Sol-gel synthesis and luminescence of Y4Al2O9:RE3+(RE=Eu, Tb)

Y4Al2O9 (YAM) was prepared by a sol-gel process, using yttrium and aluminum citrate complexes as precursors. The sol-gel process produced single-phase YAM at 900 degrees C, as opposed to the conventional solid-state reaction, which led to the formation of other phases, even if at 1600 degrees C. The emission and excitation spectra of Eu3+ and Tb3+ in YAM showed the existence of two luminescence centers, agreeing with the crystal structure of YAM. The spectral properties of the samples are discussed.

LUMINESCENCE OF DY3+ ENHANCED BY SENSITIZATION

Four types of sensitized luminescence of Dy3+ are reported: (1) by a host having a broad-band spectrum as in Na3Y0.99Dy0.01(VO4)(2); (2) by a sensitizer having a broad-band spectrum as in Ca2B2O5:Dy3+, Bi3+; (3) by a sensitizer having a narrow-band spectrum as in Mg2Gd7.9Dy0.1(SiO4)(6)O-2; (4) by a sensitizer having a broad-band spectrum and energy migration as in Gd compounds such as Ca1.96Pb0.04Gd7.9Dy0.1(SiO4)(6)O-2. The luminescent intensity of Dy3+ can be enhanced in these ways.

A STUDY ON THE LUMINESCENCE PROPERTIES OF EU3+ AND DY3+ IN M(2)RE(8)(SIO4)(6)O-2 (M=MG, CA RE=Y, GD, LA)

In this paper, the luminescence properties of Eu3+ and Dy3+ in the oxyapatites M(2)RE(8)(SiO4)(6)O-2 (M=Mg, Ca; RE=Y, Gd, La) were studied. The spectral characters of Eu3+ were discussed in relation to the crystal structure. The dependence of the red-to-orange intensity ratio and the position of the charge transfer band of Eu3+ and the yellow-to-blue intensity ratio of Dy3+ together with their fluorescence intensities (I-R for Eu3+ and I-Y for Dy3+) On the M(2+) and the substitution of BO45- and PO43- for SiO44- was discussed. Finally, the concentration quenching of Dy3+ luminescence was reported.

LUMINESCENCE AND ENERGY-TRANSFER OF RARE-EARTH-METAL IONS IN MG2Y8(SIO4)(6)O-2

The photoluminescence of Ce3+, Tb3+ and Sm3+, and energy transfer from Ce3+ to Tb3+, Dy3+ and Sm3+ in Mg2Y8(SiOd(4))(6)O-2 are reported and discussed. The Ce3+ ion shows blue luminescence under UV excitation, and occupies simultaneously the 4f site and 6h site in the host lattice. The optimum concentrations for the D-5(3) and D-5(4) emissions of Tb3+ and the (4)G(5/2) emission of Sm3+ are determined to be 0.04, 0.20 and 0.10 mol in every mol of Mg2Y8(SiO4)(6)O-2, respectively. The critical distances responsible for the cross-relaxation between the D-5(3)-D-5(4) and F-7(6)-F-7(0) transitions of Tb3+ and between the (4)G(5/2)-F-4(9/2) and H-6(5/2)-F-4(9/2) transitions of Sm3+ are estimated to be 1.43 and 1.06 nm, respectively. Both Tb3+ and Dy3+ can be sensitized by Ce3+, but Ce3+ and Sm3+ quench each other.

LIFETIMES OF RYDBERG LEVELS IN THE PERTURBED 6SNP P-1,3(1) SERIES OF YBI

Using two methods: (1) three-step excitation and (2) single UV photon excitation in an atomic beam with direct observation of the decay of the fluorescence light, we have measured the lifetimes of the Rydberg levels of YbI belonging to the perturbed series 6snp J = 1 levels. The measured values have been interpreted by the multichannel quantum defect theory (MQDT).

LUMINESCENCE AND ENERGY MIGRATION IN THE OXYAPATITE CA2GD8(SIO4)6O2 DOPED WITH SEVERAL RARE-EARTH AND MERCURY-LIKE IONS

Energy transfer phenomena have been observed by activating the oxyapatite host-lattice Ca2Gd8(SiO4)6O2 with Eu3+, Tb3+, Dy3+, Sm3+. This is based on the energy migration in the Gd3+ sublattice and trapping by the activators. The trapping efficiency for G

LUMINESCENCE AND ENERGY-TRANSFER IN GDP5O14-EU3+,SM3+ SINGLE-CRYSTALS

In this paper we report on the luminescence and energy transfer in GdP4O14:Eu3+,Sm3+ (GdPP:Eu,Sm) in single crystals grown by the hydrothermal method. The room temperature excitation, emission, absorption and IR spectra of the crystals have been measured and analysed. The energy transfer from Gd3+ and Sm3+ to Eu3+ ions in GPP:Eu,Sm crystals is also discussed.

