Luminescence enhancement by blending PVK with blue PPV copolymer

The PL and EL properties of the polymer blends of PVK and blue PPV copolymer were studied. Considerable enhancement of both the photoluminescent and the electroluminescent intensity were observed by using the polymer blends as emission layer in the LED devices. The energy transfer process and the formation of exciplex in the polymer blends were also discussed.

Studies on the interfacial adhesion between functionalized polypropylene and polyamide 1010

The interface behavior of polyamide 1010 (PA1010) and polypropylene (PP) was studied. In order to improve their interfacial adhesion, functional PP was prepared by means of grafting glycidyl methacrylate (GMA) on PP main chains and used instead of plain PP. Several technological characterizations were performed here on their interfaces. ESCA was used to confirm that some kind of reaction occurred between end groups of PA1010 and epoxy species of PP-g-GMA. The peel test was adopted to measure interfacial adhesion. It was found that the fracture energy of interfaces between PA1010 and PP-g-GMA was dramatically increased with the content of GMA. Their interfaces were observed as being blurred by using SEM and TEM and a crack that could be seen in the case of the interfaces of the PA1010 and the plain PP disappeared.

Monte Carlo simulation of phase separation of A/B/A-B ternary mixtures

Monte Carlo simulations were used to model A/B/A-B ternary mixtures with different AB diblock copolymer volume fractions for which both the dispersed and continuous phase volume fractions were kept constant. For concentrations of the diblock copolymer below a critical value, the domain size increment of the dispersed phase decreases linearly with the copolymer concentration. This is in agreement with the predictions of Noolandi and Hong. The dependence of the domain size as a function of the copolymer volume fraction can also be fitted by the equation of Tang and Huang. Our simulations indicate, for the first time, that the micelles form before saturation of the interface occurs. This means that the formation of the micelles is not a result of the saturation of the interface.

Phase-separation behavior of the system PES/phenoxy: An application of the Sanchez-Lacombe lattice fluid theory

Cloud-point curves reported for the system polyethersulfone (PES)/phenoxy were calculated by means of the Sanchez-Lacombe (SL) lattice fluid theory. The one adjustable parameter epsilon(12)*/k (quantifying the interaction energy between mers of the different components) can be evaluated by comparison of the theoretical and experimental phase diagrams. The Flory-Huggins (FH) interaction parameters are computed based on the evaluated epsilon(12)*/k and are approximately a linear function of volume fraction and of inverse temperature. The calculated enthalpies of mixing of PES/phenoxy blends for different compositions are consistent with the experimental values obtained previously by Singh and Walsh [1].

Crystallization of micelles and matrix in dilute diblock copolymer/homopolymer solutions

The crystallization, morphology, and crystalline structure of dilute solid solutions of tetrahydrofuran-methyl methacrylate diblock copolymer (PTHF-b-PMMA) in poly(ethylene oxide) (PEO) and PTHF have been studied with differential scanning calorimetry (DSC), X-ray, and optical microscopy. This study provides a new insight into the crystallization behavior of block copolymers. For the dilute PTHF-b-PMMA/PEO system containing only 2 to 7 wt % of PTHF content, crystallization of the PTHF micellar core was detected both on cooling and on heating. Compared the crystallization of the PTHF in the dilute solutions with that in the pure copolymer, it was found that the crystallizability of the PTHF micellar core in the solution is much greater than that of the dispersed PTHF microdomain in the pure copolymer. The stronger crystallizability in the solution was presumably due to a softened PMMA corona formed in the solution of the copolymer with PEG. However, the "soft" micelles formed in the solution (meaning that the glass transition temperatures (T-g) of the micelle is lower than the T-m of the matrix phase) showed almost no effects on the spherulitic morphology of the PEO component, compared with that of the pure PEO sample. In contrast, significant effects of the micelles with a "hard" PMMA core (meaning that the T-g of the core is higher than the T-m of the PTHF homopolymer) on the nucleation, crystalline structure, and spherulitic morphology were observed for the dilute PTHF-b-PMMA/PTHF system. (C) 1998 John Wiley & Sons, Inc.

