Multiple melting and crystallization behavior of nylon 1212

The wide-angle X-ray diffraction (WAXD) patterns of isothermally crystallized Nylon 1212 show that gamma-form crystals form below 90 degrees C and the alpha-form crystals call exist above 140 degrees C. In the temperature range of 90-140 degrees C, the a-form gamma-form crystals coexist. Variable-temperature WAXD exhibits that the nylon 1212 gamma-form does not show crystal and transition on heating, while a-form isothermally crystallized at 160 degrees C exhibits Brill transition at a little higher than 180 degrees C on heating. The multiple melting behaviors of Nylon 1212 isothermally crystallized from melt come from a complex mechanism of different crystal structures, dual lamellar population and melting-recrystallization. In polarized optical microscope (POM) observations, Nylon 1212 isothermally crystallized at 175 degrees C shows the ringed banded spherulites. However, at temperatures below 160 degrees C the ringed handed image disappears, and cross-extinct spherulites are formed.

Destabilization of basic fibroblast growth factor by oligodeoxynucleotides

The effects of oligodeoxynucleotide (ODN) on the conformation of basic fibroblast growth factor (bFGF) were studied by spectral method. The results showed that ODN destabilized the protein.

Context and conformation dictate function of a transcription antitermination switch

In bacteriophage, transcription elongation is regulated by the N protein, which binds a nascent mRNA hairpin ( termed boxB) and enables RNA polymerase to read through distal terminators. We have examined the structure, energetics and in vivo function of a number of N boxB complexes derived from in vitro protein selection. Trp18 fully stacks on the RNA loop in the wild-type structure, and can become partially or completely unstacked when the sequence context is changed three or four residues away, resulting in a recognition interface in which the best binding residues depend on the sequence context. Notably, in vivo antitermination activity correlates with the presence of a stacked aromatic residue at position 18, but not with N boxB binding affinity. Our work demonstrates that RNA polymerase responds to subtle conformational changes in cis-acting regulatory complexes and that approximation of components is not sufficient to generate a fully functional transcription switch.

Triplex selective 2-(2-naphthyl)quinoline compounds: Origins of affinity and new design principles

A novel competition dialysis assay was used to investigate the structural selectivity of a series of substituted 2-(2-naphthyl)quinoline compounds designed to target triplex DNA. The interaction of 14 compounds with 13 different nucleic acid sequences and structures was studied. A striking selectivity for the triplex structure poly dA:[poly dT](2) was found for the majority of compounds studied. Quantitative analysis of the competition dialysis binding data using newly developed metrics revealed that these compounds are among the most selective triplex-binding agents synthesized to date. A quantitative structure-affinity relationship (QSAR) was derived using triplex binding data for all 14 compounds used in these studies. The QSAR revealed that the primary favorable determinant of triplex binding free energy is the solvent accessible surface area. Triplex binding affinity is negatively correlated with compound electron affinity and the number of hydrogen bond donors. The QSAR provides guidelines for the design of improved triplex-binding agents.

Synthesis, structure and ionic conductivity of La2/3-xLi3xMoO4

A series of compounds, La2/3 - xLi3xMoO4, were first prepared. Their structures are tetragonal scheelites with the cationic defects. The cell parameters a, c and values of c/a decrease with the increasing of the substitution amount (3x) of lithium ion. Cationic vacancies are getting more as Li+ concentration is lower. The diffusion of lithium ion is predominant. The concentration of charge carriers increases with increasing the substitution amount (3x) of lithium ion, meanwhile, the concentration of cationic vacancies decreases. The conductivity approaches the best when the substitution amount (3x) of lithium ion is about 0.3. The conductivity of La0.567Li0.3MoO4 is 6.5 x 10(-6) S . cm(-1) at room temperature.

Low temperature preparation of ceria solid solutions doubly doped with rare-earth and alkali-earth and their properties as solid oxide fuel cells

A series of solid electrolytes, (Ce(0.8)Ln(0.2))(1 - x)MxO2 - delta(Ln = La, Nd, Sm, Gd, M:Alkali-earth), were prepared by amorphous citrate gel method. XRD patterns indicate that a pure fluorite phase is formed at 800 degreesC. The electrical conductivity and the AC impedance spectra were measured. XPS spectra show that the oxygen vacancies increase owing to the MO doping, which results in the increase of the oxygen ionic transport number and conductivity. The performance of ceria-based solid electrolyte is improved. The effects of rare-earth and alkali-earth ions on the electricity were discussed. The open-circuit voltages and maximum power density of planar solid oxide fuel cell using (Ce0.8Sm0.2)(1 - 0.05)Ca0.05O2 - delta as electrolyte are 0.86 V and 33 mW . cm(-2), respectively.