LUMINESCENCE OF BI(3+) AND THE ENERGY-TRANSFER FROM BI(3+) TO R(3+) (R=EU,DY,SM,TB) IN ALKALINE-EARTH BORATES

At room temperature, the Bi3+ ion shows broad band characters of its luminescence in Ca2B2O5, M3B2O6 ( M=Ca,Sr ) and SrB4O7. The maxima of the Bi3+ S-1(0)-->P-3(1) absorption bands are located in the range of 240-300nm, but the energy variation of the corresponding P-3(1)-->S-1(0) emissions is very large. The maxima of these emission bands change from 350nm in Ca3B2O6;Bi3+ to 586nm in SrB4O7:Bi3+. The Stokes shift of the Bi3+ luminescence increases from 6118 cm-1, in Ca2B2O5:Bi3+, to 24439 cm-1, in SrB4O7:Bi3+. The emission intensity of the Bi3+ luminescence increases with the decreasing Stokes shift. It has been found that in Ca2B2O5, the Bi3+ ion could transfer its excitation energy to the R3+ ions ( R=Eu, Dy, Sm, Tb ) , but in, Ca3B2O6 and Sr3B2O6, only Bi3+-->Eu3+ was observed. No energy transfer from Bi3+ to R3+ was detected in SrB4O7.

LIFETIMES OF RYDBERG LEVELS IN THE PERTURBED 6SNP 3P2 SERIES OF YTTERBIUM-I

Using three-step laser excitation in an atomic beam and a time-resolved spectroscopy technique, we measured both the lifetimes of the Rydberg levels of Yb I belonging to the perturbed series 6nsp 3P2 and the lifetimes of the perturbing 4f(13)5d(2)6s 3P2, 1D2 levels. An expected shortening has been observed for the lifetimes of those levels which are strongly mixed with the perturbers.

NATURAL RADIATIVE LIFETIMES OF THE EXCITED-LEVELS OF THULIUM

The radiative lifetimes of eight excited levels of thulium have been measured with the method of stepwise excitation from the 4f13(F-degrees-7/2)6s2(1S0)\7/2\ ground state to the states studied using two pulsed dye lasers. Optical transients were recorded through observing fluorescences and evaluated with regard to the decay time. The accuracy of the measured lifetime values is about 10%.

INVESTIGATION ON THE LUMINESCENCE PROPERTIES OF DY3+ AND EU3+ IN M3LN2(BO3)4 (M=CA, SR, BA, LN= LA, GD, Y)

In this paper, the luminescence properties of Dy3+ and Eu3+ in M3Ln2 (BO3)4 (M = Ca,Sr,Ba; Ln = La, Gd, Y) were systematically studied. The hypersensitive transitions of Dy3+ and Eu3+ were investigated in relation to the host compositions; the relationship between the energy of Eu3+ charge-transfer band and M2+ ion was discussed, and the concentration quenching of Dy3+ luminescence was reported.

INVESTIGATION ON THE LUMINESCENCE PROPERTIES OF DY-3+ AND EU-3+ IN ALKALINE-EARTH BORATES

In this paper, the yellow-to-blue intensity ratio of Dy3+ (Y/B) and the red-to-orange intensity ratio of Eu3+ (R/O) were studied in relation to the compositions and structures of alkaline-earth borates. The dependence of the energy of the Eu3+ charge-transfer band (CTB) and of the emission intensity of Dy3+ on the alkaline-earth ions and the boron content of the hosts is discussed.

MEASUREMENT AND CALCULATION OF SPONTANEOUS EMISSION BRANCHING RATIOS, RELATIVE OSCILLATOR-STRENGTHS, TRANSITION-PROBABILITIES AND LEVEL LIFETIMES FOR ATOMIC URANIUM

We propose a laser induced sensitized fluorescence spectrometry for measuring the spontaneous emission branching ratios o?the transitions from the ten levels 5f36d7s7p-7M7, 5f36d7s7p-7L6, 5f37s27p-5K6, 5f26d27s2 - 5L7, 5f46d7s - 7L6, (17,070cm-1)-5L6, 5f26d27s2-5K6, 6d7s7p-7L5, 5f36d7s7p-7K5 and 5f26d27s2-5I5 to the ground state of atomic uranium (UI) for the first time. Their relative oscillator strengths have been measured by means of hollow cathode discharge (HCD) emission spectrometry. The radiative...