Phi 140 mm sapphire crystal growth by temperature gradient techniques and its color centers

Sapphire crystals, 140 mm in diameter and 90 turn in height, have been grown by temperature gradient techniques (TGT). The growth direction of the boule was fixed by means of Lane X-ray diffraction. A prominent 204 nm absorption band in TGT-Al2O3. which does not appear in single crystals grown by Czochralski method has been studied. Analysis further substantiates the F-center model of this band. Two relatively weaker bands absorbing at 232 nm and 254 nm were ascribed to F+ centers. F-type centers concentration was determined using Smakula's equation. (c) 2005 Elsevier B.V. All rights reserved.

温梯法生长大尺寸蓝宝石晶体的脱碳去色退火研究

温度梯度法（temperature gradient technique，TGT）生长的Al2O3晶体因石墨发热体在高温时的挥发和原料中过渡性金属离子的存在，在不同部位呈现不同颜色，一般上部为浅红色，尾部为浅黄绿色．将TGT法生长的Al2O3晶体（Ф110×80mm^3）依次经过高温氧化气氛、高温还原气氛脱碳、去色退火实验，即“两步法”退火实验，晶体变成无色、透明．经测试，Al2O3晶体的完整性、光学透过率和光学均匀性均有显著提高.

Cr4+在八面体格位中的光谱特性研究

Cr-doped and Mg, Cr-codoped Al2O3 crystals were grown by Czochralski method. The latter has a broad absorption peak in 900-1600nm region. We investigated the change of the absorption band with annealing under different atmospheres or temperatures. Through establishing a structure defect model, we successfully interpreted all the experiment results and confirmed that the extremely broad infrared absorption band belonged to Cr4+, which should occupy the octahedral sites in Al2O3.

氧化铝透明陶瓷中Cr3+的发光性能

采用传统无压烧结工艺制备出透明性良好的掺Cr3+氧化铝陶瓷;测定了陶瓷的吸收光谱、发射光谱和激发光谱。结果表明,氧化铝陶瓷吸收峰与红宝石单晶一致,吸收截面大小与单晶相近;陶瓷中Cr3+离子所处格位的晶体场强较单晶弱,但其发射谱仍有较好的锐线发射;陶瓷中微量添加剂以及晶界的存在使得Al2O3晶胞发生畸变,造成其发射峰宽化。

La2O3对氧化铝透明陶瓷显微结构和透光性能的影响

采用传统无压烧结工艺在氢气氛下制备Al2O3透明陶瓷。实验结果表明：MgO和La2O3复合添加时，随着La2O3掺杂量的增加体积密度总体上保持上升的趋势。随着保温时间的延长，陶瓷的致密化程度增大，残余气孔逐步排出，晶粒进一步长大。采用La2O3和MgO复合添加比单独掺入MgO陶瓷样品透过率更高，掺杂效果更好。在烧结温度为1750℃，保温时问为1h条件下，在波艮为300～800nm测试范围内，陶瓷样品的全透过率大于82％，最大值为86％。

退火处理对ZnO薄膜发光特性的影响

用脉冲激光沉积法(PLD)在MgO(100)、a-Al2O3(0001)和MgAl2O4(111)衬底上沉积了ZnO薄膜，测量了它们的发射光谱，观察到430nm的蓝光发射，并研究了退火、衬底和激发波长对ZnO薄膜这一蓝光发射的影响。指出ZnO薄膜中430nm的蓝光发射是由锌填隙原子缺陷能级到价带顶能级间的跃迁以及电子从氧空位浅施主能级到价带顶能级间的跃迁两种机理共同作用的结果。在MgO衬底上沉积的ZnO薄膜在350nm光激发下蓝光发射峰最强。

Diode-pumped passively q-switched Nd : YAG ceramic laser with a Cr4+: YAG crystal-satiable absorber