Interfacial layer and phase inversion behavior in the blend of polyethersulfone and polycarbonate

A blend of polyethersulfone (PES) and polycarbonate (PC) with a ratio of 40/60 was studied by scanning electron microscopy (SEM), dynamic mechanical analysis, and transmission electron microscopy (TEM). It was found that the PES-PC blend is a partially miscible, two-phase system, and an interfacial layer exists between the phases of PES and PC. Specific interaction resulting from the n-complex between PES and PC provides the driving force for formation of the interfacial layer. In addition, phase inversion behavior was also observed for the 40/60 composition.

Blue-light emitting diodes and flat display based on poly(p-phenylenevinylene) copolymers

Copolymers containing alternating flexible aliphatic blocks and rigid poly(p-phenylenevinylene) (PPV) blocks were synthesized and characterized. It was found that the fluorescent intensity increases with increasing length of the flexible blocks. Bright blue-light emitting diodes were fabricated using PPV copolymers as electroluminescent layers. The devices show 190 cd/m(2) light-emitting brightness at 460 nm and 15 V rum-on voltage. The effects of oxadiazole derivative PBD and tris(8-hydroxyquinoline) aluminum Alq(3) electron-transporting layers on the luminance and stability of the devices are discussed.

Novel morphology in ring-banded spherulites from single-phase mixtures of poly(epsilon-caprolactone) with poly(styrene-co-acrylonitrile)

Novel morphology of ring-banded spherulites in the surface of poly(epsilon-caprolactone)/poly(styrene-co-acrylonitrile) (PCL/SAN) blends was discovered and studied by SEM and TEM. The ring-banded spherulites separate into those exhibiting a very dark contrast, of relatively regular bundles of lamellae and others appearing with a much brighter intensity, of a coarse and irregular aggregates of lamellae. The origin of the novel morphology is not due to different crystalline structures as in the case of isotactic polypropylene because only one crystal structure exists in PCL/SAN blends. The formation may reflect whether spherulites in PCL/SAN blends are nucleated at the bottom surface or at the top (free) surface.

Toughening of nylon with epoxidised ethylene propylene diene rubber

Blends of nylon-6 and epoxidised ethylene propylene diene (eEPDM) rubber were prepared through reactive mixing. It is found that the toughness of nylon-6 can be much improved by this method, and that the particle size of eEPDM is much smaller than that of unexpoxidised EPDM (uEPDM) rubber in a nylon-6 matrix. This indicates that the epoxy group in eEPDM could react with a nylon-6 end group to form a graft copolymer which could act as an interfacial compatibiliser between the nylon-6 and the eEPDM rubber dispersed phase. (C) 1998 Elsevier Science Ltd. All rights reserved.

High resolution solid-state NMR and DSC study of poly(ethylene glycol) silicate hybrid materials via sol-gel process

Hybrid materials incorporating poly(ethylene glycol) (PEG) with tetraethoxysilane (TEOS) via a sol-gel process were studied for a wide range of compositions of PEG by DSC and high resolution solid-state C-13- and Si-29-NMR spectroscopy. The results indicate that the microstructure of the hybrid materials and the crystallization behavior of PEG in hybrids strongly depend on the relative content of PEG. With an increasing content of PEG, the microstructure of hybrid materials changes a lot, from intimate mixing to macrophase separation. It is found that the glass transition temperatures (T-g) (around 373 K) of PEG homogeneously embedded in a silica network are much higher than that (about 223 K) of pure PEG and also much higher in melting temperatures T-m (around 323 K) than PEG crystallites in heterogeneous hybrids. Meanwhile, the lower the PEG content, the more perfect the silica network, and the higher the T-g of PEG embedded in hybrids. An extended-chain structure of PEG was supposed to be responsible for the unusually high T-g of PEG. Homogeneous PEG-TEOS hybrids on a molecular level can be obtained provided that the PEG. content in the hybrids is less than 30% by weight. (C) 1998 John Wiley & Sons, Inc.

