大尺寸高质量γ-LiAlO2晶体的制备研究

采用提拉法快速（6mm／h）生长了透明、φ45mm×50mm完整的铝酸锂晶体，但晶体中下部出现了一个树状、乳白色的核芯．分别从透明和乳白色核芯部位取样，研磨作粉末X射线衍射测试，发现两个样品所有的衍射峰均可以用γ-LiAlO2指标化．双晶摇摆曲线显示晶体透明和乳白色部位的半高宽分别为116．9arcsec和132．0axcsec，结晶质量较差．通过三步气相传输平衡法（简称VTE）处理后，透明部位半高宽值（FWHM）降至44．2arcsec，乳白色部位FWHM值降至53．3arcsec．结合快速生长和VTE

Comparison of ZnO films grown on before- and after-vapor transport equilibration (VTE) LiAlO2 substrates by pulsed laser deposition (PLD)

About Phi 45 mm LiAlO2 single crystal was grown by Czochralski (Cz) technique. However, the full-width at half-maximum (FWHM) value was high to 116.9 arcsec. After three vapor transport equilibration (VTE) processes, we can obtain high-quality LiAlO2 slice with the FWHM value of 44.2 arcsec. ZnO films were fabricated on as-grown slices and after-VTE ones by pulsed laser deposition (PLD). It was found that ZnO films on the two slices have similar crystallinity, optical transmittance and optical band gap at room temperature. These results not only show that LAO substrate is suitable for ZnO growth, but also prove that the crystal quality of LAO substrate slightly affects the structural and optical properties of ZnO film.

Influence of vapor transport equilibration on the crystal quality and thermal-expansion coefficients of gamma-LiAlO2

gamma-LiAlO2 (LAO) single crystal has been grown by the Czochralski method. However, its quality was deteriorated due to lithium volatilization during the crystal growth. The full width at half maximum value drops from 116.9 to 44.2 arc sec after the LAO slice was treated by vapor transport equilibration at 1000, 1100, and 1200 degrees C/48 h in sequence. The treated slice shows higher optical transmission than the as-grown one in the measured wavelength range of 190-1900 nm, meanwhile, its absorption edge exhibits a blueshift. According to Raman spectra, the treated slice has homogeneous quality at different depths from surface to 0.01 mm. The expansion coefficient of the treated slice for a axis drops from 17.2398x10(-6)/degrees C to 16.5240x10(-6)/degrees C, and that for c axis drops from 10.7664x10(-6)/degrees C to 10.0786x10(-6)/degrees C.