Transparent polycrystalline Nd:YAG ceramics were fabricated by solid-state reactive sintering a mixture of commercial Al2O3,Y2O3, and Nd2O3 powders. The powders were mixed in ethanol and doped with 0.5 wt% tetraethoxysilane, dried, and pressed. Pressed samples were sintered at 1750 degrees C in vacuum. Transparent fully dense samples with average grain sizes of 10 mu m were obtained. The 1 at.% Nd:YAG ceramic was used to research passively Q-switched laser output with a Cr4+:YAG crystal as a saturable absorber. An average output power of 94 mW with a pulse width of 50 ns was obtained when the incident pump power was 750 mW. The slope efficiency was 13%. The pulse energy is 5 mu J, and the peak power is about 100 W.

Diode-pumped Yb : YAG ceramic laser

Transparent polycrystalline Yb:YAG ceramics were fabricated by solid-state reactive sintering a mixture of commercial Al2O3, Y2O3, and Yb2O3 powders. The powders were mixed in ethanol and doped with 0.5 wt% tetraethoxysilane, dried, and pressed. Pressed samples were sintered at 1730 degrees C in vacuum. Transparent fully dense samples with grain sizes of several micrometers were obtained. The phase from 1500 degrees to 1700 degrees C was important for the grain growth, in which the grains grew quickly and a mass of pores were eliminated from the body of the sample. Annealing was an important step to remove the vacancies of oxygen and transform Yb2+ to Yb3+. The 1 at.% Yb:YAG ceramic sample was pumped by a diode laser to study the laser properties. The maximum output power of 1.02 W was obtained with a slope efficiency of 25% at 1030 nm. The size of the lasering sample was 4 mm x 4 mm x 3 mm.

Annealing effects of sapphire substrate on properties of ZnO films grown by magnetron sputtering

The annealing effects of sapphire substrates on the quality of epitaxial ZnO films grown by dc reactive magnetron sputtering were studied. The atomic steps formed on (0001) sapphire (alpha-Al2O3) substrates surface by annealing at high temperature were analyzed by atomic force microscopy. Their influence on the growth of ZnO films was examined by X-ray diffraction and photoluminescence measurements. Experimental results indicate that the film quality is strongly affected by annealing treatment of the sapphire substrate surface. The optimum annealing temperature of sapphire substrates for ZnO grown by magnetron sputtering is 1400 degrees C for 1 h in air.

固相法制备Al2（WO4）3粉体及其负热膨胀性能

以Al2O3和WO3为原料，采用固相反应法制备了负热膨胀性能的Al2（WO4）3粉体。用X射线粉末衍射和扫描电镜分别对粉体进行物相、晶体结构分析和形貌观察；通过热重-差热分析了粉体的热性能；采用热膨胀仪测定了热膨胀系数。结果表明：产物为高纯度正交晶系结构的Al2（WO4）3，形状规则，大小均匀，平均尺寸为0．6μm×0．4μm。从室温到熔点范围内，Al2（WO4）3粉体无相变，不发生分解，30～900℃的平均热膨胀系数为-1．56×10^-6K^-1。

Influence of carbon on the thermoluminescence and optically stimulated luminescence of α -Al2O3:C crystals

alpha-Al2O3:C crystal shows excellent thermoluminescence (TL) and optically stimulated luminescence (OSL) properties but the real role carbon plays in this crystal is still not clearly understood so far. In this work, alpha-Al2O3:C crystal doping with different amounts of carbon were grown by the temperature gradient technique, and TL and OSL properties of as-grown crystals were investigated. Additionally, a mechanism was proposed to explain the role of carbon in forming the TL and OSL properties of alpha-Al2O3:C. TL and OSL intensities of as-grown crystals increase with the increasing amount of carbon doping in the crystal, but no shift is found in the glow peak location at 465 K. As the amount of carbon doping in the crystals decreases, OSL decay rate becomes faster. With the increase in heating rate, the integral TL response of as-grown crystals decreases and glow peak shifts to higher temperatures. TL response decrease rate increases with the increasing amount of carbon doping in the crystals. All the TL and OSL response curves of as-grown crystals show linear-sublinear-saturation characteristic, and OSL dose response exhibits higher sensitivity and wider linear dose range than that of TL. The crystal doping with 5000 ppm carbon shows the best dosimetric properties. Carbon plays the role of a dopant in alpha-Al2O3:C crystal and four-valent carbon anions replace the two-valent anions of oxygen during the crystal growth process, and large amounts of oxygen vacancies were formed, which corresponds to the high absorption coefficient of F and F+ centers in the crystals.

