here has important implications for realizing stacked 1.3 mu m InAs/GaAs QD lasers based on MOCVD.

High-speed and high-power 1.3 mu m InGaAsP/InP selective proton-bombarded buried crescent lasers with optical field attenuation regions

High-speed and high-power InGaAsP/lnP selective proton-bombarded buried crescent (SPB-BC) lasers with optical field attenuation regions were reported. The defect of proton bombardment can not affect the lifetime of the SPB-BC laser because the optical field attenuation region obstructs the growth and propagation of defects. A CW light output over 115 mW was achieved at room temperature using a 500 mu m long cavity SPB-BC laser. The 3 dB bandwidth was 8.5 GHz, and the lifetime was about 8.5 x 10(5) h. The capacitance of four kinds of current blocking structures was first measured in our experiment, and the results shown that the capacitance of proton-bombarded pnpn structure was not only less than that of pnpn current blocking structure, but also less than that of semi-insulating Fe-InP structure.