Twinning and Stacking Fault Formation during Tensile Deformation of Nanocrystalline Ni

Deformation twins and stacking faults have been observed in nanocrystal line Ni, for the first time under uniaxial tensile test conditions. These partial dislocation mediated deformation mechanisms are enhanced at cryogenic test temperatures. Our observations highlight the effects of deformation conditions, temperature in particular, on deformation mechanisms in nanograins.

Mixed-mode fracture mechanisms near the fatigue threshold of aisi-316 stainless-steel

Near threshold, mixed mode (I and II), fatigue crack growth occurs mainly by two mechanisms, coplanar (or shear) mode and branch (or tensile) mode. For a constant ratio of ΔK_I/ΔK_II the shear mode growth shows a self-arrest character and it would only start again when ΔK_I and ΔK_II are increased. Both shear crack growth and the early stages of tensile crack growth, are of a crystallographic nature; the fatigue crack proceeds along slip planes or grain boundaries. The appearance of the fracture surfaces suggest that the mechanism of crack extension is by developing slip band microcracks which join up to form a macrocrack. This process is thought to be assisted by the nature of the plastic deformation within the reversed plastic zone where high back stresses are set up by dislocation pile-ups against grain boundaries. The interaction of the crack tip stress field with that of the dislocation pile-ups leads to the formation of slip band microcracks and subsequent crack extension. The change from shear mode to tensile mode growth probably occurs when the maximum tensile stress and the microcrack density in the maximum tensile plane direction attain critical values.

Formation of Single and Multiple Deformation Twins in Nanocrystalline fcc Metals

Deformation twins are often observed to meet each other to form multi-fold twins in nanostructured face-centered cubic (fcc) metals.Here we propose two types of mechanism for the nucleation and growth of four different single and multiple twins. These mechanisms provide continuous generation of twinning partials for the growth of the twins after ucleation. A relatively high stress or high strain rate is needed to activate these mechanisms, making them more prevalent in nanocrystalline materials than in their coarse-grained counterparts.Experimental observations that support the proposed mechanisms are presented.

Mechanisms of ultrafast laser-induced deep-subwavelength gratings on graphite and diamond

Deep-subwavelength gratings with periodicities of 170, 120, and 70 nm can be observed on highly oriented pyrolytic graphite irradiated by a femtosecond (fs) laser at 800 nm. Under picosecond laser irradiation, such gratings likewise can be produced. Interestingly, the 170-nm grating is also observed on single-crystal diamond irradiated by the 800-nm fs laser. In our opinion, the optical properties of the high-excited state of material surface play a key role for the formation of the deep-subwavelength gratings. The numerical simulations of the graphite deep-subwavelength grating at normal and high-excited states confirm that in the groove the light intensity can be extraordinarily enhanced via cavity-mode excitation in the condition of transverse-magnetic wave irradiation with near-ablation-threshold fluences. This field enhancement of polarization sensitiveness in deep-subwavelength apertures acts as an important feedback mechanism for the growth and polarization dependence of the deep-subwavelength gratings. In addition, we suggest that surface plasmons are responsible for the formation of seed deep-subwavelength apertures with a particular periodicity and the initial polarization dependence. Finally, we propose that the nanoscale Coulomb explosion occurring in the groove is responsible for the ultrafast nonthermal ablation mechanism.

Mechanisms of optical confinement in phase-locked laser arrays

The nature of optical confinement in phase-locked laser arrays (PLLAs) with a mesa-stripe structure (MSS) has been studied. Two main mechanisms are distinguished, which are based on the variation of the waveguide effective refractive index due to MSS formation and on the refractive index modulation induced by the heating of the structure. Stable operation was achieved when either weak or strong optical coupling was realized in the PLLA. A phase-locked regime of radiation was obtained only for laser diodes with strong optical coupling. In the latter case the angle divergency was not greater than 2 degrees for the antisymmetric supermode emission from the PLLA.