Thermal and electric conductivity of near-zero thermal expansion ZrW 2O8//ZrO2 composites

In this work, the microstructure, thermal and electric conductivity properties of near-zero thermal expansion ZrW2O8/ZrO2 and Al2O3 added ZrW2O8/ZrO2 composites were studied. Both the two composites exhibit very low thermal conductivity and the thermal conductivity decreases slightly as the temperature increases. The electric conductivity of the two composites increases with the increasing of the measurement temperature. The Al2O3 added ZrW2O8/ZrO2 composite has higher thermal and electric conductivity than ZrW2O8/ZrO2 composite. The most important factor which causes the difference of the thermal and electric conductivity of the composites is the porosity. (C) 2008 The Ceramic Society of Japan. All rights reserved.

α-Al_2O_3:C晶体的热释光和光释光特性

以高纯α-Al2O3和石墨为原料,采用温梯法生长了α-Al2O3:C晶体,使用RisΦTL/OSL-DA-15型热释光和光释光仪研究了其热释光和光释光特性.α-Al2O3:C晶体在462K附近有单一热释光峰,发射波长位于410nm.随着辐照剂量的增加,热释光强度逐渐增强,462K的热释光特征峰位置保持不变.α-Al2O3:C晶体的光释光衰减曲线由快衰减和慢衰减两个部分组成,随着辐照剂量的增加,快衰减部分衰减速率变化不大,而慢衰减部分衰减速率加快.在5×10-6—10Gy剂量范围内,α-Al2O3:C晶体的热释光剂量响应呈现良好的线性关系,30Gy时达到饱和;光释光剂量响应在5×10-6—60Gy剂量范围内呈现良好的线性关系,100Gy时达到饱和.与热释光相比,光释光剂量响应具有更高的灵敏度和更宽的线性剂量响应范围.

Growth and annealing properties of Mg0.4Al2.4O4 crystal

Mg0.4Al2.4O4 single crystals with good optical quality were successfully grown by the Czochralski method. The transmission spectrum indicated that the absorption edge of the crystal was at 220nm, while no apparent absorption peaks were found. The X-ray diffraction and DSC curve analysis showed that Mg0.4Al2.4O4 crystal was stable at room temperature. While after annealing in the air and hydrogen atmosphere at about 1200 degrees C,Mg0.4Al2.4O4 decomposed into Al2O3 and (MgO)(0.4)(Al2O3)(x) (0.4 < x < 1.2). The reaction mainly occurred on the crystal surface, barely inside. (C) 2008 Elsevier B.V. All rights reserved.

微缺陷对薄膜滤光片环境稳定性的影响

用热蒸发方法沉积了薄膜滤光片．并将样品分别在去离子水中浸泡10天和30天．通过分光光度计、光学暗场显微镜、及扫描电子显微镜等多种测试手段，对诱导透射滤光片在潮湿环境下的稳定性进行了研究．实验发现，在潮湿环境下滤光片产生的膜层分离都是从薄膜中微缺陷点处开始发生和发展的，微缺陷是影响滤光片环境稳定性的重要原因之一，其中杂质和针孔是滤光片中两种最常见的微缺陷．EDS能谱分析进一步表明，薄膜中杂质缺陷成分即为Al2O3膜料本身，所以不能推测，薄膜沉积中的喷溅可能是微缺陷产生的根本原因，抑制喷溅可以有效提高薄膜滤光