Preparation and characterization of a new blend of poly(2-hydroxyethyl methacrylate) and poly(ethylene glycol)

A new blend of poly(2-hydroxyethyl methacrylate) (PHEMA) with poly (ethylene glycol) (PEG) was prepared. The results from solid-state NMR indicate that the PHEMA/PEG(88:12, w/w) blend is miscible on a molecular level.

Application of digital image analysis to the study of banded spherulite during growing and melting process

A digital image analysis(DIA) technique can be applied directly to the image obtained by polarizing microscope. The time-resolved DIA apparatus including image collecting, showing and data analysis has been home-made. As an example, it has been used to study the banded spherulite in the blends of poly(epsilon-caprolactone) (PCL) and poly(styrene-ran-acrylonitrile) (SAN).

Isothermal melt and cold crystallization kinetics of poly(aryl ether ether ketone ketone) (PEEKK)

Isothermal melt and cold crystallization kinetics of PEEKK have been investigated by differential scanning calorimetry in two temperature regions. During the primary crystallization process, the relative crystallinity develops with a time dependence described by the Avrami equation, with exponent n = 2 for both melt and cold crystallization. The activation energies are -544.5 and 466.7 kJ/mol for crystallization from the melt and amorphous glassy state, respectively. The equilibrium melting point T-m(o) is estimated to be 371 degrees C by using the Hoffman-Weeks approach. The lateral and end surface free energies derived from the Lauritzen-Hoffman spherulitic growth rate equation are sigma=10 erg/cm(2) and sigma(e) = 60 erg/cm(2), respectively. The work of chain folding q is determined as 3.98 kcal/mol. These observed crystallization kinetic characteristics of PEEKK are compared with those of PEEK. (C) 1997 Elsevier Science Ltd.

Thermal analysis of ethylene propylene copolymer-grafted-acrylic acid

The thermal properties of ethylene propylene copolymer-grafted-acrylic acid (EP-g-AA) were investigated by using differential scanning calorimetry (DSC). Compared with the ethylene propylene copolymer (EP), the peak values of the melting temperature (T-m) of the propylene sequences in the grafted EP changed a little, the crystallization temperature (T-c) increased about 8-12 degrees C, and the melting enthalpy (Delta H-m) increased about 4-6 J/g. The isothermal crystallization kinetics of grafted and ungrafted samples was carried out by DSC. Within the scope of the researched crystallization temperature, the Avrami exponent (n) of the ungrafted sample was 1.6-1.8, and that of grafted samples were all above 2, which indicated that the grafted monomer could become the crystal nuclei for the crystallization of propylene sequence. With increasing grafted monomer content, the crystallization rate of propylene sequence in grafted EP increased; it might be the result of rapid nucleation rate and crystal growth rate.

Critical crystallization temperature for the occurrence of epitaxy between high-density polyethylene and isotactic polypropylene

The crystallization behavior of high-density polyethylene (HDPE) on highly oriented isotactic polypropylene (iPP) at elevated temperatures (e.g., from 125 to 128 degrees C), was studied using transmission electron microscopy and electron diffraction. The results show that epitaxial crystallization of HDPE on the highly oriented iPP substrates occurs only in a thin layer which is in direct contact with the iPP substrate, when the HDPE is crystallized from the melt on the oriented iPP substrates at 125 degrees C. The critical layer thickness of the epitaxially crystallized HDPE is not more than 30 nm when the HDPE is isothermally crystallized on the oriented iPP substrates at 125 degrees C. When the crystallization temperature is above 125 degrees C, the HDPE crystallizes in the form of crystalline aggregates and a few individual crystalline lamellae. But both the crystalline aggregates and the individual crystalline lamellae have no epitaxial orientation relationship with the iPP substrate. This means that there exists a critical crystallization temperature for the occurrence of epitaxial crystallization of HDPE on the melt-drawn oriented iPP substrates (i.e., 125 degrees C). (C) 1997 John Wiley & Sons, Inc.