Surface renewable graphite organosilicate composite electrode containing indium(III) hexacyanoferrate(II/III)

Indium(III) hexacyanoferrate(II/III) (InHCF) supported on graphite powder was prepared using the in situ chemical deposition procedure and subsequently dispersed into methyltrimethoxysilane-derived gels to yield a conductive graphite organosilicate composite. The composite was used as the electrode material to fabricate a three-dimensional InHCF-modified electrode. InHCF acts as a catalyst, graphite powder ensures conductivity by percolation, the silicate provides a rigid porous backbone and the methyl groups endow hydrophobicity and thus limit the wetting section of the modified electrode. The chemically modified electrode can electrocatalyze the oxidation of thiosulfate, and exhibits a good repeatability of surface-renewal by simple mechanical polishing, as well as simple preparation, good chemical and mechanical stability.

Synthesis of bis [bis (tert-butylcyclopentadienyl) neodymium chloride] and structural trend of bis[bis(tertbutylcyclopentadienyl) lanthanide chloride]

The reaction of NdCl3 with 2 equiv. of Na-(BuC5H4)-C-t in THF(tetrahydrofuran) gives blue crystals [((BUC5H4)-C-t)(2)NdCl](2), C36H52Cl2Nd2(M-r = 844.11) Which crystallizes in the triclinic system with space group . The crystal data are a=11.978 (1), b=12.671(4), c=12.706(2)Angstrom, alpha=105.47(2), beta=99.38(1)? gamma=93.15 (2)degrees, V=1825 (3) Angstrom(3), Z = 2 , D-c = 1.53g/cm(3), F(000) = 450 , T = 298K , lambda(MoK alpha) = 0.71069 Angstrom, , mu = 14.97cm(-1). Final R = 0.0390, R-w = 0.0376 for 4329 reflections with I greater than or equal to 3 sigma(I-o). The molecule has a dimer structure with two certrosymmetrical chlorine bridges. The structural trend of these analogous complexes is discussed.

Morphology, thermal behavior, and mechanical properties of PA6/UHMWPE blends with HDPE-g-MAH as a compatibilizing agent

A functionalized high-density polyethylene (HDPE) with maleic anhydride (MAH) was prepared using a reactive extruding method. This copolymer was used as a compatibilizer of blends of polyamide 6 (PA6) and ultrahigh molecular weight polyethylene (UHMWPE). Morphologies were examined by a scanning electron microscope. It was found that the dimension of UHMWPE and HDPE domains in the PA6 matrix decreased dramatically, compared with that of the uncompatibilized blending system. The size of the UHMWPE domains was reduced from 35 mu m (PA6/UHMWPE, 80/20) to less than 4 mu m (PA6/UHMWPE/HDPE-g-MAH, 80/20/20). The tensile strength and Izod impact strength of PA6/UHMWPE/HDPE-g-MAH (80/20/20) were 1.5 and 1.6 times as high as those of PA6/UHMWPE: (80/20), respectively. This behavior could be attributed to chemical reactions between the anhydride groups of HDPE-g-MAH and the terminal amino groups of PA6 in PA6/UHMWPE/HDPE-g-MAH blends. Thermal analysis was performed to confirm that the above chemical reactions took place during the blending process. (C) 2000 John Wiley & Sons, Inc.

The electrical and magnetic properties of lanthanide alkaline-earth transition-metal oxides

Five Ln(2)SrMCuO(6.5) oxides (M = Co, Ln = Y and Ho; M = Fe, Ln = Y, Ho, and Dy) were synthesized, and their crystal structures, IR spectra, and physical properties were studied. They have almost the same structure and crystallize in orthorhombic systems. Below room temperature, Y2SrFeCuO6.5, a known layered oxide, shows antiferromagnetic behavior, but the four new oxides are paramagnetic. Y2SrFeCuO6.5 fits the Curie-Weiss law in the temperature range 300-100 K, but Y2SrCoCuO6.5 shows complex magnetic behavior because of the disproportion of some Co+3 to Co+2 and Co+4 The five oxides are all p-type semiconductors in the measured temperature range and have large electrical resistivities at room temperature.

Low temperature preparation and fuel cell properties of rare earth doped barium cerate solid electrolytes

The solid electrolytes, BaCe(0.8)Ln(0.2)O(2.9) (Ln: Gd, Sm, Eu), were prepared by the sol-gel method. XRD indicated that a pure orthorhombic phase was formed at 900 degrees C. The synthesis temperature by the sol-gel method was about 600 degrees C: lower than the high temperature solid phase reaction method. The electrical conductivity and impedance spectra were measured and the conduction mechanism was studied. The grain-boundary resistance of the solid electrolyte could be reduced or eliminated by the sol-gel method. The conductivity of BaCe0.8Gd0.2O2.9 is 7.87 x 10(-2) S.cm(-1) at 800 degrees C. The open-circuit voltage of hydrogen-oxygen fuel cell using BaCe0.8Gd0.2O2.9 as electrolyte was near to 1 V and its maximum power density was 30 mW.cm(-2).