Crystallization and Si incorporation mechanisms of SAPO-34

In this study of the synthesis of SAPO-34 molecular sieves, XRD, SEM, XRF, IR and NMR techniques were applied to monitor the crystalloid, structure and composition changes of the samples in the whole crystallization process in order to get evidence for the crystallization as well as Si incorporation mechanism of SATO-34. XRD results revealed that the crystallization contained two stages. In the first 2.5 h (the earlier stage), high up to similar to80% of relative crystallinity could be achieved and the crystal size of SAPO-34 was almost the same as that of any longer time, indicating a fast crystallization feature of the synthesis. In this stage, IR revealed that the formation of SAPO-34 framework structure was accompanied by the diminution of hydroxyls, suggesting that crystal nuclei of SAPO-34 may arise from the structure rearrangement of the initial gel and the condensation of the hydroxyls. NMR results reveal that the template and the ageing period are crucial for the later crystallization of SAPO-34. Preliminary structure units similar to the framework of SAPO-34 have already formed before the crystallization began (0 h and low temperature). Evidence from IR, NMR, and XRF shows that the formation of the SAPO-34 may be a type of gel conversion mechanism, the solution support and the appropriate solution circumstance are two important parameters of the crystallization of SAPO-34. Meanwhile, NMR measurements demonstrated that about 80% of total Si atoms directly take part in the formation of the crystal nuclei as well as in the growth of the crystal grains in the earlier stage (<2.5 h). Evidence tends to support that Si incorporation is by direct participation mechanism rather than by the Si substitution mechanism for P in this stage (<2.5 h). In the later stage (>2.5 h), the relative content of Si increased slightly with a little decrease of Al and P. The increase of Si(4Al) and the appearance of the Si(3Al), Si(2Al), Si(1Al) and Si(OAl) in this stage suggest that substitution of the Si atoms for the phosphorus and for the phosphorus and aluminum pair takes place in the crystallization. The relationship among structure, acidity and crystallization process is established, which suggests a possibility to improve the acidity and catalytic properties by choosing a optimum crystallization time, thus controlling the number and distribution of Si in the framework of SAPO-34. (C) 2002 Elsevier Science Inc. All rights reserved.

Mechanisms of sodium and potassium ions transfer facilitated by dibenzo-15-crown-5 across the water /1,2-dichloroethane interface using micropipettes

The transfer of sodium and potassium ions facilitated by dibenzo-15-crown-5 (DB15C5) has been studied at the micro-water/1,2-dichloroethane (water/DCE) interface supported at the tip of a micropipette. Cyclic volt-ammetric measurements were performed in two limiting conditions: the bulk concentration of Na+ or K+ in the aqueous phase is much higher than that of DB15C5 in the organic phase (DB15C5 diffusion controlled process) and the reverse condition (metal ion diffusion controlled process). The mechanisms of the facilitated Na+ transfer by DB15C5 are both transfer by interfacial complexation (TIC) with 1 : 1 stoichiometry under these two conditions, and the corresponding association constants were determined at log beta(1) = 8.97 +/- 0.05 or log beta(1) = 8.63 +/- 0.03. However, the transfers of K+ facilitated by DB15C5 show different behavior. In the former case it is a TIC process and its stoichiometry is 1 : 2, whereas in the latter case two peaks during the forward scan were observed, the first of which was confirmed as the formation of K (DB15C5)(2) at the interface by a TIC mechanism, while the second one may be another TIC process with 1 : 1 stoichiometry in the more positive potential. The relevant association constants calculated for the complexed ion, K+(DB15C5)(2), in the organic phase in two cases, logbeta(2), are 13.64 +/- 0.03 and 11.34 +/- 0.24, respectively.

Catalytic mechanisms of triphenyl bismuth, dibutyltin dilaurate, and their combination in polyurethane-forming reaction

The catalytic mechanisms of triphenyl bismuth (TPB), dibutyltin dilaurate (DBTDL) and their combination have been studied in a model polyurethane reaction system consisting of copolyether (tetrahydrofuran-ethyleneoxide) and N-100; NMR spectroscopy was used to detect the associations between reactants and catalysts. A relatively stable complex was shown to be formed between hydroxyl and isocyanate; the catalysts showed different effects on the isocyanate-hydroxyl complex, therefore resulting in different curing characteristics. The formation of hydrogen bonding between the complexed hydroxyl and other hydroxyl or the resulting urethane provided an ''auto-catalysis'' to urethane formation. DBTDL destroyed the isocyanate-hydroxyl complex before catalyzing the reaction through the formation of a ternary complex, whereas TPB was able to activate the isocyanate-hydroxyl complex directly to form urethane. The reaction catalyzed by the combination of TPB and DBTDL gained advantages from the multiple catalytic entities, i.e., TPB, DBTDL, and a TPB-DBTDL complex. (C) 1997 John Wiley & Sons, Inc.

Formation and dissociation of protonated pyridine-methanol cluster ions at 355 and 266 nm

The multi-photon ionization process of the hydrogen-bond cluster of pyridine-methanol has been investigated using a conventional and reflectron time-of-flight mass spectrometer (RTOF-MS) at 355 and 266 nm laser wavelengths, respectively. The sequences of the protonated cluster ions (CH3OH)(n)H+ and (C5H5Nn)(CH3OH)(m)H+ (n = 1,2) were observed at both laser wavelengths, while the sequence of the cluster ions (CH3)OHn (H2O)H+ was observed only at 355 nm laser wavelength. The difference between the relative signal intensities of the protonated methanol cluster ions at different laser wavelengths is attributed to different photoionization mechanisms. Some nascent cluster ions in metastable states dissociated during free flight to the detector. The dissociation kinetics is also discussed. (C) 2000 Elsevier Science B.V.