The PPh3 ligand modified Rh/SiO2 catalyst for hydroformylation of olefins

A novel family of hybrid catalyst with high turnover frequency (TOF) and high selectivity towards aldehydes for hydroformylation of olefins could be successfully approached through direct coordination with the PPh3 ligand to the highly dispersed Rh metal particle precursors. A further advantage is that the catalyst is easily prepared and recyclable. The results revealed that hydroformylation of olefins to aldehydes dominantly took place on the surface of PPh3 ligand modified Rh metal particles of the hybrid catalyst. It was found that the formation of chemical coordination bond between the Rh metal particles and the lone-pair electron of PPh3 was evident through the TG and P-31 NMR measurement. Moreover, the addition of PPh3 onto the Rh/SiO2 exert a significant influence on the adsorption state of reactant CO, H-2 and C2H4 on the PPh3-Rh/SiO2 sample, which probably lead to good catalytic performances for hydroformylation of olefins. (C) 2004 Elsevier B.V. All rights reserved.

Recyclable heterogeneous Rh/SiO2 catalyst enhanced by organic PPh3 ligand

Heterogeneous PPh3-Rh/SiO2 catalysts for hydroformylation of olefins, prepared by direct doping of phosphine onto the heterogeneous Rh/SiO2 precursor, exhibited high activity and selectivity towards aldehydes, which originated from chemical coordination bond between the phosphine and Rh metal nantoparticles on the SiO2 support.

A novel method for preparing PEMFC catalytic layers

A novel PEMFC catalytic layer was fabricated by a Nafion-pyrolyzed method, which demonstrated a high performance with a maximum power density of 0.82 W/cm(2) on an electrode prepared by this method. The effects of the heat-treatment temperature and Nation content in the catalyst layer on performance were studied.

On the surface sites Of MOP/SiO2 catalyst under sulfiding conditions: IR spectroscopy and catalytic reactivity studies

The surface sites of MoP/SiO2 catalysts and their evolution under sulfiding conditions were characterized by IR spectroscopy using CO as the probe molecule. The HDS activities of thiophene were measured on the MoP/SiO2 catalyst that was subjected to different sulfidation and reactivation pretreatments. Cus Modelta+ (0 < delta less than or equal to 2) sites are probed on the surface of fresh MoP/SiO2 by molecularly adsorbed CO, exhibiting a characteristic IR band at 2045 cm(-1). The surface of MoP/SiO2 is gradually sulfided in HDS reactions, as revealed by the shift of the IR band at 2045 to ca. 2100 cm(-1). Although the surface of a MoP/SiO2 catalyst becomes partially sulfided, the HDS activity tests show that MoP/SiO2 is fairly stable in the initial stage of the HDS reaction, providing further evidence that molybdenum phosphide is a promising catalytic material for industrial HDS reactions. Two kinds of surface sulfur species are formed on the sulfided catalyst: reversibly and irreversibly bonded sulfur species. The MoP/SiO2 catalyst remains stable in the HDS of thiophene because most sulfur species formed under HDS conditions are reversibly bonded on the catalyst surface. A detrimental effect of presulfidation on the HDS activity is observed for the MoP/SiO2 catalyst treated by H2S/H-2 at temperatures higher than 623 K, which is ascribed to the formation of a large amount of the irreversibly bonded sulfur species. The irreversibly sulfided catalyst can be completely regenerated by an oxidation and a subsequent reduction under mild conditions. (C) 2003 Elsevier Inc. All rights reserved.

Influence of iron promoter on catalytic properties of Rh-Mn-Li/SiO2 for CO hydrogenation

The effect of iron promoter on the catalytic properties of Rh-Mn-Li/SiO2 catalyst in the synthesis Of C-2 oxygenates from syngas was investigated by means of the following techniques: CO hydrogenation reaction, temperature-programmed reduction (TPR), temperature-programmed desorption and reaction of adsorbed CO (CO-TPD and TPSR) and pulse adsorption of CO. The results showed that the addition of iron promoter could improve the activity of the catalysts. Unexpectedly, the yield of C-2 oxygenates increased greatly from 331.6 up to 457.5 g/(kg h) when 0.05% Fe was added into Rh-Mn-Li/SiO2 catalyst, while no change in the selectivity to C-2 oxygenates was observed. However, the activity and selectivity Of C-2 oxygenates were greatly decreased if the Fe amount exceeded 1.0%. The existence of a little iron decreased the reducibility of Rh precursor, while the reduction of Fe component itself became easier. CO uptake decreased with increasing the quantity of Fe addition. This phenomenon was further confirmed by CO-TPD results. The CO-TPD and TPSR results showed that only the strongly adsorbed CO could be hydrogenated, while the weakly adsorbed CO was desorbed. We propose that Fe is highly dispersed and in close contact with Rh and Mn; such arrangements were responsible for the high yield Of C-2 oxygenates. (C) 2002 Elsevier Science B.V. All rights reserved.