Ammonia-treated activated carbon as support of a Ru-Ba catalyst for ammonia synthesis

Ammonia-treated activated carbon has been studied as a support of Ru-Ba catalyst for ammonia synthesis. It is shown that the introduction of nitrogen leads to a decrease of ammonia synthesis activity for the catalysts with a low Ba/Ru molar ratio, while no significant changes are obtained for the catalysts with a high Ba/Ru molar ratio, confirming that electronegative impurities suppress the activity in ammonia synthesis and consume part of the promoters.

Ammonia synthesis on graphitic-nanofilament supported Ru catalysts

Graphitic-nanofilaments (GNFs) supported ruthenium catalysts were prepared and characterized by NZ physisorption, X-ray diffraction (XRD), transmission electron microscope (TEM) and temperature programmed reduction-mass spectroscopy (TPR-MS) and used for ammonia synthesis in a fixed bed microreactor. The TEMs of the Ru/GNFs and Ru-Ba/GNFs catalysts indicate that the Ru particles are in the range of 2-4 nm, which is the optimum size of Ru particles for the maximum number of B5 type sites. The activity of Ru-Ba/GNFs catalysts is higher than that of Ru-Ba/AC by about 25%. The methanation reaction on the Ru/GNFs catalyst is remarkably inhibited compared with a Ru/AC catalyst. High graphitization of GNFs is likely to be the reason for the high resistance to the methanation reaction. The power rate law for ammonia synthesis on Ru-Ba/GNFs catalysts can be expressed by r = Kp(NH3)(-0.4) P-N2(0.8) P-H2(-0.7), indicating that H-2 is an inhibitor for N-2 activation on the catalyst. Catalysts with the promoters Ba, K and Cs show large differences in activity for ammonia synthesis. The catalyst promoted with Ba (Ba/Ru = 0.2 molar ratio) was found to be the most active, whereas that with a K promoter was the least active. (C) 2003 Elsevier B.V. All rights reserved.

Effects of ammonia and cetyltrimethylammonium bromide (CTAB) on morphologies of ZnO nano- and micromaterials under solvothermal process

Submicrometer zinc oxide (ZnO) with different morphologies including spindle-like, pencil-like, branch rod-like and frizzy flower-like shapes, have been hydrothermally synthesized in mixed solvents of ethanol and water at 140 degrees C. It was found that the volumes of added ammonia, surfactant (cetyltrimethylammonium bromide, CTAB), and mixed solvent play crucial roles in morphological control of ZnO nanostructures. Increasing the volume of ammonia added to the reaction system, the shape of ZnO evolves from spindle into branch rod-like. Synergetic influence between CTAB and ammonia can only be observed at high concentration of ammonia.

Preparation, physico-chemical behavior and catalytic property for ammonia oxidation of perovskite like mixed oxides La2-xSrxCuO4-lambda

A series of Sr2+ doped perovskite like oxides La2-xSrxCuO4-lambda (x = 0 similar to 1) were prepared, the structure, lattice parameters, content of Cu3+, oxygen vacancies created by Sr2+ substitution and composition of these complex oxides were studied by XRD and iodic titration method. The redox ability,active oxygen species and surface image were evaluated and analyzed with TPD, TG, XPS and SEM measurements. The catalytic activity for ammonia oxidation over these oxides was tested, and the relationship among the catalytic properties, structure, nonstoichiometric oxygen,redox ability and surface behavior were correlated and some information on the mechanism of ammonia oxidation was obtained.